This is a preliminary investigation on the mechanical properties of Pb-free Sn-1.0Ag-0.5Cu solder joints containing 0.02 wt.% to 0.1 wt.% Y under a range of thermal aging and reflow conditions. Despite the significantly thicker intermetallic compound (IMC) formed at the solder joint, the 0.1 wt.% Y-doped joint exhibited a higher fracture strength than its baseline Sn-1.0Ag-0.5Cu counterpart under most aging and reflow conditions. This may be associated with the formation of Y-Cu IMCs formed at the interface between the solder and the Cu substrate, because the Y-Cu IMCs have recently been referred to as relatively ‘ductile’ IMCs.
Article PDF
Avoid common mistakes on your manuscript.
References
L. Zhang, S. Xue, Y. Chen, Z. Han, J. Wang, S. Yu, and F. Lu, J. Rare Earth 27, 138 (2009).
W.M. Xiao, Y.W. Shi, G.C. Xu, R. Ren, F. Guo, Z.D. Xia, and Y.P. Lei, J. Alloys Compd. 472, 198 (2009).
T.H. You, Y.S. Kim, W.G. Jung, J.T. Moon, and H.M. Choe, J. Alloys Compd. 486, 242 (2009).
T.H. You, Y.S. Kim, J.N. Kim, J.H. Lee, B.W. Jung, J.T. Moon, and H.M. Choe, J. Electron. Mater. 38, 410 (2009).
L. Wang, D.Q. Yu, J. Zhao, and M.L. Huang, Mater. Lett. 56, 1039 (2002).
C.M.L. Wu, D.Q. Yu, C.M.T. Law, and L. Wang, Mat. Sci. Eng. R 44, 1 (2004).
Z. Chen, Y. Shi, Z. Xia, and Y. Yan, J. Electron. Mater. 32, 235 (2003).
J.T. Guo, K.W. Huai, Q. Gao, W.L. Ren, and G.S. Li, Intermetallics 15, 727 (2007).
A.C.K. So and Y.C. Chan, IEEE Trans. Compon. Packag. Manuf. Technol. B 19, 661 (1996).
H.-T. Lee, M.-H. Chen, H.-M. Jao, and T.-L. Liao, Mat. Sci. Eng. A 358, 134 (2003).
T.-C. Chiu, K. Zeng, R. Stierman, D. Edwards, and K. Ano, 2004 Electronic Components and Technology Conf. (Las Vegas: IEEE, 2004), pp. 1256–1262.
D.-G. Kim, J.-W. Kim, and S.-B. Jung, Mater. Sci. Eng. B 121, 204 (2005).
C.-M. Chuang, P.-C. Shin, and K.-L. Lin, J. Electron. Mater. 33, 1 (2004).
J.Y. Sung, S.E. Pyo, J.M. Koo, J.W. Yoon, Y.E. Shin, and S.B. Jung, J. Korean Inst. Met. Mater. 47, 261 (2009).
J.W. Yoon, H.S. Chun, and S.B. Jung, Mater. Sci. Eng. A 483, 731 (2008).
P. Yao, P. Liu, and J. Liu, Microelectron. Eng. 86, 1969 (2009).
K. Gschneidner Jr., A. Russell, A. Pecharsky, J. Morris, Z. Zhang, T. Lograsso, D. Hsu, C.H.C. Lo, Y. Ye, A. Slager, and D. Kesse, Nat. Mater. 2, 587 (2003).
M. Satta, P. Rizzi, and M. Baricco, J. Alloys Compd. 483, 50 (2009).
Z. Zhang, A.M. Russell, S.B. Biner, K.A. Gschneidner Jr., and C.C.H. Lo, Intermetallics 13, 559 (2005).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Choi, H., Kaplan, W.D. & Choe, H. Effect of Yttrium on the Fracture Strength of the Sn-1.0Ag-0.5Cu Solder Joints. J. Electron. Mater. 45, 3259–3262 (2016). https://doi.org/10.1007/s11664-016-4489-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-016-4489-2