Abstract
LiMnBO3 is synthesized via solid state reaction at various calcination temperatures, in order to investigate their lithium electrochemical behavior for Li-ion batteries. At lower calcination temperature, LiMnBO3 is composed of mostly monoclinic phase, with a small amount of hexagonal phase, but the ratio of hexagonal/monoclinic phase increases with an increase of calcination temperature, resulting in almost pure hexagonal phase at 800°C. Generally, monoclinic/hexagonal mixed phased LiMnBO3 displays better lithium electrochemical performance. While the pristine LiMnBO3 shows very low capacity, carbon-incorporated LiMnBO3 shows hugely improved charge-discharge capacity, in all samples. The maximum capacity, 108.2 mAh/g after 50 cycles, is obtained from LiMnBO3/C composite calcined at 600°C.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
J. B. Goodenough and Y. Kim, Chem. Mater. 22, 5872 (2010).
T. B. Reddy, Linden’s Handbook of Batteries, Fourth ed., McGraw Hill, New York (2011).
A. K. Padhi, K. S. Nanjundaswamy, and J. B. Goodenough, J. Electrochem. Soc. 144, 1188 (1997).
H. Song, K. T. Lee, M. G. Kim, L. F. Nazar, and J. Cho, Adv. Funct. Mater. 20, 3818 (2010).
R. Mukherjee, R. Krishnan, T.-M. Lu, and N. Koratkar, Nano Energy 1, 518 (2012).
B. L. Ellis, K. T. Lee, and L. F. Nazar, Chem. Mater. 22, 691 (2010).
Y. Oh, S. Nam, S. Wi, S. Hong, and B. Park, Electron. Mater. Lett. 8, 91 (2012).
M.-S. Yoon, M. Islam, Y. M. Park, and S.-C. Ur, Electron. Mater. Lett. 9, 187 (2013).
R. Dominko, J. Power Sources 184, 462 (2008).
T. Muraliganth, K. R. Stroukoff, and A. Manthiram, Chem. Mater. 22, 5754 (2010).
V. Legagneur, Y. An, A. Mosbah, R. Portal, A. Le Gal La Salle, A. Verbaere, D. Guyomard, and Y. Piffard, Solid State Ionics 139, 37 (2001).
A. Yamada, N. Iwane, Y. Harada, S. Nishimura, Y. Koyama, and I. Tanaka, Adv. Mater. 22, 3583 (2010).
L. Chen, Y. Zhao, X. An, J. Liu, Y. Dong, Y. Chen, and Q. Kuang, J. Alloy. Compd. 494, 415 (2010).
Y. Z. Dong, Y. M. Zhao, Z. D. Shi, X. N. An, P. Fua, and L. Chen, Electrochim. Acta 53, 2339 (2008).
J. C. Kim, C. J. Moore, B. Kang, G. Hautier, A. Jain, and G. Ceder, J. Electrochem. Soc. 158, A309 (2011).
S. Afyon, D. Kundu, F. Krumeich, and R. Nesper, J. Power Sources 224, 145 (2013).
O. S. Bondareva, M. A. Simonov, Y. K. Egorovtismenko, and N. V. Belov, Sov. Phys. Crystallogr. 23, 269 (1978).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lee, YS., Lee, H. Structure and electrochemical behavior of LiMnBO3 synthesized at various temperatures. Electron. Mater. Lett. 10, 253–258 (2014). https://doi.org/10.1007/s13391-013-3170-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13391-013-3170-7