Abstract
Lead-free 0.98(Na0.5K0.5Lix)NbO3-0.02Ba(Zr0.52Ti0.48)O3 piezoelectric ceramics were investigated. The experimental results show that Li content strongly affects the orthorhombic-tetragonal morphotropic phase boundary (MPB) which results in different piezoelectric properties. The phase transition composition shows a range from 0.05 to 0.1. The sample with a composition of x = 0.1 showed the maximum values of piezoelectric coefficient (d 33= 201 ρC/N), electromechanical coupling coefficient (k p= 39%), and remnant polarization (P r= 21 μC/cm2).
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
P. Hansen, D. Hennings, and H. Schreinemacher, J. Am. Ceram. Soc. 81, 1369 (1998).
H. Kishi, N. Kohzu, and J. Sugino, J. Eur. Ceram. Soc. 20, 1997 (2000).
S. P. Nam, S. G. Lee, S. G. Bae, and Y. H. Lee, J. Electrical Engineering & Technology, 2, 98 (2007).
S. Anwar, P. R. Sagdeo, and N. P. Lalla, Solid State Commun. 138, 331 (2006).
B. J. Sung, E. W. Lee, and J. G. Lee, J. Electrical Engineering & Technology, 3, 293 (2008).
I. J. Cho, K. S. Yun, and H. J. Nam, J. Electrical Engineering & Technology, 6, 119 (2011).
M. Matsubara, T. Yamaguchi, K. Kikuta, and S. Hirano, Jpn. J. Appl. Phys. 43, 7159 (2004).
W. K. Jeung, S. M. Choi, and Y. J. Kim, J. Electrical Engineering & Technology, 1, 263 (2006).
S. J. Zhang, R. Xia, T. R. Shrout, G. Z. Zang, and J. F. Wang, J. Appl. Phys. 100, 104108 (2006).
H. J. Bae, J. Koo, and J. P. Hong, J. Electrical Engineering & Technology, 1, 120 (2006).
G. L. Yuan and S. W. Or, Appl. Phys. Lett. 88, 062905 (2006).
M. S. Kim, Y. M. Jeon, Y. M. IM, Y. H. Lee, and T. H. Nam, Trans. Electr. Electron. Mater. 12, 20 (2011).
S. H. Lee, J. Electrical Engineering & Technology, 2, 102 (2007).
H.-J. Noh, S. G. Lee, and S. P. Nam, J. Electrical Engineering & Technology, 4, 527 (2009).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lee, SH., Kim, HJ., Lee, SG. et al. Electrical properties of lead-free 0.98(Na0.5K0.5Lix)NbO3-0.02Ba(Zr0.52Ti0.48)O3 ceramics. Electron. Mater. Lett. 8, 43–45 (2012). https://doi.org/10.1007/s13391-011-1063-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13391-011-1063-1