Abstract
Strength development in the mushy zone during solidification of three aluminum alloys (Al-4 wt pct Cu, Al-7 wt pct Si-1 wt pct Cu, and Al-7 wt pct Si-4 wt pct Cu) has been measured with two different techniques—horizontal tensile testing and direct shear cell testing. The strength results from the two methods correspond with one another to a much higher degree than suggested by the results presented in the literature. Tensile strength starts to develop at the maximum packing solid fraction, confirmed by the shear strength measurements. The maximum packing fraction represents the point where the internal network structure of the mushy zone is established and ligaments of the network must be broken to rearrange the dendrites. The data indicate a converging trend of the shear and tensile strength at high solid fractions, therefore indicating that the deformation mechanisms are also becoming similar. The results presented in this article suggest that it is possible to develop constitutive equations for the mechanical properties of the mushy zone over the entire solid fraction regime, i.e., from coherency to complete solidification. These equations could be used for the prediction of stress development as well as defect formation.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
A.K. Dahle and L. Arnberg: JOM, 1996, vol. 48 (3), pp. 34–37.
A.K. Dahle and D.H. StJohn: Acta Mater., 1999, vol. 47, pp. 31–41.
A.K. Dahle and D.H. StJohn: Trans. 20th Int. Die Casting Congress & Exposition, North American Die Casting Association (NADCA), Rosemont, IL, Cleveland, OH, November 1–4, 1999, pp. 203–10.
J. Campbell: Castings, Butterworth-Heinemann Ltd, Oxford, UK, 1991.
A.K. Dahle, L. Arnberg, and D. Apelian: AFS Trans., 1997, vol. 105, pp. 963–70.
D.R. Gunasegaram, A.K. Dahle, and T.T. Nguyen: AFS Trans., 1999, vol. 107, pp. 257–63.
Z.H. Lee, T.G. Kim, and Y.S. Choi: Metall. Mater. Trans. B, 1998, vol. 29B, pp. 1051–56.
T.G. Kim and Z.H. Lee: Int. J. Heat Mass Transfer, 1997, vol. 40, pp. 3513–25.
M. Kubota and S. Kitaoka: AFS Trans., 1973, vol. 81, pp. 424–27.
T. Isobe, M. Kubota, and S. Kitaoka: Proc. 47th World Foundry Congr., Jerusalem, Israel, 1980, pp. 559–89.
B. Forest and S. Bercovici: Solidification Technology in the Foundry and Casthouse, The Metals Society, London, 1983, pp. 607–12.
P. Wisniewski and H.D. Brody: in Modelling of Casting, Welding and Advanced Solidification Processes V, M. Rappaz, M.R. Ozgu, and K.W. Mahin, eds., TMS Warrendale, PA, 1991, pp. 273–78.
C.H. Dickhaus, L. Ohm, and S. Engler: AFS Trans., 1993, vol. 101, pp. 677–84.
J.A. Spittle, S.G.R. Brown, J.D. James, and R.W. Evans: Proc. 7th Int. Symp. on Physical Simulation, Tsukuba, Japan, 1997, pp. 81–91.
P. Suvanchai, T. Okane, and T. Umeda: in Solidification Processing 1997, J. Beech and H. Jones, eds., The University of Sheffield, Sheffield, 1997, pp. 190–94.
M.G. Chu and D.A. Granger: in Solidification Processing 1997, J. Beech and H. Jones, eds., The University of Sheffield, Sheffield, 1997, pp. 198–202.
H. Mizukami, M. Kawamoto, and T. Watanabe: in Solidification Processing 1997, J. Beech and H. Jones, eds., The University of Sheffield, Sheffield, 1997, pp. 222–25.
S. Instone: Ph.D. Thesis, The University of Queensland, Brisbane, Australia, 1999.
S. Instone, D. StJohn, and J. Grandfield: Int. J. Cast Met. Res., 2000, vol. 12, pp. 441–56.
A.A. Tseng, J. Horsky, M. Raudensky, and P. Kotrbacek: Mater. Design, 2001, vol. 22 (2), pp. 83–92.
A.K. Dahle and L. Arnberg: Proc. 4th Int. Conf. on Aluminum Alloys, Atlanta, GA, 1994, T.H. Sanders, Jr. and E.A. Starke, Jr., eds., Georgia Institute of Technology, Atlanta, GA, pp. 91–98.
A.K. Dahle and L. Arnberg: Acta Mater., 1997, vol. 45, (2), pp. 547–59.
A.K. Dahle, S.M. Nabulsi, and D.H. StJohn: AFS Trans., 1998, vol. 106, pp. 137–42.
S. Nabulsi, Ph.D. Thesis, The University of Queensland, Brisbane, Australia, 1999.
T. Sumitomo, D.H. StJohn, and T. Steinberg: Mater. Sci. Eng., 2000, vol. A289, pp. 18–29.
A.K. Dahle, H.J. Thevik, L. Arnberg, and D.H. StJohn: Metall. Mater. Trans. B, 1999, vol. 30B, pp. 287–93.
I. Farup and A. Mo: Metall. Mater. Trans. A, 2000, vol. 31 A, pp. 1461–72.
L. Bäckerud: Solidification Characteristics of Aluminum Alloys Volume 1: Wrought Alloys, Skanaluminium, Oslo, Norway, 1986.
J. Pilling and A. Hellawell: Metall. Mater. Trans. A, 1996, vol. 27A, pp. 229–32.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Dahle, A.K., Sumitomo, T. & Instone, S. Relationship between tensile and shear strengths of the mushy zone in solidifying aluminum alloys. Metall Mater Trans A 34, 105–113 (2003). https://doi.org/10.1007/s11661-003-0212-z
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-003-0212-z