Abstract
Four-point bend (4PB) tests of notched specimens loaded at various loading rates, for low alloy steel with different grain sizes, were done, and the microscopic observation and finite-element method (FEM) calculations were carried out. It was found that for the coarse-grained (CG) microstructure, an appreciable drop in notch toughness with a loading rate of around 60 mm/min appeared, and further increasing the loading rate leads to a slight additional decrease in notch toughness. For the fine-grained (FG) microstructure, the effect of loading rate was not apparent. The change in toughness resulted from a change of the critical event controlling the cleavage fracture with increasing loading rate. For the CG microstructure with a lower cleavage-fracture stress (σ f ), with an increasing loading rate, the critical event of cleavage fracture can be changed from the propagation of a pearlite colony-sized crack or a ferrite grain-sized crack, through the mixed critical events of crack propagation and crack nucleation, then to crack nucleation. This change deteriorates the toughness. For the FG microstructure with a higher cleavage-fracture stress, the critical event of cleavage fracture is the crack propagation and does not change in the loading-rate range from 120 to 500 mm/min. The measured σ f values do not change with loading rate, as long as the critical event of cleavage fracture does not change. The higher notch toughness of the FG microstructure arises from its higher σ f and the critical plastic strain (ε pc ) for initiating a crack nucleus, and the fracture behavior of this FG steel is not sensitive to loading rate in the range of this work.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
D.A. Curry, I. Milne, and R.S. Gates: Mater. Sci. Eng., 1984, vol. 63, pp. 101–09.
H. Couque, R.J. Asaro, J. Duffy, and S.H. Lee: Metall Trans. A, 1988, vol. 19A, pp. 2179–206.
A.K. Zurek, P.S. Follansbee, and J. Hack: Metall. Trans. A, 1990, vol. 21A, pp. 431–39.
S. Lee, J.W. Rhyu, K.M. Cho, and J. Duffy: Metall. Trans. A, 1993, vol. 24A, pp. 901–12.
H. Qiu, H. Mori, M. Enoki, and T. Kishi: Metall. Mater. Trans. A, 2000, vol. 31A, pp. 2785–91.
A. Venkert, P.R. Gudure, and G. Ravichandran: J. Eng. Mater. Technol., 2001, vol. 123, pp. 261–67.
M.S. Mirza, D.C. Barton, and P. Church: J. Mater. Sci., 1996, vol. 31, pp. 453–61.
J.H. Yoon, B.S. Lee, Y.J. Oh, and J.H. Hong: Int. J. Pressure Vessels Piping, 1999, vol. 76, pp. 663–70.
V. Jablokov, D.M. Goto, D.A. Koss, and J.B. McKirgan: Mater. Sci. Eng. A, 2001, vol. 302, pp. 197–205.
M.G. Mendiratta, R.L. Goetz, and D.M. Dimiduk: Metall. Mater. Trans. A, 1996, vol. 27A, pp. 3903–12.
G.Z. Wang and J.H. Chen: Int. J. Fract., 1998, vol. 89, pp. 269–84.
J.J. Lewandowski and A.W. Thompson: Acta Metall. 1987, vol. 35, pp. 1453–66.
J.H. Chen and C. Yan: Mater. Sci. Technol., 1988, vol. 4, pp. 732–39.
D.J. Alexander, J.J. Lewandowski, W.J. Sisak, and A.W. Thompson: J. Mech. Phys. Solids, 1986, vol. 34, pp. 433–54.
M. Srinivas and S.V. Kamat: Mater. Sci. Technol., 2001, vol. 17, pp. 529–35.
J.S. Lin: Ph.D. Thesis, Xian Jiaotong University, Xian, China, 1989.
J.R. Griffiths and D.R.J. Owen: J. Mech. Phys. Solids, 1971, vol. 19, pp. 419–31.
J.H. Chen, G.Z. Wang, Y. Chen, H. Ma, and L. Zhu: Int. J. Fract., 1997, vol. 83, pp. 105–20.
C.J. McMahon and M. Cohen: Acta Metall., 1965, vol. 13, pp. 591–605.
E. Smith: Proc. Conf. on the Physical Basis of Yield and Fracture, Physics Society, Oxford, United Kingdom, 1966, pp. 36–53.
D.A. Curry and J.F. Knott: Mater. Sci., 1978, Nov., pp. 511–14.
G.T. Hahn: Metall. Trans. A, 1984, vol. 15A, pp. 947–59.
M. Wall, C.E. Lane, and C.A. Hippsley: Acta Metall. Mater., 1994, vol. 42, pp. 1295–309.
G. Oates and J.R. Griffiths: Met. Sci. J., 1869, vol. 3, pp. 111–15.
J.H. Chen, G.Z. Wang, and H. Ma: Metall. Trans. A, 1990, vol. 21A, pp. 321–30.
T. Lin, A.G. Evans, and R.O. Ritchie: J. Mech. Phys. Solids, 1986, vol. 34, pp. 477–97.
J.H. Chen, G.Z. Wang, and Q. Wang: Metall. Mater. Trans. A, 2002, vol. 33A, pp. 3393–402.
J.H. Chen, Z. Li, and G.Z. Wang: Metall. Mater. Trans. A, 2003, vol. 34A, pp. 1055–68.
G.Z. Wang, J.H. Chen, and Z.H. Li: Metall. Mater. Trans. A, 1997, vol. 28A, pp. 1689–99.
G.Z. Wang and J.H. Chen: Fatigue Fract. Eng. Mater. Struct., 2001, vol. 24, pp. 451–59.
R.O. Ritchie, J.F. Knott, and J.R. Rice: J. Mech. Phys. Solids, 1973, vol. 21, pp. 395–410.
F.M. Beremin: Metall. Trans. A, 1983, vol. 14A, pp. 2277–87.
J.J. Lewandowski and A.W. Thompson: Metall. Trans. A, 1986, vol. 17A, pp. 1769–86.
A.V. Samant and J.J. Lewandowski: Metall. Mater. Trans. A, 1997, vol. 28A, pp. 389–99.
J.H. Chen, L. Zhu, and H. Ma: Acta Metall. Mater., 1990, vol. 38, pp. 2527–35.
J.H. Chen, X.J. Hu, and G.Z. Wang: Fatigue Fract. Eng. Mater. Struct., 1996, vol. 19, pp. 68–80.
G.Z. Wang, H.J. Wang, and J.H. Chen: Fatigue Fract. Eng. Mater. Struct., 1999, vol. 22, pp. 849–58.
G.Z. Wang, G.H. Liu, and J.H. Chen: Int. J. Fract., 2001, vol. 112, pp. 183–96
D.A. Curry: Met. Sci., 1980, vol. 14, pp. 319–23.
T. Miyata, R.C. Yang, A. Otsuka, T. Haze, and S. Ahira: Advances in Fracture Research, Proc. ICF6, K Salama, K. Ravi-Chander, R. Taplin, and P. Rama Rao, eds., Pergamon Press, Houston, TX, 1989, pp. 2563–572.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Wang, G.Z., Chen, J.H. & Ren, X.C. Effects of loading rate on fracture behavior of low-alloy steel with different grain sizes. Metall Mater Trans A 35, 1765–1778 (2004). https://doi.org/10.1007/s11661-004-0085-9
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-004-0085-9