Abstract
The main emphasis of this study has been placed on understanding the effects of manganese and silicon additions and of heat-treatment (intercritical annealing and isothermal treatment) conditions on the microstructures and mechanical properties of 0.15 wt pct C transformation-induced plasticity (TRIP)-aided cold-rolled steel sheets. The steel sheets were intercritically annealed and isothermally treated at the bainitic region. Microstructural observation and tensile tests were conducted, and volume fractions of retained austenite were measured. Steels having a high manganese content had higher retained austenite fractions than the steels having a low manganese content, but showed characteristics of a dual-phase steel such as continuous yielding behavior, high tensile strength over 1000 MPa, and a low elongation of about 20 pct. The retained austenite fractions and mechanical properties varied with the heat-treatment conditions. In particular, the retained austenite fractions increased with decreasing intercritical annealing and isothermal treatment temperatures, thereby resulting in the improvement of the elongation and strength-ductility balance without a serious decrease in the yield or tensile strength. These findings suggested that the intercritical annealing and isothermal treatment conditions should be established in consideration of the stability of austenite and the solubility of alloying elements in the austenite formed during the intercritical annealing.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
K.I. Sugimoto, N. Ushi, M. Kobayashi, and S.I. Hashimoto: Iron Steel Inst. Jpn., 1992, vol. 32, p. 1311.
K.I. Sugimoto, N. Ushi, M. Kobayashi, and S.I. Hashimoto: Metall. Trans. A, 1992, vol. 23A, pp. 3085–91.
H.C. Chen, H. Era, and M. Shimizu: Metall. Trans. A, 1989, vol. 20A, pp. 4371–45.
S.K. Kim, H.C. Shin, J.H. Chung, and Y.W. Chang: J. Kor. Inst. Metall. Mater., 1998, vol. 36, p. 151.
C.G. Lee and S.J. Kim: J. Kor. Inst. Metall. Mater., 1998, vol. 36, p. 1024.
B.V.N. Rao and A.K. Sachdev: Metall. Trans. A, 1982, vol. 13A, pp. 1899–1906.
B.V.N. Rao and M.S. Rashid: Metallography, 1983, vol. 31, p. 19.
N.C. Goel, J.P. Chakravarty, and K. Tangri: Metall. Trans. A, 1987, vol. 18A, pp. 5–9.
W.C. Leslie and G.C. Rauch: Metall. Trans. A, 1978, vol. 9A, pp. 343–49.
J.H. Chung: Ph.D. Thesis, Pohang University of Science Technology, Pohang, 1994, p. 64.
O. Matsumura, Y. Sakuma, and H. Takechi: Iron Steel Inst. Jpn., 1987, vol. 27, p. 570.
C.G. Lee, S.J. Kim, S.G. Park, and I. Choi: J. Kor. Inst. Metall. Mater., 1998, vol. 36 p. 1382.
S.J. Kim and C.G. Lee: J. Kor. Inst. Metall. Mater., 1999, vol. 37, p. 774.
R.L. Miller: Trans. ASM, 1964, vol. 57, p. 892.
R.L. Miller: Trans. ASM, 1968, vol. 61, p. 592.
W.C. Leslie: The Physical Metallurgy of Steels, McGraw-Hill Press, New York, NY, 1981, p. 172.
A.D. Romig, Jr. and R. Salzbrenner: Scripta Metall., 1982, vol. 16, p. 33.
N. Pussegoda, W.R. Tyson, P. Wycliffe, and G.R. Purdy: Metall. Trans. A, 1984, vol. 15A, pp. 1499–1502.
B.V.N. Rao and M.S. Rashid: Metallography, 1983, vol. 13, p. 19.
J.M. Rigsbee and P.J. VanderArend: in Formable HSLA and Dual-Phase Steels, A.T. Davenport, ed., TMS-AIME, Warrendale, PA, 1979, p. 56.
H.K.D.H. Bhadeshia and D.V. Edmonds: Met. Sci., 1983, vol. 17, p. 411.
G.S. Ansell, P.J. Brofman, and G. Judd: Proc. Int. Conf. on Martensitic Transformations ICOMAT 1979’, MIT Press, Boston, MA, 1980, p. 350.
S.J. Kim, C.G. Lee, and S. Lee: J. Kor. Inst. Metall. Mater., 1997, vol. 35, p. 1278.
N.J. Kim and G. Thomas: Metall. Trans. A, 1981, vol. 12A, pp. 483–89.
G.E. Dieter: in Mechanical Metallurgy, S.I. Metric, ed., McGraw-Hill Press, New York, NY, 1988, p. 197.
Y. Sakuma, D.K. Matlock, and G. Krauss: Metall. Trans. A, 1992, vol. 23A, pp. 1233–41.
G. Thomas and J.Y. Koo: Structure and Properties of Dual-Phase Steels, R.A. Kot and J.W. Morris, eds., TMS-AIME, Warrendale, PA, 1979, p. 183.
I. Sawai, S. Uchida, and E. Kamisaka: Tetsu-to-Hagané, 1985, vol. 71, p. 1292.
H.K.D.H. Bhadeshia and D.V. Edmonds: Metall. Sci., 1983, vol. 17, p. 411.
B.P.J. Sandvik and H.P. Novalanien: Met. Technol., 1981, vol. 8, p. 213.
V.T.T. Mijhkinen and D.V. Edmonds: Mater. Sci. Technol., 1987, vol. 3, p. 422.
Binary Alloy Phase Diagrams, 2nd ed., T.B. Massalski, ed., ASM, Metals Park, OH, 1990, p. 1725.
K.W. Andrew: J. Iron Steel Inst., 1965, vol. 203, p. 721.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kim, SJ., Lee, C.G., Choi, I. et al. Effects of heat treatment and alloying elements on the microstructures and mechanical properties of 0.15 wt pct C transformation-induced plasticity-aided cold-rolled steel sheets. Metall Mater Trans A 32, 505–514 (2001). https://doi.org/10.1007/s11661-001-0067-0
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-001-0067-0