Abstract
In general, formation and growth of intermetallic compounds (IMCs) play a major role in the reliability of the solder joint in electronics packaging and assembly. The formation of Cu-Sn or Ni-Sn IMCs have been observed at the interface of Sn-rich solders reacted with Cu or Ni substrates. In this study, a nanoindentation technique was employed to investigate nanohardness and reduced elastic moduli of Cu6Sn5, Cu3Sn, and Ni3Sn4 IMCs in the solder joints. The Sn-3.5Ag and Sn-37Pb solder pastes were placed on a Cu/Ti/Si substrate and Ni foil then annealed at 240°C to fabricate solder joints. In Sn-3.5Ag joints, the magnitude of the hardness of the IMCs was in the order Ni3Sn4>Cu6Sn5>Cu3Sn, and the elastic moduli of Cu6Sn5, Cu3Sn, and Ni3Sn4 were 125 GPa, 136 GPa, and 142 GPa, respectively. In addition, the elastic modulus of the Cu6Sn5 IMC in the Sn-37Pb joint was similar to that for the bulk Cu6Sn5 specimen but less than that in the Sn-3.5Ag joint. This might be attributed to the strengthening effect of the dissolved Ag atoms in the Cu6Sn5 IMC to enhance the elastic modulus in the Sn-3.5Ag/Cu joint.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
C.S. Chang, A. Oscilowski, and R.C. Bracken, IEEE Circuit. Dev. 14, 45 (1998).
J.H. Lau, Flip Chip Technologies (New York: McGraw-Hill, 1996), pp. 26–30.
K.L. Lin and Y.C. Liu, Proc. Electronic Components Technology Conf. (Piscataway, NJ: IEEE, 1999), pp. 607–612.
K. Zeng and K.N. Tu, Mater. Sci. Eng. R 38, 55 (2002).
C.S. Huang, J.G. Duh, Y.M. Chen, and J.H. Wang, J. Electron. Mater. 32, 89 (2003).
H.H. Manko, Solders and Soldering (New York: McGraw-Hill, 2001), pp. 61–167.
A.A. Liu, H.K. Kim, K.N. Tu, and P.A. Totta, J. Appl. Phys. 80, 2774 (1996).
H.K. Kim, K.N. Tu, and P.A. Totta, Appl. Phys. Lett. 68, 2204 (1996).
C.S. Huang, G.Y. Jang, and J.G. Duh, J. Electron. Mater. 32, 1273 (2003).
H.W. Miao and J.G. Duh, Mater. Chem. Phys. 71, 255 (2001).
D.R. Frear, J.W. Jang, J.K. Lin, and C. Zang, JOM 53, 28 (2001).
M. McCormack, S. Jin, G.W. Kammlott, and H.S. Chen, Appl. Phys. Lett. 63, 15 (1993).
J.S. Kang, R.A. Gagliano, G. Ghosh, and M.E. Fine, J. Electron. Mater. 31, 1238 (2002).
R.J. Fields, S.R. Low III, and G.K. Lucey, Jr. in The Metal Science of Joining, eds. M.J. Cieslak, J.H. Perepezko, S. Kang, and M.E. Glicksman (Warrendale, PA: TMS, 1991), pp. 165–174.
L.M. Ostrovskaya, V.N. Rodin, and A.I. Kuznetsov, Sov. J. Non-Ferrous Metall. (Tsv. Metally) 26, 90 (1985).
R.R. Chromik, R.P. Vinci, S.L. Allen, and M.R. Notis, JOM 55, 66 (2003).
R.R. Chromik, R.P. Vinci, S.L. Allen, and M.R. Notis, J. Mater. Res. 18, 2251 (2003).
J.I. Goldstein, Scanning Electron Microscopy and X-ray Microanalysis (New York: Plenum Press, 1992), pp. 306–330.
W.C. Oliver and G.M. Pharr, J. Mater. Res. 7, 1564 (1992).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Jang, GY., Lee, JW. & Duh, JG. The nanoindentation characteristics of Cu6Sn5, Cu3Sn, and Ni3Sn4 intermetallic compounds in the solder bump. J. Electron. Mater. 33, 1103–1110 (2004). https://doi.org/10.1007/s11664-004-0111-0
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11664-004-0111-0