Abstract
Thick trivalent chromium layers were prepared in a modified chromium sulfate bath by pulse plating to replace hexavalent hard chromium coating in industrial fields; layer microstructure development was systematically studied by using electron microscopy and small angle neutron scattering (SANS) to give a model for nucleation and growth behaviors during the pulse plating. Finer columnar grain was formed by pulse plating due to its high nucleation rate at the same current density. Average deposition rate of the trivalent chromium layers is in the range of 32.4 μm/h to 49.7 μm/h. The deposition rate increases as the diameter of cylindrical shape of chromium cluster in a columnar grain is reduced. The highest deposition rate in this study was observed under the conditions of direct current density of 0.4 Acm−2, combined with a rectangular shape pulse current density of 1.5 Acm−2 with a 10/2 on-off time ratio. Most of the inner-cracks of the trivalent chromium layers have dimensions in the range of about 39 nm. Ultrasonic agitation during pulse plating resulted in an increase of neutral salt fog spray life, which is related to smaller crack size and broader size distribution in the trivalent chromium.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
M. S. Chandrasekar and M. Pushpavanam, Electrochem. Acta 53, 3313 (2008).
I. Drela, J. Szynkarczuk, and J. Kubicki, J. Appl. Electrochem. 19, 933 (1989).
H. H. Wan and H. Y. Cheh, J. Electrochem. Soc. 135, 643 (1988).
J. S. Kim, R. H. Song, S. I. Pyun, and H. C. Kim, J. Mater. Sci. 24, 2704 (1989).
Y. Choi, J. Mater. Sci. Lett. 15, 629 (1996).
N. V. Mandich, Plat. Surf. Finish. 84, 108 (1997).
Y. Choi, J. Mater. Sci. 32, 1581 (1997).
Y. Choi, M. Kim, and S. C. Kwon, Surf. Coat. Tech. 169, 81 (2003).
J. C. Puippe, Theory and Practice of Pulse Plating, p. 177, American Electroplaters Society (1986).
Y. Choi, M. Y. Choi, Y. S. Hahn, M. Kim, and S. C. Kwon, Mater. Sci. Forum. 475, 4005 (2005).
S. G. Pyo, D. W. Lee, and S. B. Kim, Met. Mater. Int. 14, 773 (2008).
K. Kohlbrecher, SASFIT (c), version 08.2, PSI, Switzerland (2007).
P. Leisner, G. Bech-Nielsen, and P. Møler, J. Appl. Electrochem. 23, 1232 (1993).
O. M. Bockris, A. K. N. Reddy, and M. Gamboa-Aldeco, Modern Electrochemistry 2A. Fundamentals of Electrodics, 2 nd ed., p. 1083, Kluwer Academic/Plenum Publishers (2000).
M. Jalochowski, M. Hoffmann, and E. Bauer, Phys. Rev. Lett. 51, 7231 (1995).
C. M. Pina, D. Bosbach, M. Prieto, and A. Putnis, J. Cryst. Growth 187, 119 (1998).
R.-J. Roe, Method of X-ray and Neutron Scattering in Polymer Science, p. 15, Oxford University Press, New York (2000).
N. Laversanne, J. Phys. Chem. B 105, 11081 (2001).
Y. Choi, J. Kor. Inst. Met. & Mater. 34, 773 (1996).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Choi, Y. Electro-deposition behaviors of trivalent chromium during pulse plating. Met. Mater. Int. 16, 755–760 (2010). https://doi.org/10.1007/s12540-010-1009-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12540-010-1009-4