Abstract
To improve the mechanical properties and the adhesion to a natural rubber (NR)/styrene-butadiene rubber (SBR) matrix, continuous basalt fibre (CBF) cords with and without a silane coupling agent (3-aminopropyl)triethoxysilane (KH550) treatment were dipped into a typical resorcinol-formaldehyde-latex (RFL) system. The breaking force and elongation at break of the cords were tested using a universal testing machine. The adhesive properties were evaluated by both static mode and dynamic (fatigue) mode with H-shape cord-rubber samples. An elastomer testing system was employed to conduct the fatigue test, and the evolution of the adhesive properties between the CBF cord and the NR/SBR matrix was tracked. The interfacial fracture caused by H pull out and fatigue were both observed with a scanning electron microscope (SEM). The results of this investigation show that the RFL-dipping treatment can significantly improve the mechanical properties of the CBF cord and its adhesion to the NR/SBR matrix, and the pre-treatment of the CBF cord with KH550 can further improve the interfacial fatigue property.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
V. Fiore, T. Scalici, G. Di Bella, and A. Valenza, Compos. Pt. B-Eng., 74, 74 (2015).
V. Lopresto, C. Leone, and I. De Iorio, Compos. Pt. BEng., 42, 717 (2011).
A. Greco, A. Maffezzoli, G. Casciaro, and F. Caretto, Compos. Pt. B-Eng., 67, 233 (2014).
M. Jamshidi and F. A. Taromi, J. Adhes. Sci. Technol., 20, 1693 (2006).
V. Manikandan, J. T. W. Jappes, S. M. S. Kumar, and P. Amuthakkannan, Compos. Pt. B-Eng., 43, 812 (2012).
J. M. Espana, M. D. Samper, E. Fages, L. Sanchez-Nacher, and R. Balart, Polym. Compos., 34, 376 (2013).
B. Wei, H. L. Cao, and S. H. Song, Compos. Pt. A-Appl. Sci. Manuf., 42, 22 (2011).
G. J. Wang, Y. W. Liu, Y. J. Guo, Z. X. Zhang, M. X. Xu, and Z. X. Yang, Surf. Coat. Technol., 201, 6565 (2007).
T. S. Solomon, Rubber Chem. Technol., 58, 561 (1985).
G. R. Hamed and C. Ruksakulpiwat, J. Appl. Polym. Sci., 91, 1993 (2004).
G. Gillberg, L. C. Sawyer, and A. L. Promislow, J. Appl. Polym. Sci., 28, 3723 (1983).
M. Shirazi, M. B. de Rooij, A. G. Talma, and J. W. M. Noordermeer, J. Adhes. Sci. Technol., 27, 1886 (2013).
W. B. Wennekes, R. N. Datta, and J. W. M. Noordermeer, Rubber Chem. Technol., 81, 523 (2008).
M. Shirazi, A. G. Talma, and J. W. M. Noordermeer, J. Adhes. Sci. Technol., 27, 1048 (2013).
A. I. Abou-Kandil, A. Awad, N. Darwish, A. B. Shehata, and B. K. Saleh, Int. J. Adhes. Adhes., 44, 26 (2013).
M. P. Wagner and N. L. Hewitt, J. Elastomers Plast., 10, 95 (1978).
Y. M. Chen and Y. Zhang, Tire Industry, 34, 188 (2014).
M. Jamshidi, F. Afshar, and B. Shamayeli, J. Appl. Polym. Sci., 101, 2488 (2006).
X. Y. Shi, M. Q. Ma, C. B. Lian, and D. W. Zhu, Polym. Test., 32, 1145 (2013).
A. K. Naskar, A. K. Mukherjee, and R. Mukhopadhyay, Polym. Degrad. Stabil., 83, 173 (2004).
J. M. Park and R. V. Subramanian, J. Adhes. Sci. Technol., 5, 459 (1991).
J. M. Park and R. V. Subramanian, J. Adhes. Sci. Technol., 8, 1473 (1994).
T. Deak, T. Czigany, P. Tamas, and C. Nemeth, Express Polym. Lett., 4, 590 (2010).
Y. L. Liu, S. J. Shen, L. Zhang, and L. M. Shao, Adv. Mater. Res., 236-238, 1467 (2011).
J. Militky, V. Kovacic, and J. Rubnerova, Eng. Fract. Mech., 69, 1025 (2002).
X. Y. Shi, C. B. Lian, Y. Y. Shang, and H. Y. Zhang, Polym. Test., 48, 175 (2015).
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Li, Z., Xiao, T. & Zhao, S. Effects of surface treatments on Mechanical properties of Continuous basalt fibre cords and their Adhesion with rubber matrix. Fibers Polym 17, 910–916 (2016). https://doi.org/10.1007/s12221-016-5928-7
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12221-016-5928-7