Abstract
Here, we study the effect of bonding time on the intermetallic compound (IMC) formation and shear property of Cu/In-50Ag/Cu TLP solder joints based on low-temperature transition liquid phase (TLP) bonding of In-Ag composite powder. The bonding process was carried out at a temperature of 260°C using a wafer bonding machine. The results show that the solder joints are composed of an (Ag,Cu)2In phase and a Cu2In phase in the interfacial diffusion reaction zone and an Ag2In phase and In rich phase in the in␣situ reaction zone. It was observed that the (Ag,Cu)2In phase is formed firstly in the diffusion reaction zone when the bonding time is 0.5 min, then transforms completely into the Cu2In phase when the bonding time reaches 30 min. The shear strength increased and then decreased with increasing bonding time. The observed shear fracture mode of solder joints is brittle.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
D.H. Jung, A. Sharm, and J.P. Jung, J. Mater. Sci. 53, 47 (2017).
S. Terashima, Y. Kariya, T. Hosoi, and M. Tanaka, J. Electron. Mater. 32, 1527 (2003).
S. Liu, S.B. Xue, P. Xue, and D.X. Luo, J. Mater. Sci. 26, 4389 (2015).
F.J. Wang, L.L. Zhou, X.J. Wang, and P. He, J. Alloys Compd. 688, 15 (2016).
G.O. Cook and C.D. Sorensen, J. Mater. Sci. 46, 5305 (2011).
J. Gu, Y.P. Lei, J. Lin, H.G. Fu, and Z.W. Wu, J. Electron. Mater. 46, 1396 (2017).
N.S. Bosco and F.W. Zok, Acta Mater. 52, 10 (2004).
C. Buttay, D. Planson, B. Allard, D. Bergogne, P. Bevilacqua, C. Joubert, M. Lazar, C. Martin, H. Morel, D. Tournier, and C. Raynaud, Mater. Sci. Eng., B 176, 4 (2011).
H.K. Shao, A.P. Wu, Y.D. Bao, and Y. Zhao, J. Mater. Sci. 52, 3508 (2016).
Y.Q. Deng, G.M. Sheng, F.L. Wang, X.J. Yuan, and Q. An, Mater. Des. 92, 1 (2016).
R.S. Xie, X.G. Chen, Z.W. Lai, L. Liu, G.S. Zou, J.C. Yan, and W.X. Wang, Mater. Des. 91, 19 (2016).
W.B. Zhu, Y.Y. Zhu, X. Ma, and M.Y. Li. Proceeding of the 22nd Annual Meeting of Soldering, Brazing and Special Joining Technologies, vol. 1 (2018), p. 276.
X. Deng, G. Piotrowski, J.J. Williams, and N. Chawla, J. Electron. Mater. 32, 12 (2003).
H.K. Shao, A.P. Wu, Y.D. Bao, Y. Zhao, G.S. Zou, and L. Liu, Mater. Charact. 144, 469 (2018).
C.F. Yu, H.C. Chen, and W.H. Chen, Rsc. Adv. 5, 70609 (2015).
Y.M. Liu and T.H. Chuang, J. Electron. Mater. 29, 11 (2000).
B. Gollas, Intermetallics 16, 8 (2008).
Y.Z. Ma, H.T. Luo, Y.J. Li, W.S. Liu, Y.K. Wang, and B.Y. Huang, J. Mater. Sci.: Mater. Electron. 26, 7967 (2015).
A.A. Wronkowska, A. Wronkowski, A. Bukaluk, M. Trzcinski, K. Okulewicz, and Ł. Skowroński, Appl. Surf. Sci. 254, 4401 (2008).
J.C. Lin, L.W. Huang, G.Y. Jang, and S.L. Lee, Thin Solid Films 410, 212 (2002).
I. Dutta, P. Kumar, and G. Subbarayan, JOM 61, 29 (2009).
X.J. Wang, Q.S. Zhu, Z.G. Wang, and J.K. Shang, Acta Metall. Sin. 45, 8 (2009).
Acknowledgments
This research was financially supported by the National Natural Science Foundation of China (Foundation No. 51865006) and Natural Science Foundation of the Jiangsu Higher Education Institutions of China (Grant Nos. 19KJA430001 and 18KJA460001).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Yang, L., Qiao, J., Zhang, Y.C. et al. Effect of Bonding Time on Microstructure and Shear Property of Cu/In-50Ag/Cu TLP Solder Joints. J. Electron. Mater. 49, 4300–4306 (2020). https://doi.org/10.1007/s11664-020-08149-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-020-08149-z