Abstract
Ni nanoparticles were mass synthesized by solution reduction process successfully. The influence of the parameters on the particle size of Ni nanoparticles were studied and the referential process parameters were obtained. The morphology and structure of the synthesized Ni nanoparticles were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) surface area analysis and infrared spectroscopy (IR). The results show that Ni nanoparticles are of high purity and are covered by hydroxyethyl carboxymethyl cellulose (HECMC) layer and the mean size being about 31 nm. The magnetic measurement revealed that Ni nanoparticles are ferromagnetic.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Degen A and Matek J 1999 NanoStruct. Mater. 12 225
Hinotsu T, Jeyadevan B, Chinnasamy C N, Shinoda K and Tohji K 2004 J. Appl. Phys. 95 7477
Hou Y L and Gao S 2004 J. Alloy. Compd. 365 112
Gray D E 1972 America institute of physics handbook (New York: McGraw-Hill Book Company)
Guo P S, Sun Z, Chen Y W and Zheng Z H 2006 Mater. Lett. 60 966
Kumar D, Yarmolenko S, Sankar J, Narayan J, Zhou H and Tiwari A 2004 Compos. Part B-Eng. 35 149
La Mer V K and Dinegar R H 1950 J. Am. Chem. Soc. 72 4847
Liu Q, Liu H J, Liang Y Y, Xu Zh and Yin G 2006 Mater. Res. Bull. 41 697
Liu X S, Meridor U, Zhao P, Song G B, Frydmanc A and Gedanken A 2006 J. Magn. Magn. Mater. 301 13
Luo Zh S, Chen Ch L, Zhao D J, Luo Sh L and Li Zh Ch 2006 Chem. Phys. Lett. 421 584
Ni X M, Su X B, Yang Z B and Zheng H G 2003 J. Cryst. Growth 252 612
Pfeil and Leonard B 1987 US Patent 4,673,430
Sun C Q 2003 Prog. Mater. Sci. 48 521
Swanson H E and Tatge E 1953 Nat. Bur. Stand. (US) Circ. 539 1 13
Syukri T Ban, Ohya Y and Takahashi Y 2003 Mater. Chem. Phys. 78 645
Törnqvist E, Adams E D, Copel M, Gustafsson T and Graham W R 1984 J. Vac. Sci. Technol. A2 939
Wei Zh Q, Xia T D, Bai L F, Wang J, Wu Zh G and Yan P X 2006 Mater. Lett. 60 766
Yu X F, Liu X, Zhang K and Hu Z Q 1999 J. Phys. Condens. Matter. 11 937
Zheng H G, Liang J H, Zeng J H and Qian Y T 2001 Mater. Res. Bull. 36 947
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wang, H., Kou, X., Zhang, J. et al. Large scale synthesis and characterization of Ni nanoparticles by solution reduction method. Bull Mater Sci 31, 97–100 (2008). https://doi.org/10.1007/s12034-008-0017-1
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-008-0017-1