Abstract
In this work, friction stir spot welding with 1.6 mm thickness of the 2024-T3 aluminum alloy is carried out. The effects of the tool rotational speed and shoulder penetration depth on surface appearance, macrostructure, temperature profile, maximum failure load and failure modes are investigated. Results show that, the effect of the tool rotational speed on maximum tensile shear load is similar to the effect of the shoulder penetration depth, increasing tool rotational speed and shoulder penetration depth resulted in the increase of the tensile shear load. Maximum load of about 8282 N is obtained by using 1000 rpm rotational speed and 0.7 mm shoulder penetration depth. Observation of the failed specimens indicates two types of failure modes under tensile shear loading, the shear fracture that occurs in low shoulder penetration depths and tensile shear fracture that occurs in high shoulder penetration depths.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
R. Hancock, Friction welding of aluminum cuts energy cost by 99%, Welding Journal, 83 (2004) 40.
P. C. Lin, J. Pan and T. Pan, Failure modes and fatigue life estimations of spot friction welds in lap-shear specimens of aluminium 6111-T4 sheets. Part 2: Welds made by a flat tool, Int. J. Fatigue, 30 (2008) 90–105.
C. Herbelot, T. D. Hoang, A. Imad and N. Benseddiq, Damage mechanisms under tension shear loading in friction stir spot welding, Sci. Technol. Weld. Join., 15 (2010) 688–693.
V. X. Tran, J. Pan and T. Pan, Effects of processing time on strengths and failure modes of dissimilar spot friction welds between aluminum 5754-O and 7075- T6 sheets, J. Mater. Process. Techno., 209 (2009) 3724–3739.
S. Hirasawaa, H. Badarinarayan, K. Okamoto, T. Tomimura and T. Kawanami, Analysis of effect of tool geometry on plastic flow during friction stir spot welding using particle method, J. Mater. Process. Technol., 210 (2010) 1455–1463.
S. Lathabai, M. J. Painter, G. M. D. Cantin and V. K. Tyagi, Friction spot joining of an extruded Al-Mg-Si alloy, Scripta. Mater., 55 (2006) 899–902.
Y. Tozaki, Y. Uematsu and K. Tokaji, Effect of tool geometry on microstructure and static strength in friction stir spot welded aluminium alloys, Int. J. Mach. Tools. Manuf., 47 (2007) 2230–2236.
T. Pan, A. Joaquin, D. E. Wilkosz, L. Reatherford, J. M. Nicholson and Z. Fengm, Spot friction welding for sheet aluminum joining, In: Proceedings of the 5th international symposium of friction stir welding, Metz, France (2004).
M. Fujimoto, M. Inuzuka, M. Nishio and Y. Nakashima, Development of friction spot joining (Report 1)-cross sectional structures of friction spot joints, The National Meeting of Japan Welding Society, Japan (2004) 4–5.
M. Fujimoto, M. Inuzuka, M. Nishio and Y. Nakashima, Development of friction spot joining (Report 1)- mechanical properties of friction spot joints, The National Meeting of Japan Welding Society, Japan (2004) 6–7.
S. O. Yoon, M. S. Kang, Y. J. Kwon, S. T. Hong, D. H. Park, K. H. Lee, K. H. Lim and J. D. Seo, Influences of tool penetration speed and tool penetration depth on friction spot joining of AA5454-O aluminum alloy plates with different thicknesses. Trans. Nonferrous. Met. Soc. China, 22 (2012) 629–633.
N. Pathak, K. Bandyopadhyay, M. Sarangi and S. K. Panda, Microstructure and mechanical performance of friction stir spot- welded aluminum-5754 sheets, J. Mater. Eng. Perform., 22 (2012) 131–144.
D. Mitlin, V. Radmilovic, T. Pan, J. Chen, Z. Feng and M. L. Santalla, Structure properties relations in spot friction welded 6111 aluminium, Mater. Sci. Eng. A, 441 (2006) 79–96.
Z. Zhang, X. Yang, J. Zhang, G. Zhou, X. Xu and R. Zou, Effect of welding parameters on microstructure and mechanical properties of friction stir spot welded 5052 aluminum alloy, Mater. Des., 32 (2011) 4462–4470.
A. Gerlich, T. H. North and M. Yamamoto, Local melting and cracking in Al 7075-T6 and Al 2024-T3 friction stir spot welds, Sci. Technol. Weld. Join., 12 (2007) 472–480.
H. Badarinarayan, Y. Shi, X. Li and K. Okamoto, Effect of tool geometry on hook formation and staticstrength of friction stir spot welded aluminum 5754-O sheets, Int. J. Mach. Tools. Manuf., 49 (2009) 814–823.
D. A. Wang, C. W. Chao, P. C. Lin and J. Y. Uan, Mechanical characterization of friction stir spot microwelds, J. Mater. Process. Techno., 14 (2010) 1942–1948.
M. K. Bilici and A. I. Yukler, Effects of welding parameters on friction stir spot welding of high density polyethylene sheets, Mater. Des., 33 (2012) 545–550.
A. Gerlich, P. Su, M. Yamamoto and T. H. North, Effect of welding parameters on the strain rate and microstructure of friction stir spot welded 2024 aluminium alloy, J. Mat. Sci., 42 (2007) 5589–5601.
Author information
Authors and Affiliations
Corresponding author
Additional information
Recommended by Associate Editor Chongdu Cho
Moslem Paidar received his B.S. in Materials Engineering from Shahrekord University, Iran, in 2010. Then, He received his M.S. degrees from Graduate School of Matrials Engineering, Tehran Science and Research Branch, Islamic Azad University, Tehran, Iran in 2013. Mr. Paidar is currently Ph.D student in South Tehran Branch, Islamic Azad University in Tehran, Iran. Mr. Paidar’s research interests include Laser Beam Welding, Difusion Welding, Welding-Brazing, Surface engineering, Brazing And Activated TIG for disimilar materilas and Light metals.
Alireza Khodabandeh is an assistant professor of Materials Engineering Department at Science and Research Branch of Islamic Azad University in Tehran, Iran, where he has been a faculty member since 2008. He received his B.S. degree in Materials Engineering from Shiraz University, Iran, at 1994. He also received his M.Sc. in Materials Engineering from Tarbiat Modares University, Iran, at 1997 and then he completed his Ph.D. at 2005, from Tarbiat Modares University. His research interests lie in the area of Physical Properties of Materials with a focus on Solid State Transformation, Diffusion in Solids and Microstructure.
Hamidreza Najafi received his B.S. degree in Materials Engineering from University of Tehran, Iran, in 1999. Then, He received his M.S. degree from Sharif University of Technology, Iran, 2001. He graduated in 2007 with a Ph.D. in Materials Engineering from University of Tehran, Iran. Dr. Najafi is currently an Assistant Professor at Department of Materials Engineering at Tehran Science and Research Branch, Islamic Azad University, Tehran, Iran. His research interests include phase transformations and materials characterization.
Alireza Sabour rouh-Aghdam an associate professor of Materials Engineering Department at Tarbiat Modares University in Iran, Tehran. He received his M.S. degree from Germany, 1988. He graduated in 1993 with a Ph.D. in Materials Engineering from in German. Dr. Sabour rouh-Aghdam is faculty member of Department at Tarbiat Modares University since 1995. His research interests include Surface engineering and materials characterization.
Rights and permissions
About this article
Cite this article
Paidar, M., Khodabandeh, A., Najafi, H. et al. Effects of the tool rotational speed and shoulder penetration depth on mechanical properties and failure modes of friction stir spot welds of aluminum 2024-T3 sheets. J Mech Sci Technol 28, 4893–4898 (2014). https://doi.org/10.1007/s12206-014-1108-0
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12206-014-1108-0