Abstract
Ce-doped Pb1−x Ce x Te alloys with x = 0, 0.005, 0.01, 0.015, 0.03, and 0.05 were prepared by induction melting, ball milling, and spark plasma sintering techniques. The structure and thermoelectric properties of the samples were investigated. X-ray diffraction (XRD) analysis indicated that the samples were of single phase with NaCl-type structure for x less than 0.03. The lattice parameter a increases with increasing Ce content. The lower Ce-doped samples (x = 0.005 and 0.01) showed p-type conduction, whereas the pure PbTe and the higher doped samples (x = 0, 0.015, 0.03, and 0.05) showed n-type conduction. The lower Ce-doped samples exhibited a much higher absolute Seebeck coefficient, but the higher electrical resistivity and higher thermal conductivity compared with pure PbTe resulted in a lower figure of merit ZT. In contrast, the higher Ce-doped samples exhibited a lower electrical resistivity, together with a lower absolute Seebeck coefficient and comparable thermal conductivity, leading to ZT comparable to that of PbTe. The lowest thermal conductivity (range from 0.99 W m−1 K−1 at 300 K to 0.696 W m−1 K−1 at 473 K) was found in the alloy Pb0.95Ce0.05Te due to the presence of the secondary phases, leading to a ZT higher than that of pure PbTe above 500 K. The maximum figure of merit ZT, in the alloy Pb0.95Ce0.05Te, was 0.88 at 673 K.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
L.E. Bell, Science 321, 1457 (2008).
B. Yu, Q.Y. Zhang, H. Wang, X.W. Wang, H.Z. Wang, D.Z. Wang, H. Wang, G. Jeffrey Snyder, G. Chen, and Z.F. Ren, J. Appl. Phys. 108, 016104 (2010).
J.R. Sootsman, H.J. Kong, C. Uher, J.J. D’Angelo, C. Wu, T.P. Hogan, T. Caillat, and M.G. Kanatzidis, Angew. Chem. Int. Ed. 47, 8618 (2008).
K.F. Hsu, S. Loo, F. Guo, W. Chen, J.S. Dyck, C. Uher, T. Hogan, E.K. Polychroniadis, and M.G. Kanatzidis, Science 303, 818 (2004).
B. Paul, V. Ajay Kumar, and P. Banerji, J. Appl. Phys. 108, 064322 (2010).
K. Nouneh, K.J. Plucinski, M. Bakasse, and I.V.J. Kityk, Mater. Sci. 42, 6847 (2007).
K. Ahn, C.P. Li, C. Uher, and M.G. Kanatzidis, Chem. Mater. 21, 1361 (2009).
K. Ahn, C.P. Li, C. Uher, and M.G. Kanatzidis, Chem. Mater. 22, 876 (2010).
P. Fita, K. Smoliński, Z. Golacki, and K. Lawniczak- Jablonska, Appl. Phys. 68, 681 (1999).
T.B. Massalski, eds., Binary Alloy Phase diagram, Vol. 2 (Metals Park, OH: American Society for Metals, 1990), p. 1118.
H.S. Dow, M.W. Oh, B.S. Kim, S.D. Park, B.K. Min, H.W. Lee, and D.M. Wee, J. Appl. Phys. 108, 113709 (2010).
P.M. Nikolić, K.T. Radulović, S.S. Vujatović, D. Vasiljević-Radović, S. Đurić, V. Blagojević, P. Mihajlović, D. Urošević, Z. Dohčević-Mitrović, and O. Jakšić, J. Optoelectron. Adv. Mater. 2, 465 (2000).
H. Li, K.F. Cai, H.F. Wang, L. Wang, J.L. Yin, and C.W. Zhou, J. Solid State Chem. 182, 869 (2009).
M. Orihashi, Y. Noda, L.D. Chen, T. Goto, and T. Hirai, J. Phys. Chem. Solids. 61, 919 (2000).
Y.Q. Cao, T.J. Zhu, and X.B. Zhao, J. Phys. D: Appl. Phys. 42, 015406 (2009).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Li, J., Li, S., Wang, Q. et al. Effect of Ce-Doping on Thermoelectric Properties in PbTe Alloys Prepared by Spark Plasma Sintering. J. Electron. Mater. 40, 2063–2068 (2011). https://doi.org/10.1007/s11664-011-1715-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-011-1715-9