Abstract
CuS nano/submicro materials with different morphologies were synthesized with spherical, tubular, leaf-like and strip type structures in a simple aqueous system under microwave irradiation and sunlight and employing Cu (CH3COO)2, CuSO4·5H2O, CuCl2, and as copper source and H2NCSNH2, Na2S2O3·5H2O and CH3CSNH2 as sulfur sources. The starting materials were used without assistance of any surfactant or template. An X-ray powder diffraction pattern confirms that the product was CuS with hexagonal phase. Scanning electron microscopy was used to observe the morphologies of the product. Different Phase transitions in CuS with respect to temperature are studied by DSC/TGA. The dependence of morphologies of product on different experimental conditions was also discussed.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Since the past few years, researchers are showing inclusive concentration on the study of the appropriate control over the size and shape of Nanomaterials. Nanomaterials show illustrious and exceptional chemical, optical, catalytic, magnetic, and electronic properties depending on the size of the nanoparticles (Shipway et al. 2000; Wong et al. 2002). Self-assembly technique offers chances to utilize the distinctive optical and electronic properties of nanoparticles and promise to investigate new prospectively collective trends (Lu et al. 2002). The assembly of nanoparticles is understood through intermolecular force, electrostatic interaction, and hydrogen bonding, etc. Thus, to synthesize nanomaterials effectively by the means of self-assembly, an elegant reaction is mandatory to fabricate nanoparticles with a fine size distribution and a high extent of shape control, and to accumulate the formed nanoparticles into a desired nanostructure concurrently (Brust and Kiely 2002), such as ordered clusters (Brousseau et al. 1999), spherical shape (Boal et al. 2000), and tubular shape (Wu et al. 2006; Ni et al. 2004). On the other hand, compared with the synthesis of distinct nanoparticles, the well-defined superstructures of nanoparticles by self-assembly is a challenge in material science. Copper monosulfide (CuS) is renowned as one of the vital transition metal semiconductors (Cui et al. 2004) It can also be used as p-type semiconductors (Sakamoto et al. 2003). CuS covellite stacked CuS4–CuS3–CuS4 layers which are held together by covalent S–S bonds (Nair and Nair 1989) thus introducing notable properties in it. As a useful mineral, have outstanding potential optoelectronic material. It is a potential candidate for solar cell application, IR detectors, sensors, electrochemistry cells, and catalysts (Yang et al. 1997; Ahmadi et al. 1996; Lindroos et al. 2000; Erokhina et al. 2003; Podder et al. 2005; Setkus et al. 2001; Blachnik and Muller 2000; Rodriguez et al. 2000; Huang et al. 2001), There are many ways adopted to the synthesize CuS, such as solid-state reaction (Wang et al. 2006), hydrothermal synthesis (Tezuka et al. 2007; Jiang et al. 2005) sonochemical treatment (Xu et al. 2006), and photochemical deposition method (Yang et al. 1997). In this current research, micro- and nano-sized CuS material with different morphologies such as assemblies of nanoparticles into solid spheres, leaf-like and strip-type structures were successfully synthesized from different copper and sulfur sources in aqueous medium by exposure of microwave irradiation and under sunlight. No templates and catalysts were used in the method, which is very simple and novel.
Experimental work
Materials
All reagents used in this experiment were of analytical grade purity, purchased from the commercial market, and were used without further purification. For all the reactions, the copper acetate mono hydrated Cu (CH3COO)2·H2O, copper chloride CuCl2 and copper sulfate pantahydrate CuSO4·5H2O were used as Cu sources, and thiourea (Tu) H2NCSNH2, thioacetamide CH3CSNH2 and sodium thiosulfate pantahydrate Na2S2O3·5H2O were used as sulfur sources, respectively.
Sample 1
In this sample H2NCSNH2 as sulfur source provides the sulfur ion for the reaction and similarly Cu (CH3COO)2·H2O as copper sources provides the copper ion for the reaction. Solutions were prepared for copper and sulfur sources for required molarities in 1:2 ratios. Then, solution of copper source was added to solution of sulfur source dropwise under tough stirring condition. The mixed solution was then treated under microwave irradiation (2.45 GHz) at 160 W for 25 min, black ppt were formed, which were collected and washed with distil water and ethanol many times.
Sample 2 and 3
In 2nd and 3rd samples CuCl2 and Na2S2O3·5H2O were used as copper and sulfur sources; aqueous solution with 2:3 molar ratio were prepared for copper and sulfur sources, respectively; dropwise addition under stirring condition was done as in sample 1 and then mixed green solution was treated in two different environments, employing microwave irradiation (180 W, 30 min) and under sunlight (max day temp ~38°C); products were collected in the form of black ppt and then washed again and again with distilled water and ethanol.
Sample 4
We dissolved 7 mmol CuSO4·5H2O and 21 mmol CH3CSNH2 in 100 mL water separately and then added sulfur source solution into cooper source solution dropwise slowly under stirring condition; light green solution formed, which is treated under microwave irradiation by a domestic microwave oven at 180 W power for 30 min; black ppt formed, which were collected for washing with distilled water and ethanol many time (Table 1).
Powder X-ray diffraction (XRD) data were recorded and collected on the XRD model MPD X’PERT PRO of PANalytical Company Ltd., Holland, using Cu Kα as characteristic radiation (λ = 0.15418 nm) with θ–θ configuration. The measurements were made in 2θ ranging from 20° to 70°. Study was mainly done by the software X’Pert HighScore of the same company. Scanning electron microscopy (SEM) images were taken using a scanning electron microscope (JOEL JSM-6480). a Differential Scanning Calorimeter (DSC) and thermal thermogravimetric analysis (TGA) were performed by SDT Q600 of TA Instrument in control environment for thermal Oxidation, weight loss, and Phase changes in Copper Sulfide.
Characterization of the product
Figure 1 give the XRD patterns for the synthesized products. Samples were well crystallized. All diffraction peaks can be indexed as the hexagonal CuS by comparison with data from JCPDS file no. 00-001-1281 with lattice constants a = 3.8020 Å, b = 3.8020 Å and c = 16.4300 Å; no other characteristic peaks of any other impurity were observed.
The morphologies of the as-prepared CuS nanotubes were investigated by SEM. In Fig. 2a, tubes and some aggregated particles were observed with an average thickness, or diameter of tubes is 150 nm. The length of the tubes is some microns. Fig. 2a, b illustrates other SEM images, which were magnified by 30,000 and 40,000 times. In these images copper sulfide nanotubes were more prominent and can be seen easily.
The morphologies of the as-synthesis nanospheres were investigated by SEM (Fig. 3). Many spheres and cumulated particles are observed. In Fig. 3a, besides some aggregated particles, mostly spheres have radius in the range of 400–600 nm. Figure 3b shows another SEM image, which was magnified 20,000 times; a few particles can be visibly seen on the spheres. Figure 3a, b shows that the size distribution is not very wide.
For sample 2, the leaf-like morphology was observed in SEM images, as shown in Fig. 4a, b. These leaves have very sharp edges; the average length of these leaves is 2.5 µm, but at the edges are very thin as compared with length, which is nearly of 200 nm; here we can also see aggregated nano particle around the leaves.
The third sample prepared under sunlight has solid strip-type morphology which is clearly observed in Fig. 5. These strips have length and width of few microns; this sample was treated under sunlight which possesses a range of radiation of different frequency; that is why they have a random type of shape.
It was established that the morphologies of the product were associated with the molar ratio of copper and sulfur sources, the starting materials. Three solutions were prepared with different copper and sulfur sources having molar ratios of 1:3 and 2:3, using different environment. In our experiment, the system contains only three components: water, copper and sulfur ion sources. The arrangement and self-assembly of CuS nanoparticles are associated with the interaction between copper and sulfur ion sources, in sample 1, During the synthesis, Cu (CH3COO)2 reacts with H2NCSNH2 in water in numerous steps and copper complex ([Cu(H2NCSNH2)]2+) was produced. Then, the complex was decomposed to CuS by microwave irradiation (Chen et al. 2003). H2NCSNH2 and H2O react to produce H2S. Afterward, microwave irradiation decomposed H2S (Huang et al. 2004). S2− produced and further reacted with Cu2+ to produce CuS; in sample 4, CH3CSNH2 reacts with copper source in similar fashion as H2NCSNH2:
For sample 2 and 3, CuCl2 and Na2S2O3 are used as copper and sulfur sources.
It is well known that a S2O −23 ion can hydrolyze to form H2S, which reacts with Cu+2 to produce CuS.
Availability of Sulfur and copper ions play very important role in the formation of different morphologies; when we kept the ratio as 2:3, S2− coordinated with Cu2+ to form CuS nanoparticles, S2− ions are more then Cu2+; they could not aggregate with CuS in max dimension, so two-dimensional structure was obtained. When we use 1:3 ratio, S2− ions had many more ways to aggregate with Cu2+ and that is why spherical morphology was formed.
From the above discussion it may be concluded that, with change in nature of irradiation and molar ratio, reaction kinetics are strongly affected and morphology of the product may be changed.
Thermal behavior of CuS
Differential Scanning Calorimeter (DSC) and thermal thermogravimetric analyses (TGA) for CuS were done by SDT Q600 of TA Instrument in air; the thermal decomposition curves (DSC/TGA) of copper sulfides (CuS) are depicted in Fig. 5.
Mainly, the thermal decomposition of natural and synthesized CuS studies reveals the involvement of four steps (Chen et al. 2006; Kontny et al. 2000; Godoiková et al. 2006):
-
1.
Formation of sulfides (Cu2S) with lesser sulfur content linked with evolved SO2.
-
2.
Oxidation of the presented sulfides moreover to copper oxides (Cu2O and CuO).
-
3.
By reaction of copper oxide, oxygen and releasing SO2, oxysulfates (CuSO4, and CuO·CuSO4) are formed
-
4.
Decomposition of oxysulfates gives CuO
CuS suffers a minute mass loss at 275°C, which is due to the partial conversion of CuS to Cu2S. Conversion to Cu2S is an exothermal reaction; corresponding exothermic peak appears out at 270°C in the DSC as clearly seen in Fig. 6. It was followed by a mass increment of 20% at 380°C, which is related to the oxidation of copper sulfides (CuS, Cu2S) to CuSO4 and again more 10% mass increment due to CuO·CuSO4 formation; then a huge mass loss took place after 700–830°C, which is said to have been caused by the conversion of CuO·CuSO4 and CuSO4 to CuO; corresponding endothermic peak emerges at 820 (Table 2).
Conclusion
CuS with Different Morphologies has been successfully prepared in a simple aqueous base system, using different copper and sulfur ion sources, treated under microwave irradiation and sunlight. Experimental results shows fine morphology (spherical, tubular leave-like, strip-type) of synthesized CuS. The time, nature of radiation (microwave or Sunlight), power of the microwave oven and the molar ratio of copper and sulfur sources effect the formation of products. Uniform structure was abstained by using microwave irradiation due to cyclic process. The decomposition of copper sulfide (CuS) is multifaceted in nature. The related solid state transformations and phase changes depend upon synthesizing route. Thermal decomposition of CuS gives Cu2S at 275°C then converted to CuSO4 at 380°C, and then CuO·CuSO4 formed at 500°C, CuSO4 shows much stability and decomposed at 780°C into CuO.
References
Ahmadi TS, Wang ZL, Green TC, Henglein A, El-Sayed MA (1996) Shape-controlled synthesis of colloidal platinum nanoparticles. Science 272:1924
Blachnik R, Muller A (2000) The formation of Cu2S from the elements: copper used in form of powders. J Thermochim Acta 361:31
Boal AK, Ilhan F, De Rouchey JE, Thurn-Albrecht T, Russell TP, Rotello VM (2000) Self-assembly of nanoparticles into structured spherical and network aggregates. Nature 404:746
Brousseau LC, Novak JP, Marinakos SM, Feldheim DL (1999) Assembly of phenylacetylene-bridged gold nanocluster dimers and trimers. Adv Mater 11:447
Brust M, Kiely CJ (2002) Some recent advances in nanostructure preparation from gold and silver particles: a short topical review. Colloids Surf A 202:175
Chen D, Tang K, Shen G, Sheng J, Fang Z, Liu X, Zheng H, Qian Y (2003) Microwave-assisted synthesis of metal sulfides in ethylene glycol. Mater Chem Phys 82:206
Chen SP, Mung XX, Shuai O, Jiao BJ, Gao SL, Shi QZ (2006) Thermochemistry of europium and dithiocarbamate complex Eu(C5H8NS2)3(C12H8N2). J Therm Anal Cal 86:767
Cui XJ, Yu SH, Li LL, Li K, Yu B (2004) Fabrication of Ag2SiO3/SiO2: composite nanotubes ua. one-step sacrificial templating solution approach. Adv Mater 16:1109
Erokhina S, Erokhin V, Nicolini C, Sbrana F, Ricci D, Di Zitti E (2003) Microstructure origin of the conductivity differences in aggregated CuS films of different thickness. Langmuir 19:766–771
Godoiková E, Balá P, Criado JM, Real C, Gock E (2006) Thermal behaviour of mechanochemically synthesized nanocrystalline CuS. Thermochim Acta 440:19
Huang MH, Mao S, Feick H, Yan H, Wu Y, Kind H, Weber E, Russo R, Yang P (2001) Room-temperature ultraviolet nanowire nanolasers. Science 292:1897
Huang NM, Kan CS, Khiew PS, Radiman S (2004) Single w/o microemulsion templating of CdS nanoparticles. J Mater Sci 39:2411
Jiang C, Zhang W, Zou G, Xu L, Yu W, Qian Y (2005) Hydrothermal fabrication of copper sulfide nanocones and nanobelts. Mater Lett 59:1008
Kontny A, De Wall H, Sharp TG, Pósfai M (2000) Mineralogy and magnetic behavior of pyrrhotite from a 260°C section at the KTB drilling site, Germany. Am Mineral 85:1416
Lindroos S, Arnold A, Leskela M (2000) Growth of CuS thin films by the successive ionic layer adsorption and reaction method. J Appl Surf Sci 158:75
Lu Q, Gao F, Zhao D (2002) One-step synthesis and assembly of copper sulfide nanoparticles to nanowires, nanotubes, and nanovesicles by a simple organic amine-assisted hydrothermal process. Nano Lett 2:725
Nair MTS, Nair PK (1989) Chemical bath deposition of CuxS thin films and their prospective large area applications. Semicond Sci Technol 4:191
Ni Y, Liu H, Wang F, Yin G, Hong J, Ma X, Xu Z (2004) Self-assembly of CuS nanoparticles to solid, hollow, spherical and tubular structures in a simple aqueous-phase reaction. Appl Phys A 79:2007–2011
Podder J, Kobayashi R, Ichimura M (2005) Photochemical deposition of CuxS thin films from aqueous solutions. Thin Solid Films 472:71–75
Rodriguez JA, Jirsak T, Dvorak J, Sambasivan S, Fischer D (2000) Reaction of NO2 with Zn and ZnO: photoemission, XANES, and density functional studies on the formation of NO3. J Phys Chem B 104:319
Sakamoto T, Sunamura H, Kawaura H, Hasegawa T, Nakayama T, Aono M (2003) Nanometer-scale switches using copper sulfide. Appl Phys Lett 82:3032
Setkus A, Galdikas A, Mironas A, Simkienė I, Ancutienė I, Janickis V, Kačiulis S, Mattogno G, Ingo GM (2001) Properties of CuxS thin film based structures: influence on the sensitivity to ammonia at room temperatures. Thin Solid Films 391:275–281
Shipway AN, Katz E, Willner I (2000) Nanoparticle arrays on surfaces for electronic, optical, and sensor applications. Chem Phys Chem 1:18
Tezuka K, Sheets WC, Kurihara R, Shan YJ, Imoto H, Marks TJ, Poeppelmeier KR (2007) Synthesis of covellite (CuS) from the elements. Solid State Sci 9:95–99
Wang X, Xu C, Zhang Z (2006) Synthesis of CuS nanorods by one-step reaction. Mater Lett 60:345
Wong MS, Cha JN, Choi KS, Deming TJ, Stucky GD (2002) Assembly of nanoparticles into hollow spheres using block copolypeptides. Nano Lett 2:583
Wu C, Yu S, Chen S, Liu G, Liu B (2006) Large scale synthesis of uniform CuS nanotubes in ethylene glycol by a sacrificial templating method under mild conditions. J Mater Chem 16:3326–3331
Xu JZ, Xu S, Geng J, Li GX, Zhu JJ (2006) The fabrication of hollow spherical copper sulfide nanoparticle assemblies with 2-hydroxypropyl-β-cyclodextrin as a template under sonication. Ultrason Sonochem 13:451
Yang H, Coombs N, Ozin GA (1997) Morphogenesis of shapes and surface patterns in mesoporous silica. Nature 386:692
Open Access
This article is distributed under the terms of the Creative Commons Attribution License which permits any use, distribution and reproduction in any medium, provided the original author(s) and source are credited.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Nafees, M., Ali, S., Rasheed, K. et al. The novel and economical way to synthesize CuS nanomaterial of different morphologies by aqueous medium employing microwaves irradiation. Appl Nanosci 2, 157–162 (2012). https://doi.org/10.1007/s13204-011-0050-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13204-011-0050-z