Abstract
Grain boundary engineering (GBE) is a practice of improving resistance to grain boundary failure of the material through increasing the proportion of low Σ coincidence site lattice (CSL) grain boundaries (special grain boundaries) in the grain boundary character distribution (GBCD). The GBCD in a cold rolled and annealed Fe-18Cr-18Mn-0.63N high-nitrogen austenitic stainless steel was analyzed by electron back scatter diffraction (EBSD). The results show that the optimization process of GBE in the conventional austenitic stainless steel cannot be well applied to this high-nitrogen austenitic stainless steel. The percentage of low ΣCSL grain boundaries could increase from 47.3% for the solid solution treated high-nitrogen austenitic stainless steel specimen to 82.0% for the specimen after 5% cold rolling reduction and then annealing at 1423 K for 10 min. These special boundaries of high proportion effectively interrupt the connectivity of conventional high angle grain boundary network and thus achieve the GBCD optimization for the high-nitrogen austenitic stainless steel.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
M. Diener and M.O. Speidel, Mater. Manuf. Processes 19 (2004) 111.
Z.Z. Yuan, Q.X. Dai, X.N. Cheng, K.M. Chen and W.W. Xu, Mater. Sci. Eng. A 475 (2008) 202.
H. Hänninen, J. Romu, R. Ilola, J. Tervo and A. Laitinen, J. Mater. Process. Technol. 117 (2001) 424.
D. López, N.A. Falleiros and A.P. Tschiptschin, Wear 263 (2007) 347.
G. Stein, I. Hucklenbroich and M. Wagner, Mater. Sci. Forum 318–320 (1999) 167.
M. Ogawa, K. Hiraoka, Y. Katada, M. Sagara and S. Tsukamoto, ISIJ Int. 42 (2002) 1391.
P.H. Pumphrey, In: G.A. Chadwick and D.A. Smith (Eds.), Special High Angle Boundaries, Grain Boundary Structure and Properties, Academic Press, London, 1976, pp.13–19.
X.Y. Fang, K. Zhang, H. Guo, W.G. Wang and B.X. Zhou, Mater. Sci. Eng. A 487 (2008) 7.
X.Y. Fang, W.G. Wang, Z.X. Cai, C.X. Qin and B.X. Zhou, Mater. Sci. Eng. A 527 (2010) 1571.
C.L. Hu, S. Xia, H. Li, T.G. Liu, B.X. Zhou, W.J. Chen and N. Wang, Corros. Sci. 53 (2011) 1880.
Y. Wang, J. Kaneda and N. Shigenaka, Corros. Eng. 60 (2011) 141.
M. Shimada, H. Kokawa, Z.J. Wang, Y.S. Sato and I. Karibe, Acta Mater. 50 (2002) 2331.
M. Michiuchi, H. Kokawa, Z.J. Wang, Y.S. Sato and K. Sakai, Acta Mater. 54 (2006) 5179.
R. Valerie and J. Richard, Mater. Sci. Eng. A 524 (2009) 134.
O.V. Mishin, V.Y. Gertsman, I.V. Alexandrov and R.Z. Valiev, Mater. Sci. Eng. A 212 (1996) 281.
K. Shigeaki, H. Masashi, T. Sadahiro and W. Tadao, Procedia Eng. 10 (2011) 112.
B. Ravi Kumar, S. K. Das, B. Mahato, A. Das and S. Ghosh Chowdhury, Mater. Sci. Eng. A 454–455 (2007) 239.
M. Sekine, N. Sakaguchi, M. Endo, H. Kinoshita, S. Watanabe, H. Kokawa, S. Yamashita, Y. Yano and M. Kawai, J. Nucl. Mater. 414 (2011) 232.
E.A. West and G.S. Was, J. Nucl. Mater. 392 (2009) 264.
J.A. Basinger, E.R. Homer, D.T. Fullwood and B.L. Adams, Scr. Mater. 53 (2005) 959.
S.H. Kim, U. Erb, K.T. Aust and G. Palumbo, Scr. Mater. 44 (2001) 835.
V.Y. Gertsman, M. Janecek and K. Tangri, Acta Mater. 44 (1996) 2869.
F. Shi, X.W. Li, Y. Qi and C.M. Liu, Steel Res. Int. (2013). (in press)
H. Kokawa, W.Z. Jin, Z.J. Wang, M. Michiuchi, Y.S. Sato, W. Dong and Y. Katada, Mater. Sci. Forum 539–543 (2007) 4962.
W.G. Wang and B.X. Zhou, in: the 11th procceding of Chinese Stereology and Image Analysis, Chinese Society for Stereology, Ningbo, China, October 17–21, 2006. (in Chinese)
V. Randle, Acta Mater. 52 (2004) 4067.
M. Kumar, A.J. Schwartz and W.E. King, Acta Mater. 50 (2002) 2599.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Shi, F., Li, X., Hu, Y. et al. Optimization of grain boundary character distribution in Fe-18Cr-18Mn-0.63N high-nitrogen austenitic stainless steel. ACTA METALL SIN 26, 497–502 (2013). https://doi.org/10.1007/s40195-013-0323-5
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-013-0323-5