Abstract
PVDF-CF composite films were prepared using a melt pressing method. The PVDF-CF composite films were cut into rectangular shapes with a gauge length and width of 10 and 5 mm, respectively. The films were drawn using a universal testing machine equipped with a hot chamber. The drawing temperatures and speeds were 50∼150 °C and 100∼000 %/min, respectively. The crystal structure and physical properties of the resulting PVDF-CF films were investigated by wide angle X-ray diffraction, Fourier transform infrared spectroscopy, differential scanning calorimetry, dynamic mechanical analysis and scanning electron microscopy. The crystal form of the initial films was the 〈alpha〉 phase (non polarity, lamellar structure) of PVDF. The maximum draw ratio was 4.2. The drawn PVDF-CF films prepared at 100 °C were mainly the 〈beta〉 phase (polarity, fibrillar structure) of PVDF. With increasing drawing speeds, the 〈alpha〉 phase became the dominant phase of PVDF in the PVDF-CF films. The thermal properties of the PVDF-CF films improved with increasing drawing temperature, and the dynamic mechanical properties improved with increasing drawing speed.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
J. E. Mark, “Physical Properties of Polymers Handbook”, p.509, American Institute of Physics, Woodbury, New York, 1996.
R. Hasegawa, Y. Takahashi, Y. Chatani, and H. Tadokoro, Polym. J., 3, 600 (1972).
S. Weinhold, M. H. Fitt, and J. B. Lando, Macromolecules, 13, 1178 (1980).
A. J. Lovinger, Macromolecules, 14, 322 (1981).
Y. Takahashi, Y. Matsubara, and H. Tadokoro, Macromolecules, 16, 1588 (1983).
B. Mohannadi, A. A. Yousefi, and S. M. Bellah, Polym. Test, 26, 42 (2007).
G. Wu, C. Zhang, T. Miura, S. Asai, and M. Sumita, J. Appl. Polym. Sci., 80, 1063 (2001).
A. Seema, K. R. Dayas, and J. M. Varghese, J. Appl. Polym. Sci., 106, 146 (2007).
S. Vidhate, A. Shaito, J. Chung, and N. A. D’souza, J. Appl. Polym. Sci., 112, 254 (2009).
T. Danno, H. Matsumoto, M. Nasir, M. Minagawa, H. Horibe, and A. Tanioka, J. Appl. Polym. Sci., 112, 1868 (2009).
P. Costa, J. Silvia, V. Sencadas, C. M. Costa, F. W. J. Van Hattum, J. G. Rocha, and S. Lanceros-Mendez, Carbon, 47, 2590 (2009).
L. Y. Yu, H. M. Shen, and Z. L. Xu, J. Appl. Polym. Sci., 113, 1763 (2009).
S. Ansari and E. P. Giannelis, J. Polym. Sci., Polym. Phys., 47, 903 (2009).
T. Wu, T. Xie, and C. Yang, J. Polym. Sci., Polym. Phys., 47, 888 (2009).
L. He, Q. Xu, C. Hua, and R. Song, Polym. Composite, DOI 10.1002/pc.20876 (2009).
Y. W. Nam, W. N. Kim, Y. H. Cho, D. W. Chae, G. H. Kim, S. P. Hong, S. S. Hwang, and S. M. Hong, Macromol. Symp., 249, 478 (2007).
J. H. Koo, “Polymer Nanocomposites -Processing, Characterization, and Applications-”, p.198, McGraw-Hill, New York, 2006.
P. Morgan, “Carbon Fiber and Their Composite”, p.75, CRC Press, Cambridgeshire, UK, 2005.
C. S. Park, B. S. Kang, and D. W. Lee, Transactions of the KSME A, 31, 417 (2007).
N. Mekhilef, J. Appl. Polym. Sci., 80, 230 (2001).
A. J. Lovinger, “In Development in Crystalline Polymers”, Applied Science Publishers, London, 1982.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lee, S.H., Cho, H.H. Crystal structure and thermal properties of poly(vinylidene fluoride)-carbon fiber composite films with various drawing temperatures and speeds. Fibers Polym 11, 1146–1151 (2010). https://doi.org/10.1007/s12221-010-1146-x
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12221-010-1146-x