Abstract
The present work has been focused to investigate the mechanical behavior and microstructural characteristics of cryorolled Al 6063 and Al 6061 alloys. Hardness and tensile tests of the cryorolled Al alloys were carried out to understand its deformation behavior. SEM/EBSD was used to characterise the microstructures of cryorolled Al alloys and observed the formation of ultrafine-grained microstructures in the materials due to severe plastic strain induced during cryorolling. XRD was used to analyse the formation of different phases during cryorolling of the Al alloys. It is evident from the present study that UFG Al alloys exhibit higher hardness and strength when compared to the bulk Al alloys due to the grain size, higher dislocation density and precipitation hardening effect. The cryorolled Al 6061 alloys exhibit higher tensile strength (346 MPa) and hardness (120 Hv) as compared to Al 6063 alloys (Tensile strength: 240MPa and Hardness: 96.5 Hv) in the present investigation. The deformation mechanisms of UFG Al alloys contributing to their enhanced strength are discussed.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Williams J C and Starke E A, Acta Materialia, 51 (2003) 5775.
Starke E A and Staley J T, Progress in Aerospace Science, 32 (1996) 131.
Panigrahi S K and Arun kumar V, M.Tech Thesis (2003).
Tan E and Ogel B, Turkis J. Eng. Env. Sci., 31 (2007) 53.
Reiso O, Ph.D Thesis, Norwegian Institute of Technology, (1992).
Meyers M A, Mishra A and Benson D J, Progr. in Materials Science, 51 (2006) 427.
Valiev R Z, Islamgaliev R K and Alexandrov I V, Progr. Mater. Sci., 45 (2000) 103.
Wang Y, Chen M, Zhou F and Ma E, Nature, 419 (2002) 912.
Rangaraju N, Raghuram T, Krishna B V, Rao K P and Venugopal P, Mater Sci Eng A, 398 (2005) 246.
Lee TR, Chang CP and Kao PW, Mater Sci Eng A 408 (2005) 131.
Lee Y B, Shin D H, Park K T and Nam W J, Scripta Materilia, 51 (2004) 355.
Panigrahi S K and Jayaganthan R, Mater. Sci. Eng. A, 400 (2008) 299.
Panigrahi S K and Jayaganthan R, Mater. Lett. 62 (2008) 2626.
Panigrahi S K and Jayaganthan R, Proceedings of International Conference on Recent Trends in Nanoscience and Technology, Kolkata (2006) 66.
Hall E O, Proc. Phys. Soc. B., 64 (1951) 390.
Petch N J, J. Iron Steel Inst., 174 (1953) 25.
Gubicza J, Schiller I, Chinh N Q, Illy J, Horita Z and Langdon T G, Mater. Sci. Eng. A 460 (2007) 77.
Xu C, Furukawa M, Horita Z and Langdon T G, Acta Mater., 53 (2005) 749.
Cubberly W H, Barker H, Benjamin D, ASM Handbook, 9th ed., 2 p 117.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Panigrahi, S.K., Devanand, D. & Jayaganthan, R. A comparative study on mechanical properties of ultrafine-grained Al 6061 and Al 6063 alloys processed by cryorolling. Trans Indian Inst Met 61, 159–163 (2008). https://doi.org/10.1007/s12666-008-0028-z
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-008-0028-z