Abstract
Nanocrystalline PbS thin films are deposited on glass by direct coating from a precursor solution of lead acetate and thiourea in methanol. A single coating has a thickness of 50 nm and greater thicknesses are obtained from layer by layer deposition. The films are smooth and shiny with roughness (rms) of about 1.5 nm. X-ray diffraction studies show that films are cubic PbS with crystallite size about 10 nm. The films are p-type with dark electrical conductivities in the range of 0.4–0.5 S/cm. These films are basically photoconducting. Photoconductivity monotonically increases with increase in thickness. The band gap of the films strongly depends on the thickness of the films. The band gap decreases from 2.4 eV to 1.6 eV as the thickness is increased from 50 nm to 450 nm. The tunability of the band gap is useful for technical applications, such as solar cells and photodetectors.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
R. Debnath, J. Tang, D.A. Barkhouse, X. Wang, A.G. Pattantyus-Abraham, L. Brzozowski, L. Levina, and E.H. Sargent, J. Am. Chem. Soc. 132, 5952 (2010).
K. Szendrei, W. Gomulya, M. Yarema, W. Heiss, and M.A. Loi, Appl. Phys. Lett. 97, 203501 (2010).
J. Tang, L. Brzozowski, D.A.R. Barkhouse, X. Wang, R. Debnath, R. Wolowiec, E. Palmiano, L. Levina, A.G. Pattantyus-Abraham, D. Jamakosmanovic, and E.H. Sargent, ACS Nano 4, 869 (2010).
H. Choi, J. Kwan Kim, J. Hoon Song, Y. Kim, and S. Jeong, Appl. Phys. Lett. 102, 193902 (2013).
C. Piliego, L. Protesescu, S.Z. Bisri, M.V. Kovalenko, and M.A. Loi, Energy Environ. Sci. 6, 3054 (2013).
R. Debnath, M.T. Greiner, I.J. Kramer, A. Fischer, J. Tang, D.A.R. Barkhouse, X. Wang, L. Levina, Z.H. Lu, and E.H. Sargent, Appl. Phys. Lett. 97, 023109 (2010).
A.G. Pattantyus-Abraham, I.J. Kramer, A.R. Barkhouse, X. Wang, G. Konstantatos, R. Debnath, L. Levina, I. Raabe, M.K. Nazeeruddin, M. Grätzel, and E.H. Sargent, ACS Nano 4, 3374 (2010).
J. Tang, K.W. Kemp, S. Hoogland, K.S. Jeong, H. Liu, L. Levina, M. Furukawa, X. Wang, R. Debnath, D. Cha, K.W. Chou, A. Fischer, A. Amassian, J.B. Asbury, and E.H. Sargent, Nat. Mater. 10, 765 (2011).
I.J. Kramer and E.H. Sargent, Chem. Rev. 114, 863 (2014).
J.M. Luther, J. Gao, M.T. Lloyd, O.E. Semonin, M.C. Beard, and A.J. Nozik, Adv. Mater. 22, 3704 (2010).
P.R. Brown, R.R. Lunt, N. Zhao, T.P. Osedach, D.D. Wanger, L.Y. Chang, M.G. Bawendi, and V. Bulović, Nano Lett. 11, 2955 (2011).
J. Gao, C.L. Perkins, J.M. Luther, M.C. Hanna, H.Y. Chen, O.E. Semonin, A.J. Nozik, R.J. Ellingson, and M.C. Beard, Nano Lett. 11, 3263 (2011).
H. Wang, T. Kubo, J. Nakazaki, T. Kinoshita, and H. Segawa, J. Phys. Chem. Lett. 4, 2455 (2013).
C.-H.M. Chuang, P.R. Brown, V. Bulović, and M.G. Bawendi, Nat. Mater. 13, 1 (2014).
J. Tang, H. Liu, D. Zhitomirsky, S. Hoogland, X. Wang, M. Furukawa, L. Levina, and E.H. Sargent, Nano Lett. 12, 4889 (2012).
H. Liu, D. Zhitomirsky, S. Hoogland, J. Tang, I.J. Kramer, Z. Ning, and E.H. Sargent, Appl. Phys. Lett. 101, 1 (2012).
G. Konstantatos, I. Howard, A. Fischer, S. Hoogland, J. Clifford, E. Klem, L. Levina, and E.H. Sargent, Nature 442, 180 (2006).
G. Konstantatos and E.H. Sargent, Appl. Phys. Lett. 91, 173505 (2007).
G. Konstantatos, J. Clifford, L. Levina, and E.H. Sargent, Nat. Photonics 1, 531 (2007).
V. Sukhovatkin, S. Hinds, L. Brzozowski, and E.H. Sargent, Science 324, 1542 (2009).
C. Hu, A. Gassenq, Y. Justo, K. Devloo-Casier, H. Chen, C. Detavernier, Z. Hens, and G. Roelkens, Appl. Phys. Lett. 105, 171110 (2014).
J.P. Clifford, G. Konstantatos, K.W. Johnston, S. Hoogland, L. Levina, and E.H. Sargent, Nat. Nanotechnol. 4, 40 (2008).
B.N. Pal, I. Robel, A. Mohite, R. Laocharoensuk, D.J. Werder, and V.I. Klimov, Adv. Funct. Mater. 22, 1741 (2012).
F.W. Wise, Acc. Chem. Res. 33, 773 (2000).
L. Cademartiri, E. Montanari, G. Calestani, A. Migliori, A. Guagliardi, and G.A. Ozin, J. Am. Chem. Soc. 128, 10337 (2006).
I. Moreels, Y. Justo, B. De Geyter, K. Haustraete, J.C. Martins, and Z. Hens, ACS Nano 5, 2004 (2011).
M.A. Hines and G.D. Scholes, Adv. Mater. 15, 1844 (2003).
L. Cademartiri, J. Bertolotti, R. Sapienza, D.S. Wiersma, G. Von Freymann, and G.A. Ozin, J. Phys. Chem. B 110, 671 (2006).
I.J. Kramer, J.C. Minor, G. Moreno-Bautista, L. Rollny, P. Kanjanaboos, D. Kopilovic, S.M. Thon, G.H. Carey, K.W. Chou, D. Zhitomirsky, A. Amassian, and E.H. Sargent, Adv. Mater. 27, 116 (2015).
S. Jana, R. Thapa, R. Maity, and K.K. Chattopadhyay, Phys. E Low-Dimens. Syst. Nanostruct. 40, 3121 (2008).
S. Kaci, A. Keffous, M. Trari, H. Menari, and A. Manseri, J. Alloys Compd. 496, 628 (2010).
S.B. Pawar, J.S. Shaikh, R.S. Devan, Y.R. Ma, D. Haranath, P.N. Bhosale, and P.S. Patil, Appl. Surf. Sci. 258, 1869 (2011).
N.B. Kotadiya, A.J. Kothari, D. Tiwari, and T.K. Chaudhuri, Appl. Phys. A Mater. Sci. Process. 108, 819 (2012).
A. Hussain, A. Begum, and A. Rahman, Indian J. Phys. 86, 697 (2012).
T.K. Chaudhuri, H.N. Acharya, and B.B. Nayak, Thin Solid Films 83, L169 (1981).
P. Scherrer, Nachr. Ges. Wiss. Göttingen 2, 96 (1918).
J. Tauc and A. Menth, J. Non. Cryst. Solids 8–10, 569 (1972).
A.M. Fox, Optical Properties of Solids, 1st ed. (Oxford: Oxford University Press, 2001).
F. Kicinski, Chem. Ind. 17, 54 (1948).
S. Espevik, C. Wu, and R.H. Bube, J. Appl. Phys. 42, 3513 (1971).
R.H. Harada and H.T. Minden, Phys. Rev. 102, 1258 (1956).
G.H. Blount, P.J. Schreiber, D.K. Smith, and R.T. Yamada, J. Appl. Phys. 44, 978 (1973).
Acknowledgement
The authors are grateful to the President and Provost of CHARUSAT for supporting this work. D.V. is grateful to the Department of Science and Technology (GoI) for providing an Inspire Fellowship.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Vankhade, D., Kothari, A. & Chaudhuri, T.K. Direct-Coated Photoconducting Nanocrystalline PbS Thin Films with Tunable Band Gap. J. Electron. Mater. 45, 2789–2795 (2016). https://doi.org/10.1007/s11664-016-4364-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-016-4364-1