Abstract
Y2O3 addition has a significant influence on the crystallization, thermal, mechanical, and electrical properties of BaO-Al2O3 -B2O3 -SiO2 (BABS) glass–ceramics. Semi-quantitative calculation based on x-ray diffraction demonstrated that with increasing Y2O3 content, both the crystallinity and the phase content of cristobalite gradually decreased. It is effective for the additive Y2O3 to inhibit the formation of cristobalite phase with a large coefficient of thermal expansion value. The flexural strength and the Young’s modulus, thus, are remarkably increased from 140 MPa to 200 MPa and 56.5 GPa to 63.7 GPa, respectively. Also, the sintering kinetics of BABS glass–ceramics with various Y2O3 were investigated using the isothermal sintering shrinkage curve at different sintering temperatures. The sintering activation energy Q sharply decreased from 99.8 kJ/mol to 81.5 kJ/mol when 0.2% Y2O3 was added, which indicated that a small amount of Y2O3 could effectively promote the sintering procedure of BABS glass–ceramics.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
O. Dernovsek, A. Naeini, G. Preu, W. Wersing, M. Eberstein, and W.A. Schiller, J. Eur. Ceram. Soc. 21, 1693 (2001).
M.T. Sebastian and H. Jantunen, Int. Mater. Rev. 53, 57 (2008).
D. Nowak and A. Dziedzic, Microelectron. Reliab. 51, 1241 (2011).
K.S. Chin, C.C. Chang, C.H. Chen, Z. Guo, D. Wang, and W. Che, IEEE Trans. Compon. Packag. 4, 664 (2014).
B. Li, S. Wang, and Y. Fang, J. Alloy. Compd. 693, 9 (2017).
K. Wang, H. Yan, Z. Liang, and X. Cui, Mater. Res. Bull. 65, 249 (2015).
B. Li, B. Tang, and M. Xu, J. Electron. Mater. 27, 1 (2015).
E.S. Lim, B.S. Kim, J.H. Lee, and J.J. Kim, J. Eur. Ceram. Soc. 27, 825 (2007).
E.S. Lim, B.S. Kim, J.H. Lee, and J.J. Kim, J. Electroceram. 17, 359 (2006).
S. Chen and D. Zhu, J. Alloy. Compd. 536, 73 (2012).
A.I. Borhan, M. Gromada, G.G. Nedelcu, and L. Leontie, Ceram. Int. 42, 10459 (2016).
K. Singh, N. Gupta, and O.P. Pandey, J. Mater. Sci. 42, 6426 (2007).
V. Kumar, S. Sharma, O.P. Pandey, and K. Singh, Solid State Ion. 181, 79 (2010).
V. Kumar, O.P. Pandey, and K. Singh, Ceram. Int. 36, 1621 (2010).
O. Şan and C. Özgür, J. Eur. Ceram. Soc. 29, 2945 (2009).
A.A. Appen, Silikattechnik 5, 11 (1954).
P.W. McMillan, Glass-Ceramics, 2nd ed. (London: Academic, 1979).
J. Hormadaly, J. Non Cryst. Solids 79, 311 (1986).
Z. Huang, M. Gotoh, and Y. Hirose, J. Mater. Process. Technol. 209, 2446 (2009).
V.K. Singh, J. Am. Ceram. Soc. 64, C-133 (2006).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Li, B., Li, W. & Zheng, J. Influence of Y2O3 Addition on Crystallization, Thermal, Mechanical, and Electrical Properties of BaO-Al2O3-B2O3-SiO2 Glass–Ceramic for Ceramic Ball Grid Array Package. J. Electron. Mater. 47, 766–772 (2018). https://doi.org/10.1007/s11664-017-5808-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-017-5808-y