Abstract
The thermo-mechanical properties of microbumps serving as interconnects between Si chips in three-dimensional integrated circuits were examined in this study. Arrays of SnAg microbumps were subjected to temperature cycling tests up to 2500 cycles. Extensive cracks formed in the microbumps, and some of them propagated across the entire microbump. A microstructural analysis by electron back scattering diffraction indicated that the cracks propagated along two paths: Sn grain boundaries with high misorientation angles and SnAg/Ni3Sn4 interfaces. The average Sn grain size was only 7.4 μm, implying a large proportion of grain boundaries per unit volume, which facilitated crack propagation across the microbump of 20 μm in diameter.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
K. N. Tu, Solder Joint Technology, Springer, New York, USA (2007).
D. A. Shnawah, M. F. M. Sabri, and I. A. Badruddin, Microelectron. Reliab. 52, 90 (2012).
S. Terashima, Y. Kariya, T. Hosoi, and M. Tannaka, J. Electron. Mater. 32, 1527 (2003).
Y. Kariya, T. Hosoi, S. Terashima, M. Tanaka, and M. Otsuka, J. Electron. Mater. 33, 321 (2004).
D. R. Frear, J. W. Jang, J. K. Lin, and C. Zhang, JOM 53, 28 (2001).
X. Liu, Q. Chen, V. Sundaram, M. Simmons-Matthews, K. P. Wachtler, R. R. Tummala, and S. K. Sitaraman, Electronic Components and Technology Conference (ECTC), 2011 IEEE 61st, p. 1190, IEEE, Lake Buena Vista, USA (2011).
H. Cheng, Y. Tsai, S. Lu, and W. Chen, IEEE Trans. Compon. Packag. Manuf. Technol. 3, 2037 (2013).
T. R. Bieler, H. Jiang, L. P. Lehman, T. Kirkpatrick, and E. J. Cotts, IEEE Trans. Compon. Packag. Technol. 31, 370 (2008).
J. G. Lee, A. Telang, K. N. Subramanian, and T. R. Bieler, J. Electron. Mater. 31, 1152 (2002).
Y. Shen and C. Chen, Scr. Mater. 128, 6 (2017).
J. Sylvestre and A. Blander, J. Electron. Mater. 37, 1618 (2008).
C. Lee, K. Kao, R. Cheng, C. Zhan, and T. Chang, Microelectron. Eng. 120, 138 (2014).
S. Lu, J. Juang, H. Cheng, Y. Tsai, T. Chen, and W. Chen, IEEE Trans. Device Mater. Rel. 12, 296 (2012).
M. A. Matin, E. W. C. Coenen, W. P. Vellinga, and M. G. D. Geers, Scr. Mater. 53, 927 (2005).
C. Zhan, C. Chuang, J. Juang, S. Lu, and T. Chang, Electronic Components and Technology Conference (ECTC), 2010 Proceedings 60th, p. 1043, IEEE, Las Vegas, USA (2010).
M. Abtew and G. Selvaduray, Mat. Sci. Eng. R. 27, 95 (2000).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chu, YC., Chen, C., Kao, N. et al. Effect of Sn grain orientation and strain distribution in 20-μm-diameter microbumps on crack formation under thermal cycling tests. Electron. Mater. Lett. 13, 457–462 (2017). https://doi.org/10.1007/s13391-017-7041-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13391-017-7041-5