Abstract
To use the potential heat of molten blast furnace slag completely, a CaO-Al2O3-SiO2 system glass (MSG) was prepared from the molten industrial slag. The corresponding method proposed in this study utilized both slag and its potential heat, improving the production rate and avoiding the environmental pollution. Using appropriate techniques, an MSG with uniform color and superior performances was produced. Based on the experimental results and phase diagram, the chemical composition of MSG by mass is obtained as follows: CaO 27%–33%, SiO2 42%–51%, Al2O3 11%–14%, MgO 6%–8%, and Na2O+K2O 1%–4%. Thermodynamic processes of MSG preparation were analyzed, and the phases and microstructures of MSG were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that alkali metal oxides serve as the fluxes, calcium oxide serves as the stabilizer, and alumina reinforces the Si-O network. XRD and SEM analyses show that, the prepared MSG displays the glass-feature patterns, the melting process is more complete, and the melt viscosity is lowered with an increase in calcium oxide content; however, a continuous increase in slag content induces the crystallization of glass, leading to the formation of glass subphase. The optimum content of molten slag in MSG is 67.37wt%. With respect to bending strength and acid/alkali resistance, the performance of MSG is better than that of ordinary marble.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
A.A. Francis, Conversion of blast furnace slag into new glass-ceramic material, J. Eur. Ceram. Soc., 24(2004), p. 2819.
Z.J. Wang, W. Ni, K.Q. Li, X.Y. Huang, and L.P. Zhu, Crystallization characteristics of iron-rich glass ceramics prepared from nickel slag and blast furnace slag, Int. J. Miner. Metall. Mater., 18(2011), No. 4, p. 455.
D.F. Chen, X.J. Zuo, L.Y. Wen, L.Y. Dong, and G.B. Qiu, Methods and problems of heat recovery from molten blast furnace slag, Tech. Equip. Environ. Pollut. Control, 7(2006), p. 133.
Y.L. Sun, D.W. Zuo, H.Y. Wang, Y.W. Zhu, and J. Li, Mechanism of brittle-ductile transition of a glass-ceramic rigid substrate, Int. J. Miner. Metall. Mater., 18(2011), No. 2, p. 229.
X.J. Hu, Z.S. Ren, G.H. Zhang, L.J. Wang, and K.C. Chou, A model for estimating the viscosity of blast furnace slags with optical basicity, Int. J. Miner. Metall. Mater., 19(2012), No. 12, p. 1088.
H.Y. Liu, H.X. Lu, D.L. Chen, H.L. Wang, H.L. Xu, and R. Zhang, Preparation and properties of glass-ceramics derived from blast-furnace slag by a ceramic-sintering process, Ceram. Int., 35(2009), No. 8, p. 3181.
W.Y. Zhang, H. Gao, and Y. Xu, Sintering and reactive crystal growth of diopside-albite glass-ceramics from waste glass, J. Eur. Ceram. Soc., 31(2011), No. 9, p. 1669.
V. Cannillo, F. Pierli, S. Sampath, and C. Siligardi, Thermal and physical characterisation of apatite/wollastonite bioactive glass-ceramics, J. Eur. Ceram. Soc., 29(2009), No. 4, p. 611.
F.H. ElBatal, M.A. Azooz, and Y.M. Hamdy, Preparation and characterization of some multicomponent silicate glasses and their glass-ceramics derivatives for dental applications, Ceram. Int., 35(2009), No. 3, p. 1211.
F.H. Margha, S.A.M. Abdel-Hameed, N.A.E. Ghonim, S.A. Ali, S. Kato, S. Satokawa, and T. Kojima, Crystallization behaviour and hardness of glass ceramics rich in nanocrystals of ZrO2, Ceram. Int., 35(2009), No. 3, p. 1133.
J. Ma, C.Z. Chen, D.G. Wang, and J.H. Hu, Synthesis, characterization and in vitro bioactivity of magnesium-doped sol-gel glass and glass-ceramics, Ceram. Int., 37(2011), No. 5, p. 1637.
A. Karamanov and M. Pelino, Induced crystallization porosity and properties of sintereds diopside and wollastonite glass-ceramics, J. Eur. Ceram. Soc., 28(2008), No. 3, p. 555.
E. Bernardo, R. Castellan, S. Hreglich, and I. Lancellotti, Sintered sanidine glass-ceramics from industrial wastes, J. Eur. Ceram. Soc., 26(2006), No. 15, p. 3335.
T. Toya, Y. Kameshima, A. Nakajima, and K. Okada, Preparation and properties of glass-ceramics from kaolin clay refining waste (Kira) and paper sludge ash, Ceram. Int., 32(2006), No. 7, p. 789.
E. Bernardo, J. Doyle, and S. Hampshire, Sintered feldspar glass-ceramics and glass-ceramic matrix composites, Ceram. Int., 34(2008), No. 8, p. 2037.
J. Zhou and Y.X. Wang, A novel process of preparing glass-ceramics with pseudo-bioclastic texture, Ceram. Int., 34(2008), No. 1, p. 113.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Xu, Y., Zhang, Yz., Hou, Ly. et al. Preparation of CaO-Al2O3-SiO2 system glass from molten blast furnace slag. Int J Miner Metall Mater 21, 169–174 (2014). https://doi.org/10.1007/s12613-014-0881-1
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12613-014-0881-1