Abstract
A new approach of removing the phosphorus-rich phase from high-phosphorous iron ore by melt separation at 1573 K in a super- gravity field was investigated. The iron-slag separation by super-gravity resulted in phosphorus being effectively removed from the iron-rich phase and concentrated as a phosphorus-rich phase at a temperature below the melting point of iron. The samples obtained by super-gravity exhibited obvious layered structures. All the iron grains concentrated at the bottom of the sample along the super-gravity direction, whereas the molten slag concentrated in the upper part of the sample along the opposite direction. Meanwhile, fine apatite crystals collided and grew into larger crystals and concentrated at the slag–iron interface. Consequently, in the case of centrifugation with a gravity coefficient of G = 900, the mass fractions of the slag phase and iron-rich phase were similar to their respective theoretical values. The mass fraction of MFe in the iron-rich phase was as high as 97.77wt% and that of P was decreased to 0.092wt%.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
J. Diao, X. Liu, T. Zhang, and B. Xie, Mass transfer of phosphorus in high-phosphorus hot-metal refining, Int. J. Miner. Metall. Mater., 22(2015), No. 3, p. 249.
J. Wu, Z. J. Wen, and M. J. Cen, Development of technologies for high phosphorus oolitic hematite utilization, Steel Res. Int., 82(2011), No. 5, p. 494.
R. C. Guimarães, A. C. Araugo, and A. E. C. Peres, Reagents in igneous phosphate ores flotation, Miner. Eng., 18(2005), No. 2, p. 199.
A. P. L. Nunes, C. L. L. Pinto, G. E. S. Valadão, and P. R. M. Viana, Floatability studies of wavellite and preliminary results on phosphorus removal from a Brazilian iron ore by froth flotation, Miner. Eng., 39(2012), p. 206.
J. T. Gao, L. Guo, and Z. C. Guo, Separation of P phase and Fe phase in high phosphorus oolitic iron ore by ultrafine grinding and gaseous reduction in a rotary furnace, Metall. Mater. Trans. B, 46(2015), No. 15, p. 2180.
J. T. Yu, Z. C. Guo, and H. Q. Tang, Dephosphorization treatment of high phosphorus oolitic iron ore by hydrometallurgical process and leaching kinetics, ISIJ Int., 53(2013), No. 12, p. 2056.
M. J. Fisher-White, R. R. Lovel, and G. J. Sparrow, Phosphorus removal from goethitic iron ore with a low temperature heat treatment and a caustic leach, ISIJ Int., 52(2012), No. 5, p. 797.
W. Yu, T. C. Sun, J. Kou, Y. X. Wei, C. Y. Xu, and Z. Z. Liu, The function of Ca(OH)2 and Na2CO3 as additive on the reduction of high-phosphorus oolitic hematite-coal mixed pellets, ISIJ Int., 53(2013), No. 3, p. 427.
S. J. Bai, S. M. Wen, D. W. Liu, W. D. Zhang, and Y. J. Xian, Catalyzing carbothermic reduction of siderite ore with high content of phosphorus by adding sodium carbonate, ISIJ Int., 51(2011), No. 10, p. 1601.
Z. L. Zhao, H. Q. Tang, and Z. C. Guo, Effects of CaO on precipitation morphology of metallic iron in reduction of iron oxides under CO atmosphere, J. Iron Steel Res., 20(2013), No. 7, p. 16.
L. Guo, J. T. Gao, Y. W. Zhong, H. Gao, and Z. C. Guo, Phosphorus removal of high phosphorous oolitic iron ore with acid-leaching fluidized-reduction and melt-separation process, ISIJ Int., 55(2015), No. 9, p. 1806.
H. Q. Tang, W. D. Liu, H. Y. Zhang, and Z. C. Guo, Effect of microwave treatment upon processing oolitic high phosphorus iron ore for phosphorus removal, Metall. Mater. Trans. B, 45(2014), No. 5, p. 1683.
T. Hamano, S. Fukagai, and F. Tsukihashi, Reaction mechanism between solid CaO and FeOx-CaO-SiO2-P2O5 slag at 1573 K, ISIJ Int., 46(2006), p. 490.
S. Fukagai, T. Hamano, and F. Tsukihashi, Formation reaction of phosphate compound in multi phase flux at 1573 K, ISIJ Int., 47(2007), No. 1, p. 187.
L. X. Zhao, Z. C. Guo, Z. Wang, and M. Y. Wang, Influences of super-gravity field on aluminum grain refining, Metall. Mater. Trans. A, 41(2010), No. 3, p. 670.
L. X. Zhao, Z. C. Guo, Z. Wang, and M. Y. Wang, Removal of low-content impurities from Al by super-gravity, Metall. Mater. Trans. B, 41(2010), No. 3, p. 505.
L. Guo, H. Gao, J. T. Yu, Z. L. Zhang, and Z. C. Guo, Influence of hydrogen concentration on Fe2O3 particle reduction in fluidized beds under constant drag force, Int. J. Miner. Metall. Mater., 22(2015), No. 1, p. 12.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Gao, Jt., Guo, L., Zhong, Yw. et al. Removal of phosphorus-rich phase from high-phosphorous iron ore by melt separation at 1573 K in a super-gravity field. Int J Miner Metall Mater 23, 743–750 (2016). https://doi.org/10.1007/s12613-016-1288-y
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12613-016-1288-y