Highlights
-
Due to the Se composition and thickness gradient within single MoS2(1−x)Se2x domains, the bandgap of MoS2(1−x)Se2x is gradually tuned from 1.83 to 1.73 eV.
-
The homojunction phototransistors at zero bias deliver a photoresponsivity of 311 mA W−1, a specific detectivity up to ~ 1011 Jones, and an on/off ratio up to ~ 104.
-
The biased devices yield a champion photoresponsivity of 191.5 A W−1, a specific detectivity up to ~ 1012 Jones, and a photoconductive gain of 106–107.
Abstract
Ternary transition metal dichalcogenide alloys with spatially graded bandgaps are an emerging class of two-dimensional materials with unique features, which opens up new potential for device applications. Here, visible–near-infrared and self-powered phototransistors based on spatially bandgap-graded MoS2(1−x)Se2x alloys, synthesized by a simple and controllable chemical solution deposition method, are reported. The graded bandgaps, arising from the spatial grading of Se composition and thickness within a single domain, are tuned from 1.83 to 1.73 eV, leading to the formation of a homojunction with a built-in electric field. Consequently, a strong and sensitive gate-modulated photovoltaic effect is demonstrated, enabling the homojunction phototransistors at zero bias to deliver a photoresponsivity of 311 mA W−1, a specific detectivity up to ~ 1011 Jones, and an on/off ratio up to ~ 104. Remarkably, when illuminated by the lights ranging from 405 to 808 nm, the biased devices yield a champion photoresponsivity of 191.5 A W−1, a specific detectivity up to ~ 1012 Jones, a photoconductive gain of 106–107, and a photoresponsive time in the order of ~ 50 ms. These results provide a simple and competitive solution to the bandgap engineering of two-dimensional materials for device applications without the need for p–n junctions.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Two-dimensional (2D) materials exhibit new properties due to the unique atomic thin-layered structure. The rich variety of 2D materials provides many different electrical, optical, and chemical properties. Heterostructures with “on-demand” properties can be prepared by stacking different 2D sheets via the van der Waals (dW) force, and the strict requirement in lattice match facing conventional thin films can be relaxed. Additionally, compared with traditional materials used for photodetection (e.g., MCT and III–V compound semiconductors), these new materials have the advantages of high absorption coefficient, mechanical robustness, and easy synthesis, which promise low-cost, lightweight, and high-performance detectors.
2D layered transition metal dichalcogenides (TMDs), MX2 (M = Mo, W; X = S, Se, Te), have attracted substantial attention for prospective applications, including field-effect transistors, photodetectors, lasers, memories, etc., due to the tunable bandgap not only from indirect to direct but also across the range from visible to near-infrared (NIR) spectral region [1,2,3,4,5,6,7,8,9,10,11]. To achieve high-performance optoelectronic and photonic devices and extend the already fascinating properties of the constituents, further bandgap engineering has played a crucial role. This has been mostly realized by creating vertically stacked or in-plane heterostructures, such as exfoliated-restacked MoTe2/MoS2 and epitaxially grown WS2-MoSe2 [12,13,14,15,16]. Recently, in situ controlling the alloy composition within a single domain of ternary TMDs, such as Mo1−xWxS2, WS2xSe2(1−x), and MoS2(1−x)Se2x, has been introduced to tune the bandgaps, which demonstrated an alternative to modulate bandgaps and provided more design flexibility [17,18,19,20]. However, most of the as-grown ternary alloys show a fixed elemental composition, which requires further processing (e.g., wet or dry transferring) to prepare hetero-/homojunctions for devices. The spatially bandgap-graded alloys avoid the drawback by ideally forming a homojunction that possesses continuously tuned band structures, without abruption as in the case of heterojunctions, and results in a lower adjacent barrier height and more energy-friendly [21,22,23,24]. Additionally, the in-plane homojunction can deliver a strong built-in electric field with optimum spatial bandgap grading.
Due to the spatially graded bandgap within a single-alloy domain, such homojunctions provide a novel platform for versatile optoelectronic devices. Grading of stoichiometry induced graded bandgap has been introduced to zero-dimensional (0D) material based solar cells for energy harvesting [25, 26]. Bandgap-graded one-dimensional (1D) alloys enabled by composition gradient have also been systemically investigated and showed competitive properties to conventional 1D materials [27,28,29]. It is still limited to study the spatially bandgap-graded 2D TMDs within a single domain [30, 31]. Although the fabrication of lateral composition-graded 2D materials without thickness variation is rather rewarding, it is a challenge to form desired heterostructures (e.g., p–n junction) for electronics and optoelectronics.
Here, we demonstrated spatially bandgap-graded 2D homojunction devices with p–n diode-like current rectification and photovoltaic response. The homojunctions, stemming from graded composition and thickness together, showed gate-tuned electrical and/or optical properties and enabled visible–NIR and self-powered phototransistors. Gradually selenized MoS2(1−x)Se2x alloys with thickness gradient were synthesized on a single substrate using a one-step and controllable chemical solution deposition (CSD) method. The structural asymmetry of the graded MoS2(1−x)Se2x homojunction produced an intrinsic build-in potential, and hence diode-like characteristics. Such graded homojunctions may relax the need for p–n junctions and serve as alternative building blocks for advanced electronics and optoelectronics.
2 Experimental Section
2.1 Material Synthesis
Ammonium molybdate, sulfur, and selenium powders were used as Mo, S, and Se sources, respectively. TheSiO2/Si substrates (300 nm) were pretreated by piranha solution for good hydrophilicity. For smooth few-layer alloy growth, 0.12 g KOH and 0.05 g ammonium molybdate were dissolved into the 5 mL deionized water to obtain the hydroxide-assisted aqueous solution for smooth MoS2(1−x)Se2x nanosheets with uniform thickness, while we used 0.06 g KOH instead for N/P alloy growth. Then the precursors were spin-coated onto the cleaned SiO2/Si substrates. Subsequently, an alumina boat loaded with several as-processed SiO2/Si substrates was placed at the heating center of the tube furnace, and another boat loaded with 20 mg sulfur and 20 mg selenium powders was placed at the upstream site. In an Ar/H2 (5% H2) atmosphere, the two zones were independently heated up to 650 and 280 °C, respectively. After keeping at 650 °C for 30 min, the furnace was then naturally cooled down to room temperature.
2.2 Material Characterizations
Room-temperature ADF-STEM imaging was performed using a JEOL ARM200F at 200 kV located at the David Cockayne Center for Electron Microscopy (DCCEM) within the Department of Materials at the University of Oxford. Imaging conditions used a 30-µm CL aperture with a convergence semi-angle of 22.5 mrad and a beam current of 35 pA. The acquisition angles for these images were 72.8–271 mrad. Dwell time per pixels was typically 32 µs.
The morphology of the MoS2(1−x)Se2x domains was characterized using scanning electron microscopy (SEM, FEI Scios, 15 kV), and the thickness was measured by AFM (Bruker Dimension Icon, tapping mode). X-ray photoelectron spectroscopy (XPS, Thermo Fisher ESCALAB 250Xi) was used to characterize the chemical composition of alloys. High-resolution transmission electron microscopy (HRTEM) imaging was performed on a field emission TEM (FEI Tecnai F20, 200 kV); selected-area electron diffraction (SAED) measurements were performed on a TEM operating at 120 kV (FEI Tecnai T12). Raman and micro-PL spectra/mapping were collected with a confocal Raman spectrometer (Horiba Jobin–Yvon HR Evolution) using a 532 nm laser as the excitation source. The laser spot size was 1 mm, and the laser power on the sample surface was kept below 60 mW.
2.3 Device Characterizations
The electrical and photoresponsive measurement was conducted at the ambient condition, using a Keithley 4200 semiconductor parameter analyzer equipped with a white light and laser sources. The lasers are unfocused with a spot size of ~ 1.5 mm in diameter. The power density for the 405, 650, and 808 nm lasers was 120, 15.8, and 110 µW mm−2, respectively.
The photoresponsivity was calculated based on Eq. 1:
here R, Ipc, P, and S are defined as photoresponsivity, net photocurrent (Ipc = Ilaser − Idark), laser power density, and active area of a photodetector, respectively.
Assuming that shot noise from the dark current is the major contributor to the total noise, the specific detectivity (D*) of photodetectors can be estimated from Eq. 2:
where q is the elementary charge.
2.4 Theoretical Details
All the calculations were carried out based on density functional theory (DFT), implanted in Vienna ab initio Package (VASP) [32] The projector-augmented wave method was employed to describe the core region with a cutoff of 500 eV [33]. The PBE functional was employed for describing the electronic exchange–correlation [34]. Spin-orbital coupling and dipole correction along the out-of-plane direction were considered [35]. Gamma-centered 25 × 25 × 1 k-points were used for sampling monolayer of MoS2 and MoSe2.
3 Results and Discussion
MoS2(1−x)Se2x alloys were grown using a controllable CSD method on SiO2/Si substrates. As depicted in Fig. 1a (the upper), cleaned SiO2/Si substrates were spin-coated with a precursor solution dissolved with KOH and ammonium molybdate and then loaded into a home-built tube furnace. In the Ar/H2 (5% H2) atmosphere, the mixed S/Se powders (1:2 wt%) at the upstream gas site and the as-processed substrates at the downstream site were independently heated up to 280 and 650 °C within 60 min, respectively. Noteworthy, sulfurization tends to take place at 650 °C or even lower, while at least 750 °C for full selenization [36,37,38]. As a result, after keeping the substrates at 650 °C for 30 min then followed by natural cooling down to the room temperature, MoS2(1−x)Se2x alloys with partial S atoms replaced by Se atoms (the lower in Fig. 1a) were crystallized on SiO2/Si substrates. Through changing the concentration of KOH, we can selectively obtain either few-layer MoS2(1−x)Se2x nanosheets with uniform thickness or MoS2(1−x)Se2x homojunction domains with varied thickness. Figure S1a displays an SEM image of few-layer MoS2(1−x)Se2x nanosheets with identical color contrast, suggesting the uniform thickness. In Fig. S1b, the high-resolution TEM and selected-area electron diffraction (SAED) images demonstrated the high crystallinity and hexagonal symmetry, respectively. In addition, both the Raman (Fig. S1c) and X-ray photoelectron spectroscopy (XPS) spectra (Fig. S1d, e) validate the successful incorporation of Se atoms into MoS2. As a result, the atomic percentage of Se was estimated to be ~ 10%, indicating few-layer MoS2(1−x)Se2x nanosheets possessed fixed elemental composition when thickness unchanged.
In contrast, the SEM image of MoS2(1−x)Se2x homojunction domains in Fig. S1f identifies the surface ridge lines marked by the red arrows, implying a pyramid-like configuration with varied thickness. An atomic force microscopy (AFM) image in Fig. 1b (upper) depicts the surface topography of a homojunction domain. The different color contrast associated with varied thickness and clear grain boundaries were observed, suggesting a stacked configuration composed of a thin edge and a thick center (brighter color). Figure 1b (lower) illustrates the height profiles along the line 1 and line 2 marked in the AFM image. It determines the uniform thickness of 1.9 nm corresponding to the three-layer (3L) nature for the edge while gradually thickened and pyramid-like configuration for the multilayer center. Evidently, the highest point in the blue height profile originates from the ridge lines observed in Fig. S1f. Namely, the homojunction domain can be viewed as a similar nanosheet/pyramid (N/P) structure with thickness grading, whose schematic diagram is shown in the bottom-right corner in Fig. 1a [7]. Such N/P structure was further validated by the homojunction domains selected for device fabrication in Fig. 3d. To determine the specific atomic distribution in homojunction domains, annular dark-field scanning transmission electron microscopy (ADF-STEM) characterization was performed. The ADF-STEM (Fig. 1c) and the inset of digital diffractogram images, obtained from the edge with uniform thickness of the N/P domain, show the well-aligned crystal lattice and hexagonal symmetry, respectively, suggesting the high crystallinity of the N/P structure. It was reported that Se atoms exhibited higher intensity than S atoms during the ADF-STEM imaging [20], so it can be inferred that the locations with different contrast (e.g., marked by the yellow arrows) in Fig. 1c were the sites where Se atom incorporation took place in MoS2. The further magnified ADF-STEM image (Fig. 1d) clearly identifies the atomic hexagonal rings of MoS2 and the atoms with different contrast at the sites originally corresponding to S atoms, such as the yellow arrow pointed ones, indicating the S atoms were substituted by Se atoms. To examine the characteristics of atomic substitution quantitatively, the gray values of the five atoms (red circled) along the yellow path labeled in Fig. 1d were extracted and plotted in Fig. 1f, in which the changed intensity stems from the different atomic kinds and amount. The five peaks are obtained successively as the yellow arrow passes by the five circled atoms. Thus, the peaks corresponding to Mo and S atoms were resolved according to the atomic arrangement of MoS2. Compared to the referenced Mo atoms (peak 1), S2 units (peak 3 and 4) with no Se replacement display lower gray intensity. Peak 2 with similar intensity to Mo atoms was assigned to the units of S + Se with the top S replaced by Se, while peak 5 exhibiting higher intensity than Mo atoms was attributed to the Se2 units with double S replaced by Se, consistent with the previous work [20]. On the basis of particular intensity, the schematic diagram (Fig. 1e) extracted from Fig. 1d, straightforwardly maps the corresponding distribution of the single and double Se substitution sites, presented with the yellow and white dots, respectively. These atomic incorporation characteristics were further verified by another N/P domain, as shown in Fig. S2a–c. Moreover, EDS was employed to study the spatial distribution of Mo, S, and Se atoms from the atomically thin edge to the thick center in the N/P homojunction alloys. An area with thickness grading was selected. Figure 1g, obtained from the selected area framed in Fig. S2d, illustrated more Mo, S, and Se signal was detected (white dots) when getting closer from the thin edge to the thick center (from the right to the left). This was resulted from the layer-by-layer accumulated elemental signal as thickness continuously increased, confirming the thickness grading.
Afterward, XPS was employed to determine the respective composition changing trend of Mo, S, and Se based on the dominant binding energy peaks as thickness changed. In Fig. S2e, dot 1–4 with gradually increased thickness from the edge to the center, judged by the optical contrast, were selected for elemental content analysis within a single N/P domain. As illustrated and estimated in Fig. S3, from the thin site (dot 1) to the thick site (dot 4), Se-3d% raised from ~ 18.47 to ~ 21.72% gradually, while Mo-3d% kept around ~ 33.5% and S-2p% accordingly dropped from ~ 47.97 to ~ 44.50% progressively. Evidently, XPS results revealed the elemental content changing trend complied with the stoichiometry shown in MoS2(1−x)Se2x. They also demonstrated the formation of a spatial Se composition gradient and resulted in S composition gradient when thickness gradually varied.
To probe the spatial composition and thickness gradient induced impacts on optical properties of the alloy homojunctions, we conducted Raman and micro-PL studies under 532 nm laser excitation, using a confocal Raman spectrometer. Figure 2b shows the position-dependent Raman spectra of the N/P domain displayed in Fig. 2a. In the Raman spectrum attained from dot a, the wavenumber difference between the two dominant eigen peaks from MoS2 (in-plane E 12g mode and out-of-plane A1g mode) is 23 cm−1, indicating the 3L configuration of the edge area (consistent with the AFM height analysis shown in Fig. 1b) [39, 40]. From dot a (at the thin edge) to dot c (at the thick center), this value is continuously increased to 26 cm−1 while E 12g mode redshifts and A1g mode blueshifts. Upon the reported studies, the redshift of the E 12g mode should be mainly originated from the varied S% and increased number of layers [39,40,41]. For the A1g mode, the blueshift is attributed to the stronger electron coupling with increased electron concentration according to the previous study, which could be induced by the changed concentration of S and Se in the thick center of the N/P [42]. It is worth noting that for the pristine binary MoSe2, the in-plane E 12g mode is redshifted and its intensity decreases as the number of layers increases [43]. In contrast, from dot a to dot c, the MoSe2-like E 12g mode (at ~ 273 cm−1) observed in our ternary N/P domain shows a slight blueshift (Fig. 2b) or unnoticeable shift (Fig. S4b) but obvious rising intensity with increased thickness, which can be thereby caused by the Se% variation. Additionally, such phenomena of Raman peak shift and enlarged intensity from dot a to dot c were also observed in the single crystalline ternary MoS2(1−x)Se2x alloy when the Se content was continuously increased [17, 19, 44]. Thus, it was reasonable to deduce that the features of position-dependent Raman spectra were presumably resulted from the Se composition gradient from dot a to dot c, which was further confirmed by the measurement from dot d to dot f (Fig. 2c) and observed in an entirely different 2D flake (Fig. S4a–c).
Figure 2d–f shows the corresponding Raman intensity maps of the E 12g (Mo–Se), E 12g (Mo–S), and A1g (Mo–S) modes, respectively. Obviously, the Raman peak intensity of the three Raman-active modes increases as the layer number increases from the edge to the center, which can be attributed to the Se/S composition and thickness gradient. With continuous increase in the thickness, the optical interference is involved with the coupling of the excitation laser and the emitted Raman scattering near the center [40, 45]. As a result, the Raman peak intensity gradually reduces when moving close to the center for all the three phonon modes. Therefore, the Raman intensity variation features of the three Raman-active modes confirm the N/P configuration with graded thickness. Additionally, Fig. 2h–j shows the position-dependent micro-PL spectra and intensity maps of the N/P domain displayed in Fig. 2g. The thickness of the single crystalline binary MoS2 has an obvious impact on its emission wavelength. Once the thickness increased, the micro-PL spectra slightly redshifted with a small degree < 20 meV but drastically dropped intensity [10, 11]. In contrast, as shown in Fig. 2h, i, from dot a (at the thin edge) to dot c (at the thick center) (from dot d to dot f), the peak redshifted obviously from 677 (695) to 715 nm (713 nm) (corresponding to 100 and 45 meV energy variation, respectively). This peak shift should be attributed to more introduction of Se from the edge to the center [17, 19, 30, 31]. Moreover, as shown in Fig. 2j, the peak intensity underwent unapparent change (e.g., from dot a to dot c) or even strengthened (e.g., from dot d to dot f) as thickness increased. Such irregular intensity variation of exciton peaks can stem from spatial strain inhomogeneity, affecting exciton states and populations and thus PL intensity [46]. The strain inhomogeneity was likely induced by the spatial grading of Se composition and thickness in our cases. In addition, almost no PL phenomenon was observed for the very central (thick) areas, owing to the local field effect [11]. Therefore, the features of PL peak shift and intensity changing can arise from the spatial composition together with thickness gradient. The micro-PL results were further identified in a different N/P 2D flake (Fig. S5). According to the XPS, Raman, and PL results, it was logical to assume that the thin edges of N/P domains can be more MoS2-like, while the thick centers tended to be more MoSe2-like. This suggested that the corresponding Fermi levels can be gradually different from the edges to the centers, which was further determined by the theoretical calculation below.
The presence of spatial Se composition and thickness gradient is able to lead to the formation of a bandgap-graded homojunction and thus a built-in electric field. This is desirable for 2D devices as accurate spatial doping cannot be easily obtained in 2D nanosheets. Figure 3a shows the 3D view of a phototransistor based on the bandgap-graded 2D homojunction. The source and drain electrodes were fabricated by e-beam lithography (EBL) and then e-beam evaporation of Ti/Au (10 nm/50 nm). The optical microscopy image of the selected N/P homojunctions after metallization is also shown in Fig. 3a. Figure 3d identifies the height profiles of the three metal contacts along the dashed lines marked in the AFM images of Fig. 3b, c, which reveal the different height profiles. Although the thickness of each contact increased to different heights, they all started from the bottom 1.9 nm nanosheet and illustrated the thickness grading, which was accompanied with Se composition gradient according to the above material characterization analysis.
Figure 3e shows the output characteristics of the device measured between contacts 1 and 3 (drain and source, respectively, marked in Fig. 3a, distance > 3 µm) under illumination. The back gate voltage was varied from − 3 to 3 V. A rectifying behavior modulated by gate voltage was illustrated, of which the irregular dependence on gate voltage has also been reported in different systems. It can be attributed to the built-in electric field [47, 48]. The zoomed-in linear and logarithmic plots of output curves nearby the origin point are plotted in Fig. 3f, g, respectively, clearly showing a gate-tunable photovoltaic effect. With the gate voltage changing from the negative to the positive value, a consistently shifted VOC from − 0.22 to 0.22 V was obtained. Figure 3h, presenting the map of the drain-source current (the smallest current corresponds to the VOC) in absolute value versus drain–source bias and back gate voltage, further highlights the dependence of VOC on the back gate voltage. This behavior was confirmed on the same device by measuring between contacts 2 and 3 (drain and source distance < 1 µm). Similarly, as displayed in Fig. S6, the output curves obtained under illumination delivered similar reverse current level but larger rectification ratio of forward to reverse current, which should be owing to the lower homojunction barriers when illuminated. Notably, the VOC can be continuously tuned from − 0.27 to 0.26 V as the back gate voltage varied from − 6 to 6 V (Figs. 3i and S7). When the back gate voltage is zero, VOC of − 60 mV is obtained. In comparison, a device based on a non-graded 2D with fixed elemental composition and uniform thickness shows neither rectifying feature nor photovoltaic effect under illumination (Fig. S8a–c). Accordingly, this gate-modulated photovoltaic effect is reasonably attributed to the built-in electric field in the spatially bandgap-graded homojunctions, and the homojunctions were induced by spatial Se composition and thickness gradient in the N/P structure. The photovoltaic effect observed here is stronger and more sensitive (larger VOC and modulated by smaller back gate voltage) than the previously reported ones, which were based on perovskites/2D WSe2 heterojunctions and MoSe2 homojunctions enabled by varied thickness [48, 49]. It is further verified by the self-powered photoresponse properties below.
Based on the calculated band structures of pristine MoS2 and MoSe2 (Fig. S9a, b), the bandgap-graded alloy possesses a type II-like development band alignment (Fig. S9c) along with the doping ratio [21, 22]. Considering the potential offset caused by the asymmetry of the N/P configuration, equivalent band diagrams are schematically shown in Fig. 4a. When illumination is present under zero gate voltage, the photogenerated carriers were separated and collected under the built-in electric field, resulting in modulated Fermi level and a nonzero potential. When applied a negative gate voltage, the built-in electric field is amplified, leading to larger VOC. Reversibly, by applying a positive gate voltage, the built-in electric field is compensated until being changed to a reversed direction, leading to the reversed sign of VOC.
Subsequently, photoresponse characteristics of the phototransistor (measured between contact 1 (drain) and 3 (source)) were studied when illuminated by visible–NIR lights at ambient conditions. As depicted in Fig. 4b, the dark current shows almost linear and symmetric curve passing through the origin point, while the photocurrent exhibits evident rectifying behavior, delivering an on/off ratio of ~ 102 at VDS = − 0.5 V. The bias-dependent photoresponsivity (R) was plotted in the inset. The phototransistor delivered the different R of 23.2, 191.5, and 26.2 A W−1 when excited by 405, 650, and 808 nm lasers at − 0.5 V bias, respectively. Remarkably, high detectivity (D*) up to ~ 1012 Jones was achieved for 650 and 808 nm lights. Figure 4c displays the dependence of photocurrent (Ipc) and R on the incident power density (P) of the 405 nm laser. The scattered dots of Ipc were fitted using the power law, showing a nonlinear trend. This non-unity exponent indicates the presence of carrier traps and their involvement in electron–hole generation and recombination processes in homojunctions. Opposite to the changing trend of Ipc, R decreases with power density of the incident laser increasing. The time-resolved photoswitching characteristics of the device illuminated by the 405 nm laser at VDS = 1 V are displayed in Fig. 4d, illustrating dynamic stability and reproducibility. Figure 4e shows the typical rise time of 51 ms and fall time of 51 ms. In addition, the carrier lifetime \( \tau_{\text{L}} \) on the order of 10−1–100 s level can be extracted by fitting Eq. 3 (Fig. S10) [50]:
here α is a fitting parameter. This long carrier lifetime suggested that electrons can recirculate in the homojunction channels for multiple times following each photoexcited electron–hole generation. As a result, a very high photoconductive gain (G) was estimated to be on the order of 106 ~ 107 from Eq. 4:
here \( \tau_{\text{transit}} \) denotes carrier transit time that was deduced in supporting information (Fig. S8d and Eq. S2).
Given the strong built-in electric field aforementioned, the phototransistors are expected to work without external bias. Figure 5a–c shows the self-powered photoresponse characteristics of the device illuminated by 405, 650, and 808 nm lasers, respectively. Notably, an on/off ratio up to ~ 104 and D* up to ~ 011 Jones were obtained for the 405 nm laser (1.73 mW mm−2). When the device was self-powered, Ipc and R as functions of P of the 405 and 808 nm lasers are displayed in Fig. 5d, e, respectively. Even at zero bias, the device still yielded R of 311 mA W−1 for the 405 nm wavelength. Ipc shows linear dependence on P, indicating that the total number of photogenerated carriers increased proportionally with the absorbed photon number, particularly under 808 nm illumination. Overall, the figures of merit of our phototransistors were competitive or even superior, particularly possessing the self-powered working mode, to those of mostly reported photodetectors based on 2D or multilayer TMDs, 2D layered semiconductors, and artificial heterojunctions under similar conditions [51]. Their performance comparison is shown in Table 1.
4 Conclusions
In summary, we have fabricated visible–NIR and self-powered phototransistors based on N/P homojunctions (spatially composition and thickness graded MoS2(1−x)Se2x) using a one-step and cost-effective CSD approach. ADF-STEM was used to map the distribution of Se dopants and resolve the single and double Se substitution sites. Systematic material characterizations were performed to confirm the gradient of Se composition and thickness within the individual flakes. According to the shifted peaks in micro-PL spectra, the bandgaps of the alloys were continuously tuned from 1.83 to 1.73 eV across the homojunctions, leading to the formation of an internal built-in electric field. Consequently, the strong and sensitive gate-tunable photovoltaic effect was measured, enabling the photodetectors to work without external bias. The highest photoresponsivity of 311 mA W−1, D* of ~ 1011 Jones and on/off ratio up to ~ 104 (illuminated by 405 nm laser) were attained when self-powered operating. The biased devices delivered the champion performance when excited by the lights ranging from 405 to 808 nm: a photoresponsivity of 191.5 A W−1, a specific detectivity up to ~ 1012 Jones, a very high photoconductive gain of 106–107, and a fast photoresponse time in the order of ~ 50 ms. Overall, the realization of the high-performance visible–NIR phototransistors based on such spatially bandgap-graded TMD homojunctions opens up new scope of bandgap engineering and device design.
References
B. Radisavljevic, A. Radenovic, J. Brivio, V. Giacometti, A. Kis, Single-layer MoS2 transistors. Nat. Nanotechnol. 6, 147–150 (2011). https://doi.org/10.1038/nnano.2010.279
O. Lopez-Sanchez, D. Lembke, M. Kayci, A. Radenovic, A. Kis, Ultrasensitive photodetectors based on monolayer MoS2. Nat. Nanotechnol. 8, 497–501 (2013). https://doi.org/10.1038/nnano.2013.100
B.W.H. Baugher, H.O.H. Churchill, Y. Yang, P. Jarillo-Herrero, Optoelectronic devices based on electrically tunable p-n diodes in a monolayer dichalcogenide. Nat. Nanotechnol. 9, 262–267 (2014). https://doi.org/10.1038/nnano.2014.25
Y. Ye, Z.J. Wong, X. Lu, X. Ni, H. Zhu et al., Monolayer excitonic laser. Nat. Photonics 9, 733–737 (2015). https://doi.org/10.1038/nphoton.2015.197
H.J. Chuang, B. Chamlagain, M. Koehler, M.M. Perera, J. Yan et al., Low-resistance 2D/2D ohmic contacts: a universal approach to high-performance WSe2, MoS2, and MoSe2 transistors. Nano Lett. 16, 1896–1902 (2016). https://doi.org/10.1021/acs.nanolett.5b05066
V.K. Sangwan, H.S. Lee, H. Bergeron, I. Balla, M.E. Beck et al., Multi-terminal memtransistors from polycrystalline monolayer molybdenum disulfide. Nature 554, 500–504 (2018). https://doi.org/10.1038/nature25747
H. Xu, X. Han, X. Dai, W. Liu, J. Wu et al., High detectivity and transparent few-layer MoS2/glassy-graphene heterostructure photodetectors. Adv. Mater. 30, 1706561 (2018). https://doi.org/10.1002/adma.201706561
J. Chen, Q. Ma, X.J. Wu, L. Li, J. Liu et al., Wet-chemical synthesis and applications of semiconductor nanomaterial-based epitaxial heterostructures. Nano-Micro Lett. 11, 86 (2019). https://doi.org/10.1007/s40820-019-0317-6
Y. Zhang, T.R. Chang, B. Zhou, Y.T. Cui, H. Yan et al., Direct observation of the transition from indirect to direct bandgap in atomically thin epitaxial MoSe2. Nat. Nanotechnol. 9, 111–115 (2014). https://doi.org/10.1038/nnano.2013.277
G. Eda, H. Yamaguchi, D. Voiry, T. Fujita, M. Chen et al., Photoluminescence from chemically exfoliated MoS2. Nano Lett. 11, 5111–5116 (2011). https://doi.org/10.1021/nl201874w
A. Splendiani, L. Sun, Y. Zhang, T. Li, J. Kim et al., Emerging photoluminescence in monolayer MoS2. Nano Lett. 10, 1271–1275 (2010). https://doi.org/10.1021/nl903868w
Z. Zhang, P. Chen, X. Duan, K. Zang, J. Luo et al., Robust epitaxial growth of two-dimensional heterostructures, multiheterostructures, and superlattices. Science 357, 788–792 (2017). https://doi.org/10.1126/science.aan6814
X. Hong, J. Kim, S.-F. Shi, Y. Zhang, C. Jin et al., Ultrafast charge transfer in atomically thin MoS2/WS2 heterostructures. Nat. Nanotechnol. 9, 682–686 (2014). https://doi.org/10.1038/nnano.2014.167
Y. Chen, X. Wang, G. Wu, Z. Wang, H. Fang et al., High-performance photovoltaic detector based on MoTe2/MoS2 van der waals heterostructure. Small 14, 1703293 (2018). https://doi.org/10.1002/smll.201703293
N. Huo, J. Kang, Z. Wei, S.S. Li, J. Li et al., Novel and enhanced optoelectronic performances of multilayer MoS2-WS2 heterostructure transistors. Adv. Funct. Mater. 24, 7025–7031 (2014). https://doi.org/10.1002/adfm.201401504
M.Y. Li, Y. Shi, C.C. Cheng, L.S. Lu, Y.C. Lin et al., Epitaxial growth of a monolayer WSe2-MoS2 lateral p-n junction with an atomically sharp interface. Science 349, 524–528 (2015). https://doi.org/10.1126/science.aab4097
X.X.W. Zhang, X. Li, T. Jiang, J. Song, Y. Lin et al., CVD synthesis of Mo(1−x)WxS2 and MoS2(1−x)Se2x alloy monolayers aimed at tuning the bandgap of molybdenumdisulfid. Nanoscale 7, 13554–13560 (2015). https://doi.org/10.1039/c5nr02515j
X. Duan, C. Wang, Z. Fan, G. Hao, L. Kou et al., Synthesis of WS2xSe2−2x alloy nanosheets with composition-tunable electronic properties. Nano Lett. 16, 264–269 (2016). https://doi.org/10.1021/acs.nanolett.5b03662
L. Yang, Q. Fu, W. Wang, J. Huang, J. Huang et al., Large-area synthesis of monolayered MoS2(1−x)Se2x with a tunable band gap and its enhanced electrochemical catalytic activity. Nanoscale 7, 10490–10497 (2015). https://doi.org/10.1039/c5nr02652k
Y. Gong, Z. Liu, A.R. Lupini, G. Shi, J. Lin et al., Band gap engineering and layer-by-layer mapping of selenium-doped molybdenum disulfide. Nano Lett. 14, 442–449 (2014). https://doi.org/10.1021/nl4032296
J. Kang, S. Tongay, J. Zhou, J. Li, J. Wu, Band offsets and heterostructures of two-dimensional semiconductors. Appl. Phys. Lett. 102, 012111 (2013). https://doi.org/10.1063/1.4774090
J. Kang, J. Li, S.S. Li, J.B. Xia, L.W. Wang, Electronic structural Moiré pattern effects on MoS2/MoSe2 2D heterostructures. Nano Lett. 13, 5485–5490 (2013). https://doi.org/10.1021/nl4030648
C. Feng, Y. Zhang, Y. Qian, B. Chang, F. Shi et al., Photoemission from advanced heterostructured AlxGa1−xAs/GaAs photocathodes under multilevel built-in electric field. Opt. Express 23, 19478 (2015). https://doi.org/10.1364/OE.23.019478
K. Woo, Y. Kim, W. Yang, K. Kim, I. Kim et al., Band-gap-graded Cu2 ZnSn(S1−x, Sex)4 solar cells fabricated by an ethanol-based, particulate precursor ink route. Sci. Rep. 3, 3069 (2013). https://doi.org/10.1038/srep03069
R.E. Bailey, S. Nie, Alloyed semiconductor quantum dots: tuning the optical properties without changing the particle size. J. Am. Chem. Soc. 125, 7100–7106 (2003). https://doi.org/10.1021/ja035000o
R. Zhou, L. Wan, H. Niu, L. Yang, X. Mao et al., Tailoring band structure of ternary CdSx Se1−x quantum dots for highly efficient sensitized solar cells. Sol. Energy Mater. Sol. Cells 155, 20–29 (2016). https://doi.org/10.1016/j.solmat.2016.04.049
A. Pan, W. Zhou, E.S.P. Leong, R. Liu, A.H. Chin et al., Continuous alloy-composition spatial grading and superbroad wavelength-tunable nanowire lasers on a single chip. Nano Lett. 9, 784–788 (2009). https://doi.org/10.1021/n1803456k
L. Li, H. Lu, Z. Yang, L. Tong, Y. Bando et al., Bandgap-graded CdSxSe1−x nanowires for high-performance field-effect transistors and solar cells. Adv. Mater. 25, 1109–1113 (2013). https://doi.org/10.1002/adma.201204434
X. Zhuang, C.Z. Ning, A. Pan, Composition and bandgap-graded semiconductor alloy nanowires. Adv. Mater. 24, 13–33 (2012). https://doi.org/10.1002/adma.201103191
H. Li, Q. Zhang, X. Duan, X. Wu, X. Fan et al., Lateral growth of composition graded atomic layer MoS2(1−x)Se2x nanosheets. J. Am. Chem. Soc. 137, 5284–5287 (2015). https://doi.org/10.1021/jacs.5b01594
S. Zheng, L. Sun, T. Yin, A.M. Dubrovkin, F. Liu et al., Monolayers of WxMo1−xS2 alloy heterostructure with in-plane composition variations. Appl. Phys. Lett. 106, 63113 (2015). https://doi.org/10.1063/1.4908256
G. Kresse, D. Joubert, From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758 (1999). https://doi.org/10.1103/PhysRevB.59.1758
G. Kresse, J. Furthmüller, Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996). https://doi.org/10.1016/0927-0256(96)00008-0
S. Grimme, Semiempirical GGA-type density functional constructed with a long-range dispersion correction. J. Comput. Chem. 27, 1787–1799 (2006). https://doi.org/10.1002/jcc.20495
S. Steiner, S. Khmelevskyi, M. Marsmann, G. Kresse, Calculation of the magnetic anisotropy with projected-augmented-wavemethodology and the case study of disordered Fe1−xCox alloys. Phys. Rev. B 93, 224425 (2016). https://doi.org/10.1103/PhysRevB.93.224425
J. Zhu, H. Xu, G. Zou, W. Zhang, R. Chai et al., MoS2 -OH bilayer-mediated growth of inch-sized monolayer MoS2 on arbitrary substrates. J. Am. Chem. Soc. 141, 5392–5401 (2019). https://doi.org/10.1021/jacs.9b00047
G.W. Shim, K. Yoo, S.B. Seo, J. Shin, D.Y. Jung et al., Large-area single-layer MoSe2 and its van der Waals heterostructures. ACS Nano 8, 6655–6662 (2014). https://doi.org/10.1021/nn405685j
X. Wang, Y. Gong, G. Shi, W.L. Chow, K. Keyshar et al., Chemical vapor deposition growth of crystalline monolayer MoSe2. ACS Nano 8, 5125–5131 (2014). https://doi.org/10.1021/nn501175k
H. Li, Q. Zhang, C.C.R. Yap, B.K. Tay, T.H.T. Edwin et al., From bulk to monolayer MoS2: evolution of Raman scattering. Adv. Funct. Mater. 22, 1385–1390 (2012). https://doi.org/10.1002/adfm.201102111
C. Lee, H. Yan, L.E. Brus, T.F. Heinz, J. Hone et al., Anomalous lattice vibrations of single- and few-layer MoS2. ACS Nano 4, 2695–2700 (2010). https://doi.org/10.1021/nn1003937
R. Saito, Y. Tatsumi, S. Huang, X. Ling, M.S. Dresselhaus, Raman spectroscopy of transition metal dichalcogenides. J. Phys.: Condens. Matter 28, 353002 (2016). https://doi.org/10.1088/0953-8984/28/35/353002
N.A. Lanzillo, A.G. Birdwell, M. Amani, F.J. Crowne, P.B. Shah et al., Temperature-dependent phonon shifts in monolayer MoS2. Appl. Phys. Lett. 103, 093102 (2013). https://doi.org/10.1063/1.4819337
P. Tonndorf, R. Schmidt, P. Böttger, X. Zhang, J. Börner et al., Photoluminescence emission and Raman response of monolayer MoS2, MoSe2, and WSe2. Opt. Express 21, 4908 (2013). https://doi.org/10.1364/OE.21.004908
Q. Gong, L. Cheng, C. Liu, M. Zhang, Q. Feng et al., Ultrathin MoS2(1−x)Se2x alloy nanoflakes for electrocatalytic hydrogen evolution reaction. ACS Catal. 5, 2213–2219 (2015). https://doi.org/10.1021/cs501970w
M. O’Brien, N. McEvoy, D. Hanlon, T. Hallam, J.N. Coleman et al., Mapping of low-frequency raman modes in CVD-grown transition metal dichalcogenides: layer number, stacking orientation and resonant effects. Sci. Rep. 6, 19476 (2016). https://doi.org/10.1038/srep19476
W. Hsu, L. Lu, D. Wang, J. Huang, M. Li et al., Evidence of indirect gap in monolayer WSe2. Nat. Commun. 13, 929 (2017). https://doi.org/10.1038/s41467-017-01012-6
D. Jariwala, V.K. Sangwan, C.-C. Wu, P.L. Prabhumirashi, M.L. Geier et al., Gate-tunable carbon nanotube-MoS2 heterojunction p-n diode. Proc. Natl. Acad. Sci. 110, 18076–18080 (2013). https://doi.org/10.1073/pnas.1317226110
H.C. Cheng, G. Wang, D. Li, Q. He, A. Yin et al., Van der waals heterojunction devices based on organohalide perovskites and two-dimensional materials. Nano Lett. 16, 367–373 (2016). https://doi.org/10.1021/acs.nanolett.5b03944
Y. Yang, N. Huo, J. Li, Gate tunable photovoltaic effect in a MoSe2 homojunction enabled with different thicknesses. J. Mater. Chem. C 5, 7051–7056 (2017). https://doi.org/10.1039/c7tc01806a
Y. Ma, Y. Gu, Y. Zhang, X. Chen, S. Xi et al., Carrier scattering and relaxation dynamics in n-type In0.83Ga0.17 As as a function of temperature and doping density. J. Mater. Chem. C 3, 2872–2880 (2015). https://doi.org/10.1039/c4tc02709d
C. Xie, C. Mak, X. Tao, F. Yan, Photodetectors based on two-dimensional layered materials beyond graphene. Adv. Funct. Mater. 27, 1603886 (2017). https://doi.org/10.1002/adfm.201603886
Z. Yin, H. Li, H. Li, L. Jiang, Y. Shi et al., Single-layer MoS2 phototransistors. ACS Nano 6, 74–80 (2012). https://doi.org/10.1021/nn2024557
W. Choi, M.Y. Cho, A. Konar, J.H. Lee, G.B. Cha et al., High-detectivity multilayer MoS2 phototransistors with spectral response from ultraviolet to infrared. Adv. Mater. 24, 5832–5836 (2012). https://doi.org/10.1002/adma.201201909
Y. Lee, J. Yang, D. Lee, Y.H. Kim, J.H. Park et al., Trap-induced photoresponse of solution-synthesized MoS2. Nanoscale 8, 9193–9200 (2016). https://doi.org/10.1039/c6nr00654j
C. Jung, S.M. Kim, H. Moon, G. Han, J. Kwon et al., Highly crystalline CVD-grown multilayer MoSe2 thin film transistor for fast photodetector. Sci. Rep. 5, 15313 (2015). https://doi.org/10.1038/srep15313
Y.H. Chang, W. Zhang, Y. Zhu, Y. Han, J. Pu et al., Monolayer MoSe2 grown by chemical vapor deposition for fast photodetection. ACS Nano 8, 8582–8590 (2014). https://doi.org/10.1021/nn503287m
H. Xu, J. Wu, Q. Feng, N. Mao, C. Wang, J. Zhang, High responsivity and gate tunable graphene-MoS2 hybrid phototransistor. Small 10, 2300 (2014). https://doi.org/10.1002/smll.201303670
J. Schornbaum, B. Winter, S.P. Schießl, F. Gannott, G. Katsukis et al., Epitaxial growth of PbSe quantum dots on MoS2 nanosheets and their near-infrared photoresponse. Adv. Funct. Mater. 24, 5798–5806 (2014). https://doi.org/10.1002/adfm.201400330
L. Ye, H. Li, Z. Chen, J. Xu, Near-infrared photodetector based on MoS2/black phosphorus heterojunction. ACS Photonics 3, 692–699 (2016). https://doi.org/10.1021/acsphotonics.6b00079
Y. Xue, Y. Zhang, Y. Liu, H. Liu, J. Song et al., Scalable production of a few-layer MoS2/WS2 vertical heterojunction array and its application for photodetectors. ACS Nano 10, 573–580 (2016). https://doi.org/10.1021/acsnano.5b05596
Acknowledgements
This work was supported by Grants from the UK EPSRC Future Compound Semiconductor Manufacturing Hub (EP/P006973/1). The authors would also like to acknowledge the financial support from EPSRC (EP/L018330/1, EP/N032888/1), the U.S. Army Research Laboratory under Cooperative Agreement Number W911NF-16-2-0120, the “973 Program—the National Basic Research Program of China” Special Funds for the Chief Young Scientist (2015CB358600), the Excellent Young Scholar Fund from National Natural Science Foundation of China (21422103), and the China Scholarship Council (CSC). The authors also acknowledge the use of the UCL Grace High Performance Computing Facility (Grace@UCL) and associated support services.
Author information
Authors and Affiliations
Corresponding authors
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Xu, H., Zhu, J., Zou, G. et al. Spatially Bandgap-Graded MoS2(1−x)Se2x Homojunctions for Self-Powered Visible–Near-Infrared Phototransistors. Nano-Micro Lett. 12, 26 (2020). https://doi.org/10.1007/s40820-019-0361-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-019-0361-2