Abstract
In-situ tensile tests of as-cast 96.5Sn3.5Ag eutectic solder were performed under the scanning electron microscope (SEM) using different strain rates at room temperature, and various crack initiation and propagation behavior was observed on the specimen surface. It was found that, due to the existence of Ag3Sn intermetallic particles and the special microstructure of β-Sn phases in Sn3.5Ag solder, grain boundary sliding (GBS) was no longer the dominant mechanism for this Pb-free solder. In the lower strain rate regime, accompanied by partial intragranular cracks, intergranular fracture along the grain boundaries in Sn-Ag eutectic structure or along the interphase boundaries between Sn-rich dendrites and Sn-Ag eutectic phases occurred primarily for the Sn3.5Ag solder in the early tensile stage. However, significant plastic deformation was observed in large areas for the specimens tested at higher strain rates, and cracks propagated in a transgranular manner across the Sn dendrites and Sn-Ag eutectic structure.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
F. Hua and J. Glazer, Design and Reliability of Solder Interconnections, ed. R.K. Mahidhara, D.R. Frear, S.M.L. Sastry, K.L. Murty, P.K. Liaw, and W. Winterbottom (Warrendale, PA: TMS, 1997), pp. 65–73.
W. Yang, L.E. Felton, and R.W. Messler, J. Electron. Mater. 24, 1465 (1995).
H.D. Solomon, J. Electron. Packaging 113, 102 (1991).
J. Liang, N. Gollhardt, P.S. Lee, S.A. Schroeder, and W.L. Morris, Fatigue Fract. Eng. Mater. Struct. 19, 1401 (1996).
V.I. Igoshev, J.I. Kleiman, D. Shangguan, C. Lock, S. Wong, and M. Wiseman, J. Electron. Mater. 27, 1367 (1998).
W.K. Jones, Y. Liu, M. Shah, and R. Clarke, Soldering Surface Mount Technol. 10, 37 (1998).
Y. Karita, Y. Hirata, and M. Otsuka, J. Electron. Mater. 28, 1263 (1999).
C. Kanchanomai, Y. Miyashita, and Y. Mutoh, J. Electron. Mater. 31, 142 (2002).
C. Kanchanomai, Y. Miyashita, Y. Mutoh, and S.L. Mannan, Mater. Sci. Eng. A 345, 90 (2003).
C. Kanchanomai and Y. Mutoh, Mater. Sci. Eng. A 381, 113 (2004).
M. Kerr and N. Chawla, JOM, 56 (6) (2004), pp. 50–54.
C. Kanchanomai, Y. Miyashita, and Y. Mutoh, Int. J. Fatigue 24, 987 (2002).
S. Wiese, F. Feustel, and E. Meusel, Sensors Actuators A 99, 188 (2002).
Z. Guo, A.F. Sprecher, and H. Conrad, J. Electron. Packaging 114, 112 (1992).
J.W. Morris, Jr., H.G. Song, and F. Hua, 2003 Electron. Components Technol. Conf., 54 (2003).
Y. Ding, C.Q. Wang, M.Y. Li, and H. Bang, Mater. Lett. 59, 697 (2005).
Y. Ding, C. Wang, M. Li, and H.-S. Bang, Mater. Sci. Eng. A 384, 314 (2004).
Hael Mughrabi-Weinheim, Materials Science and Technology: A Comprehensive Treatment (New York: Cambridge, 1998), pp. 7–11.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ding, Y., Wang, C. & Li, M. Scanning electron microscope in-situ investigation of fracture behavior in 96.5Sn3.5Ag lead-free solder. J. Electron. Mater. 34, 1324–1335 (2005). https://doi.org/10.1007/s11664-005-0258-3
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11664-005-0258-3