Abstract
We report on wafer-level measurements of the long-term stability of Ti and Ni ohmic contacts to n-4H-SiC during thermal treatments in air or air/moisture environments up to 500°C. Contact metallizations with and without a sputtered Ti (20 nm)/TaSi x (200 nm)/Pt (150 nm) diffusion barrier stack and Ti (20 nm)/TiN (10 nm)/Pt (150 nm)/Ti (20 nm) interconnects were compared. A protective coating consisting of a SiO x (250 nm)/SiN y (250 nm) stack deposited by plasma-enhanced chemical vapor deposition (PECVD) was used. The stability of the contact metallizations during long-term thermal treatments in air and air/moisture was studied. The best performance was achieved with Ti ohmic contacts without the Ti/TaSi x /Pt stack. This system successfully withstood 1000 h thermal treatment at 500°C in air followed by 1000 h at 500°C in air/10% moisture. After the aging, the contact failure ratio was below 1% and the specific contact resistivity amounted to (2.5 ± 1.1) × 10−4 Ω cm2. Scanning electron microscopy (SEM) cross-sectional analysis indicated no degradation in the contact metallization, demonstrating the effectiveness of the SiO x /SiN y protective coating in preventing oxidation of the contacts. These results are very promising for applications in harsh environments, where the stability of ohmic contacts is crucial.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
E. Kohn, Comprehensive Microsystems, Vol. 1 (Oxford: Elsevier Science, 2008), pp. 131–173.
R. Cheung, Silicon Carbide Micro Electromechanical Systems for Harsh Environments (London: Imperial College Press, 2006), pp. 128–168.
G.F. Eriksen and K. Dyrbye, J. Micromech. Microeng. 6, 55 (1996).
M.T. Soo, K.Y. Cheong, and A.F.M. Noor, Sens. Actuators B 151, 39 (2010).
R.S. Okojie, D. Spry, J. Krotine, C. Salupo, and D.R. Wheeler, Mater. Res. Soc. Symp. Proc., Vol. 622 (2000), p. T8.3.1–6.
R.S. Okojie, D. Lukco, Y.L. Chen, and D.J. Spry, J. Appl. Phys. 91, 6553 (2002).
R.S. Okojie, D. Lukco, Y.L. Chen, D. Spry, and C. Salupo, Mat. Res. Soc. Symp. Proc. Vol. 640 (2001), p. H7.5.1–6.
A. Virshup, L.M. Porter, D. Lukco, K. Buchholt, L. Hultman, and A.L. Spetz, J. Electron. Mater. 38, 569 (2009).
S.-W. Lee, E.-K. Suh, N.-K. Cho, H.-D. Park, L. Uneus, and A.L. Spetz, Solid State Electron. 49, 1297 (2005).
R.M. Tiggelaar, R.G.P. Sanders, A.W. Groenland, and J.G.E. Gardeniers, Sens. Actuators A 152, 39 (2009).
S.L. Firebaugh, K.F. Jensen, and M.A. Schmidt, J. Microelectromech. Syst. 7, 128 (1998).
W.R. Farner, R. Job, and M. Werner, Microsyst. Technol. 7, 138 (2001).
W. Daves, A. Krauss, N. Behnel, V. Häublein, A. Bauer, and L. Frey, Thin Solid Films (2011). doi:10.1016/j.tsf.2011.02.089.
W. Daves, A. Krauss, M. Le-Huu, S. Kronmüller, V. Häublein, A. Bauer, and L. Frey, Mater. Sci. Forum 679–680, 449 (2011).
G.K. Reeves, Solid State Electron. 23, 487 (1980).
D.K. Schroder, Semiconductor Material and Device Characterization (Hoboken, NJ: Wiley, 2006), p. 127.
C.A. Hewett, M.J. Taylor, J.F. Zeidler, and M.W. Geis, J. Appl. Phys. 77, 755 (1995).
J.H. Park and P.H. Holloway, J. Vac. Sci. Technol. B 23, 2530 (2005).
M.H. Ervin, K.A. Jones, U. Lee, and M.C. Wood, J. Vac. Sci. Technol. B 24, 1185 (2006).
B. Pécz, Appl. Surf. Sci. 184, 287 (2001).
M. Siad, C.P. Vargas, M. Nkosi, D. Saidi, N. Souami, N. Daas, and A.C. Chami, Appl. Surf. Sci. 256, 256 (2009).
L.M. Porter and R.F. Davis, Mater. Sci. Eng. B 34, 83 (1995).
W.J. Choyke, H. Matsunami, and G. Pensl, Silicon carbide. Recent major advances (Heidelberg: Springer, 2004), pp. 343–366.
B. Pécz, Phys. Stat. Sol. 195, 214 (2003).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Daves, W., Krauss, A., Häublein, V. et al. Enhancement of the Stability of Ti and Ni Ohmic Contacts to 4H-SiC with a Stable Protective Coating for Harsh Environment Applications. J. Electron. Mater. 40, 1990–1997 (2011). https://doi.org/10.1007/s11664-011-1681-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-011-1681-2