Abstract
Effect of cerium addition on the microstructure and mechanical properties of an Al-Zn-Mg-Cu alloy have been investigated. In this study, aluminum alloys with up to 0.4% cerium content have been prepared by melting, metal mould casting followed by thermo-mechanical processing. The alloys were extensively characterized by optical and transmission electron microscopy, followed by mechanical property examination by tensile tests as well as nanoindentation tests. It was observed that cerium addition results in up to 5% grain refinement of the cast dendritic structure as well as up to 38% refinement of the heat treated microstructure. Transmission electron microscopy (TEM) has revealed the uniform distribution of fine GP zones and some semi coherent β(MgZn2) precipitates in the Al rich matrix. Further TEM results show that when the Ce content was changed from 0.1% to 0.4%, precipitate size increased from 5 to 50nm and the precipitate morphology changed from spherical to needle shape. Evaluation of mechanical properties through tensile and nano-indentation tests have exhibited that both Young’s modulus and tensile strength increases with Ce addition up to 0.3% and subsequently decrease.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Fu-sheng Pan, Zhou, Shou-ze Shi, Gong-qi, et al., Light Alloy Fabrication Tech., 3 (1990) 1.
Tang Ding-xiang, Wang liang-xuan, Zhao Min-shou, et al., The Chinese Journal of Rare-Earth, 10 (1992) 66.
Yang Yu-chun, Rare-Earth Rare Metal Materials and Eng., 22 (1993) 1–6.
X.-M. Li, Starink M J, Mater. Sci. Technol., 17 (2001) 1324.
Mukhopadhyay A K, Metall. Mater. Trans. A, 30 (1999) 1693.
Belov N A, Khvan A V, Acta Materialia, 55 (2007) 5473.
Min S et al., Rare Metals, 26 (2007) 28.
Xiao D H et.al., Journal of Alloys and Compounds, 352 (2003) 84.
Li Hui-zhong et. al., Trans. Nonferrous Met. SOC. China, 17 (2007) 1194.
Zhihui Li et.al, Materials Characterization, 59 (2008) 278.
Oliver W C and Pharr G M, T. Mater. Res., 7 (1992) 1564.
Min Song, Kanghual Chen and Langpin Huang, Rare Metals, 26 (2007) 28.
Park J Yang W G, Koo C H, Mater. Trans., 44 (2003) 1029.
K, Ardell A J. Metall Trans A, 14 (1983) 1957.
Zhang M et.al., Journal of Materials Processing Technology, 115 (2001) 294.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chaubey, A.K., Mohapatra, S., Jayasankar, K. et al. Effect of cerium addition on microstructure and mechanical properties of Al-Zn-Mg-Cu alloy. Trans Indian Inst Met 62, 539–543 (2009). https://doi.org/10.1007/s12666-009-0090-1
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-009-0090-1