Abstract
The electromigration (EM) performance of Pb-free solder joints is investigated in terms of solder composition (Sn-0.5Cu vs. Sn-1.8Ag) and joining path to Cu vs. Ni(P) under bump metallization (UBM). In the double-sided joints of Ni(P)/solder/Cu, the micro-structure of solder joints and the interfacial intermetallic compound (IMC) layers are significantly affected by solder composition and joining path. The as-reflowed microstructure of Sn-0.5Cu joints consists of small columnar grains with thin IMC layers at both UBM interfaces, independent of the joining path, while Sn-1.8Ag joints have a few large grains of low-angle grain boundaries with thick IMC layers when joined first to Ni(P) UBM, but a few 60° twins with thin IMC layers when joined first to Cu UBM. The EM stressing under high current densities at 150°C reveals that Sn-1.8Ag joints have a superior lifetime compared to Sn-0.5Cu joints. In addition, the EM lifetime of Sn-1.8Ag joints reflowed first on Ni(P) UBM is the longest among four groups of the solder joints examined.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
K.N. Tu et al., AIP Conference Proceedings, 817 (2006), pp. 327–338.
L. Nicholls et al., Proc. 59th Electronic Components and Technology Conf. (Plscataway NJ: IEEE, 2009), pp. 914–921.
R Su and L Li, Proc. 59th Electronic Components and Technology Conf. (Plscataway NJ: IEEE, 2009), pp. 903–908.
S.W. Liang et al., J. Electron. Mater., 38 (2009), p. 2443.
W.K. Choi, S.W. Yoon, and H.M. Lee, Mater. Trans., 42 (2001), p. 783.
S.-K. Seo et al., J. Electron. Mater., 35 (2006), p. 1975.
D.H. Kim et al., J. Electron. Mater., 38 (2009), p. 39.
M.G. Cho et al., J. Electron. Mater., 36 (2007), p. 1501.
B.F. Dyson, J.Appl. Phys., 37 (1966), p. 2375.
B.F. Dyson, T.R. Anthony, and D. Turnbull, J. Appi. Phys., 37 (1967), p. 3408.
DC. Yeh and H.B. Huntington, Phy. Rev. Lett., 53(15) (1984), p. 1469.
RH. Huang and H.B. Huntington, Phys. Rev. B, 9(4) (1974), p. 1479.
M. Lu et al., Appi. Phys. Lett., 92 (2008), 211909.
S.-K. Seo et al., J. Electron. Mater., 38 (2009), p. 2461.
S.-K. Seo et al., J. Electron. Mater., 38 (2009), p. 257.
G.F. Bolling, J.J. Kramer, and W.A. Tiller, Trans. Met. Soc. AIME, 227 (1963), p. 1453.
S.-K. Seo, M.G. Cho, and H.M. Lee, J. Mater. Res. (under review).
C.E. Ho, S.C. Vang, and C.R. Kao, J. Mater. Sci: Mater. Electron., 18, (2007), p. 155.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Seo, SK., Kang, S.K., Cho, M.G. et al. Electromigration performance of Pb-free solder joints in terms of solder composition and joining path. JOM 62, 22–29 (2010). https://doi.org/10.1007/s11837-010-0104-9
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11837-010-0104-9