Abstract
SrFe12O19/Ni0.6Zn0.4Fe2O4 powders were prepared by the one-pot solution combustion method. The effect of calcination temperatures (700°C and 800°C) on phase, structure, microstructure and magnetic properties of SrFe12O19-x Ni0.6Zn0.4Fe2O4 (x = 0 wt.%, 10 wt.%, 20 wt.% and 30 wt.%) composites were investigated by x-ray diffractometry, scanning electron microscopy and vibrating sample magnetometry techniques. Strontium hexaferrite and spinel ferrite phases were formed through calcination at 800°C together with some α-Fe2O3 phase, while spinel ferrite was mainly crystallized at 700°C. The saturation magnetization slightly increased from 38 emu/g to 42 emu/g with the addition of 10 wt.% of Ni0.6Zn0.4Fe2O4 and then decreased to 36 emu/g at a calcination temperature of 800°C. The microwave absorption measurements in X-band (8–12 GHz) showed a minimum reflection loss of − 14.5 dB at 9.5 GHz for SrFe12O19-10 wt.% Ni0.6Zn0.4Fe2O4 composite synthesized at 800°C.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
A. Goldman, Modem Ferrite Technology, 2nd ed. (Pittsburgh: Springer, 2006).
K.J. Vinoy and R.M. Jha, Radar Absorbing Materials, 1st ed. (New York: Springer, 1996).
R. Valenzuela, Magnetic Ceramics (Cambridge: Cambridge University Press, 1994).
R.C. Pullar, Prog. Mater. Sci. 57, 1191 (2012).
G.C.P. Leite, E.F. Chagas, R. Pereira, R.J. Prado, A.J. Terezo, M. Alzamora, and E. Baggio-Saitovitch, J. Magn. Magn. Mater. 324, 2711 (2012).
X. Shen, F. Song, J. Xiang, M. Liu, Y. Zhu, and Y. Wang, J. Am. Ceram. Soc. 95, 3863 (2012).
M.A. Radmanesh and S.A. Seyyed Ebrahimi, J. Magn. Magn. Mater. 324, 3094 (2012).
S.M.A. Radmanesh and S.A. Seyyed Ebrahimi, J. Supercond. Novel Magn. 26, 2411 (2013).
D. Roy and P.S. Anil Kumar, J. Appl. Phys. 106, 073902 (2009).
V. Sharma, S. Kumari, and B.K. Kuanr, J. Alloys Compd. 736, 266 (2018).
S.R. Saeedi Afshar, M. Hasheminiasari, and S.M. Masoudpanah, J. Magn. Magn. Mater. 466, 1 (2018).
P. Jenuš, M. Topole, P. McGuiness, C. Granados-Miralles, M. Stingaciu, and M. Christensen, Spomenka Kobe Kristina ŽuŽek RoŽman 99, 1927 (2016).
H. Nikmanesh, M. Moradi, P. Kameli, and G.H. Bordbar, J. Electron. Mater. 46, 5933 (2017).
L. Pan, D. Cao, P. Jing, J. Wang, and Q. Liu, J. Nanoscale Res. Lett. 10, 131 (2015).
C. Granados-Miralles, M. Saura-Múzquiz, H.L. Andersen, A. Quesada, J.V. Ahlburg, A. Dippel, E. Canévet, and M. Christensen, ACS Appl. Nano Mater. 1, 3693 (2018).
P. Veverka, E. Pollert, K. Závěta, S. Vasseur, and E. Duguet, Nanotechnology 19, 215705 (2008).
A. Varma, A.S. Mukasyan, A.S. Rogachev, and K.V. Manukyan, Chem. Rev. 116, 14493 (2016).
H.H. Nersisyan, J.H. Lee, J.-R. Ding, K.-S. Kim, K.V. Manukyan, and A.S. Mukasyan, Prog. Energy Combust. Sci. 63, 79 (2017).
F. Li, J. Ran, M. Jaroniec, and S.Z. Qiao, Nanoscale 7, 17590 (2015).
S.M. Masoudpanah and S.A. Seyyed Ebrahimi, J. Magn. Magn. Mater. 324, 2239 (2012).
Q. Han, X. Meng, and C. Lu, J. Alloys Compd. 768, 742 (2018).
S. Hazra, B.K. Ghosh, H.R. Joshi, M.K. Patra, R.K. Jani, S.R. Vadera, and N.N. Ghosh, RSC Adv. 4, 45715 (2014).
X. Meng, Q. Han, Y. Sun, and Y. Liu, Ceram. Int. 45, 2504 (2019).
Y. Wang, Y. Huang, Q. Wang, Q. He, and M. Zong, J. Sol. Gel. Sci. Technol. 67, 344 (2013).
Z. Han, D. Li, M. Tong, X. Wei, R. Skomski, W. Liu, Z.D. Zhang, and D.J. Sellmyer, J. Appl. Phys. 107, 09A929 (2010).
E. Kiani, A.S.H. Rozatian, and M.H. Yousefi, J. Mater. Sci. Mater. Electron. 24, 2485 (2013).
S. Kanagesan, M. Hashim, S. Jesurani, T. Kalaivani, I. Ismail, and C.S. Ahmod, J. Mater. Sci. Mater. Electron. 24, 3881 (2013).
S.M. Masoudpanah, S.A. Seyyed Ebrahimi, and C.K. Ong, J. Magn. Magn. Mater. 324, 2654 (2012).
A. Rahman and R. Jayaganthan, Surf. Eng. 33, 810 (2017).
N.A. Spaldin, Magnetic Materials: Fundamentals and Applications (Cambridge: Cambridge University Press, 2010).
F. Liu, Y. Hou, and S. Gao, Chem. Soc. Rev. 43, 8098 (2014).
Y. Deng, G.P. Zhao, L. Chen, H.W. Zhang, and X.L. Zhou, J. Magn. Magn. Mater. 323, 535 (2011).
S. Torkian, A. Ghasemi, and R.S. Razavi, J. Magn. Magn. Mater. 416, 408 (2016).
D. Roy, C. Shivakumara, and P.S. Anil Kumar, J. Magn. Magn. Mater. 321, L11 (2009).
Z.W. Li, L. Chen, and C.K. Ong, J. Appl. Phys. 94, 5918 (2003).
M. Jazirehpour and S.A. Seyyed Ebrahimi, J. Alloys Compd. 638, 188 (2015).
X. Zhao, Z. Zhang, L. Wang, K. Xi, Q. Cao, D. Wang, Y. Yang, and Y. Du, Sci. Rep. 3, 3421 (2013).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflicts of interest
There is no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Saeedi Afshar, S.R., Masoudpanah, S.M. & Hasheminiasari, M. Effects of Calcination Temperature on Magnetic and Microwave Absorption Properties of SrFe12O19/Ni0.6Zn0.4Fe2O4 Composites. J. Electron. Mater. 49, 1742–1748 (2020). https://doi.org/10.1007/s11664-020-07943-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-020-07943-z