Abstract
The surface of nodular cast iron (NCI) with a ferrite substrate was rapidly remelted and solidified by plasma transferred arc (PTA) to induce a chilled structure with high hardness and favorable wear resistance. The effect of scanning speed on the microstructure, microhardness distribution, and wear properties of PTA-remelted specimens was systematically investigated. Microstructural characterization indicated that the PTA remelting treatment could dissolve most graphite nodules and that the crystallized primary austenite dendrites were transformed into cementite, martensite, an interdendritic network of ledeburite eutectic, and certain residual austenite during rapid solidification. The dimensions of the remelted zone and its dendrites increase with decreased scanning speed. The microhardness of the remelted zone varied in the range of 650 HV0.2 to 820 HV0.2, which is approximately 2.3–3.1 times higher than the hardness of the substrate. The wear resistance of NCI was also significantly improved after the PTA remelting treatment.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
K.F. Alabeedi, J.H. Abboud, and K.Y. Benyounis, Microstructure and erosion resistance enhancement of nodular cast iron by laser melting, Wear, 266(2009), No. 9–10, p. 925.
J.H. Abboud, Microstructure and erosion characteristic of nodular cast iron surface modified by tungsten inert gas, Mater. Des., 35(2012), p. 677.
K.Y. Benyounis, O.M.A. Fakron, J.H. Abboud, A.G. Olabi, and M.J.S. Hashmi, Surface melting of nodular cast iron by Nd-YAG laser and TIG, J. Mater. Process. Technol., 170(2005), No. 1–2, p. 127.
W.S. Dai, L.H. Chen, and T.S. Lui, SiO2 particle erosion of spheroidal graphite cast iron after surface remelting by the plasma transferred arc process, Wear, 248(2001), No. 1–2, p. 201.
A. Amirsadeghi and M. Heydarzadeh Sohi, Comparison of the influence of molybdenum and chromium TIG surface alloying on the microstructure, hardness and wear resistance of ADI, J. Mater. Process. Technol., 201(2008), No. 1–3, p. 673.
J. Grum and R. Šturm, Microstructure analysis of nodular iron 400–12 after laser surface melt hardening, Mater. Charact., 37(1996), No. 2–3, p. 81.
K.Y. Shi, S.B. Hu, W. Xu, and Q.W. Huang, Surface treatment of 45 steels by plasma beam alloying and plasma surface quenching, Adv. Mater. Res., 129–131(2010), p. 1109.
M. Yan and W.Z. Zhu, Surface treatment of 45 steel by plasma-arc melting, Surf. Coat. Technol., 91(1997), No. 3, p. 183.
L. Bourithis and G.D. Papadimitriou, The effect of microstructure and wear conditions on the wear resistance of steel metal matrix composites fabricated with PTA alloying technique, Wear, 266(2009), No. 11–12, p. 1155.
Q.W. Huang, S.B. Hu, and A.H. Wang, Research development of plasma beam surface strengthening technology, Heat. Treat. Met., 36(2011), No. 8, p. 1.
A. Roy and I. Manna, Laser surface engineering to improve wear resistance of austempered ductile iron, Mater. Sci. Eng. A, 297(2001), No. 1–2, p. 85.
M. Heydarzadeh Sohi, G. Karshenas, and S.M.A. Boutorabi, Electron beam surface melting of as cast and austempered ductile irons, J. Mater. Process. Technol., 153–154(2004), p. 199.
M. Yan, W.Z. Zhu, W. Luo, X.B. Zhang, B.C. Zhou, and X.B. Zhao, Effect of plasma-arc scanning on the wear resistance of gray iron, Mater. Lett., 56(2002), No. 1–2, p. 14.
X. Tong, H. Zhou, L.Q. Ren, Z.H. Zhang, R.D. Cui, and W. Zhang, Thermal fatigue characteristics of gray cast iron with non-smooth surface treated by laser alloying of Cr powder, Surf. Coat. Technol., 202(2008), No. 12, p. 2527.
M.B. Karamış and K. Yıldızlı, Surface modification of nodular cast iron: A comparative study on graphite elimination, Mater. Sci. Eng. A, 527(2010), No. 20, p. 5225.
M. Heydarzadeh Sohi, M. Ebrahimi, H.M. Ghasemi, and A. Shahripour, Microstructural study of surface melted and chromium surface alloyed ductile iron, Appl. Surf. Sci., 258(2012), No. 19, p. 7348.
J. Grum and R. Šturm, Comparison of measured and calculated thickness of martensite and ledeburite shells around graphite nodules in the hardened layer of nodular iron after laser surface remelting, Appl. Surf. Sci., 187(2002), No. 1–2, p. 116.
J.S. Wang, H.M. Meng, H.Y. Yu, Z.S. Fan, and D.B. Sun, Characterization and wear behavior of WC-0.8Co coating on cast steel rolls by electro-spark deposition, Int. J. Miner. Metall. Mater., 16(2009), No. 6, p. 707.
G.F. Sun, R. Zhou, P. Li, A.X. Feng, and Y.K. Zhang, Laser surface alloying of C-B-W-Cr powders on nodular cast iron rolls, Surf. Coat. Technol., 205(2011), No. 8–9, p. 2747.
Y. Sahin, V. Kilicli, M. Ozer, and M. Erdogan, Comparison of abrasive wear behavior of ductile iron with different dual matrix structures, Wear, 268(2010), No. 1–2, p. 153.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Cao, Ht., Dong, Xp., Huang, Qw. et al. Effect of scanning speed during PTA remelting treatment on the microstructure and wear resistance of nodular cast iron. Int J Miner Metall Mater 21, 363–370 (2014). https://doi.org/10.1007/s12613-014-0917-6
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12613-014-0917-6