Abstract
The microstructure of solder plays a key role in the reliability of electronic packages. In this study, the cyclic shear deformation experienced by Sn-37Pb solder joints was simulated by thermomechanically cycling model joints between 30°C and 125°C, and the nature of the damage investigated. Most of the developed shear strain was accommodated by the solder adjacent to the interface with the intermetallic layer, and its severity diminished exponentially with distance from the interface. Shear bands formed at this location and within the shear bands, significant microstructural coarsening occurred together with crack initiation on the outer free surface of the solder. Subsequent cycling produced multiple cracking, fragmentation, and macroscopic decohesion, progressing toward the interior of the solder. Secondary cracks initiated from the primary cracks and propagated along colony boundaries in the surface layers of the solder perpendicular to the shear direction. In the interior of the solder, well away from the interface with the intermetallic layer, a limited amount of coarsening occurred. Apart from smoothing of undulations, the intermetallic layer was unaffected.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
S.K. Kang and A.K. Sarkhel, J. Electron. Mater. 23, 701 (1994).
K.C. Liu and J.G. Duh, IEEE Trans. Comp. Hybrids Manuf. Technol. 14, 703 (1991).
J. Lynch and A. Boetti, Thermal Stress and Strain in Microelectronics Packaging, ed. J.H. Lau (New York: Van Nostrand Reinhold, 1994), pp. 579–606.
J.H. Lau and Y.H. Pao, Solder Joint Reliability of BGA, CSP, Flip, Chip, and Fine Pitch SMT Assemblies (New York: McGraw-Hill, 1997), pp. 153–218.
R.N. Wild, Welding Res. Suppl. 51, 521s (1972).
J.T. Lynch, M.R. Ford, and A. Boetti, IEEE Trans. Comp. Hybrids Manuf. Technol. 6, 237 (1983).
D. Frear, IEEE Trans. Comp. Hybrids Manuf. Technol. 12, 492 (1989).
P. Hacke, A.F. Sprecher, and H. Conrad, ASME J. Electron. Packag. 115, 153 (1993).
J.W. Morris, Jr., J.L. Freer Goldstein, and Z. Mei, The Mechanics of Solder Alloy Interconnections, ed. D. Frear, H. Morgan, S. Burchett, and J. Lau (New York: Van Nostrand Reinhold, 1994), pp. 7–41.
Z. Guo and H. Conrad, ASME J. Electron. Packag. 115, 159 (1993).
J.L. Marshall, L.A. Foster, and J.A. Sees, The Mechanics of Solder Alloy Interconnections, ed. D. Frear, H. Morgan, S. Burchett, and J. Lau (New York: Van Nostrand Reinhold, 1994), pp. 42–60.
K. Jung and H. Conrad, J. Electron. Mater. 30, 1294 (2001).
H.L.J. Pang, K.H. Tan, X.Q. Shi, and Z.P. Wang, Mater. Sci. Eng. A307, 42 (2001).
D. Frear, D. Grivas, and J.W. Morris, Jr., J. Electron. Mater. 17, 171 (1988).
H.D. Solomon, Low-Frequency, High-Temperature Low Cycle Fatigue of 60Sn-40Pb Solder, ASTM STP 942 (Philadelphia, PA: ASTM, 1988).
P.M. Hall, T.D. Dudderar, and J.F. Argyle, IEEE Trans. Comp. Hybrids Manuf. Technol. 6, 544 (1983).
X.W. Liu and W.J. Plumbridge, “Fatigue of Sn-37Pb Solder Joints under Thermomechanical Cycling,” in preparation for publication.
A.R. Syed, J. Electron. Packag. 117, 116 (1995).
D.R. Frear, IEEE Trans. Comp. Hybrids Manuf. Technol. 12, 492 (1983).
X.W. Liu, (Ph.D. thesis, The Open University, England, 1999).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Liu, X.W., Plumbridge, W.J. Damage produced in model solder (Sn-37Pb) joints during thermomechanical cycling. J. Electron. Mater. 32, 278–286 (2003). https://doi.org/10.1007/s11664-003-0222-z
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11664-003-0222-z