Abstract
Electroless Ni-P layers with three different P contents (6.1 wt.%, 8.8 wt.%, and 12.3wt.%) were deposited on copper (Cu) substrates. Multilayered samples of Sn-3.5Ag/Ni-P/Cu stack were prepared and subjected to multiple reflows at 250°C. A tensile test was performed to investigate the effect of P content on the solder joint strength. The low P samples exhibited the highest joint strength after multiple reflows, while the strength of medium and high P samples decreased more rapidly. From interfacial analysis, the Ni3Sn4 intermetallic compound (IMC) formed at the interface of low P sample was found to be more stable, while the one of medium and high P samples spalled into the molten solder. The IMC spallation sped up the consumption of electroless Ni-P, leading to the large formation of Cu-Sn IMCs. Fractographic and microstructural analyses showed that the degradation in solder joint strength was due to the formation of layers of voids and growth of Cu-Sn IMCs between the solder and the Cu substrate.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
A.A. Liu, H.K. Kim, K.N. Tu, and P.A. Totta, J. Appl. Phys. 80, 2774 (1996).
J.W. Jang, L.N. Ramanathan, J.K. Lin, and D.R. Frear, J. Appl. Phys. 95, 8286 (2004).
K.N. Tu and K. Zeng, Mater. Sci. Eng. R 34, 1 (2001).
K.L. Lin and Y.C. Liu, IEEE Trans. Adv. Packaging 22, 568 (1999).
J.W. Jang, P.G. Kim, K.N. Tu, D.R. Frear, and P. Thompson, J. Appl. Phys. 85, 8456 (1999).
G.O. Mallory and J.B. Haidu, Electroless Plating: Fundamentals and Applications (Orlando, FL: American Electroplaters and Surface Finishers Society, 1990), ch. 4.
Y.C. Chen, P.L. Tu, C.W. Tang, K.C. Hung, and K.L. Joseph, IEEE Trans. Adv. Packaging 24, 25 (2001).
M. He, Z. Chen, and G. Qi, Acta Mater. 52, 2047 (2004).
A. Kumar, M. He, and Z. Chen, Surf. Coating Technol. 198, 283 (2005).
A. Kumar, Z. Chen, S. Mhaisalkar, C.C. Wong, P.S. Teo, and V. Kripesh, Thin Solid Films 504, 410 (2006).
Y. Chonan, T. Komiyama, J. Onuki, R. Urao, T. Kimura, and T. Nagano, Mater. Trans. 43, 1840 (2002).
M.O. Alam, Y.C. Chan, and K.N. Tu, J. Appl. Phys. 94, 4108 (2003).
Y.C. Sohn, J. Yu, S.K. Kang, D.Y. Shih, and W.K. Choi, J. Electron. Mater. 33, 790 (2004).
C.Y. Lee and K.L. Lin, Thin Solid Films 249, 201 (1994).
Z. Chen, M. He, and G. Qi, J. Electron. Mater. 33, 1465 (2004).
Y.C. Sohn, J. Yu, S.K. Kang, D.Y. Shih, and T.Y., Lee, J. Mater. Res. 19, 2428 (2004).
A. Kumar and Z. Chen, Proc. 7th Electronic Packaging and Technology Conf. (Piscataway, NJ: IEEE, 2005), p. 873.
Y.C. Sohn, J. Yu, S.K. Kang, D.Y. Shih, and T.Y. Lee, Electronic Components and Technology Conf. (2005).
A. Kumar and Z. Chen, Mater. Sci. Eng. A, in press.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chen, Z., Kumar, A. & Mona, M. Effect of phosphorus content on Cu/Ni-P/Sn-3.5Ag solder joint strength after multiple reflows. J. Electron. Mater. 35, 2126–2134 (2006). https://doi.org/10.1007/s11664-006-0322-7
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11664-006-0322-7