Abstract
In this study, microstructures of a heat-affected zone (HAZ) of an SA 508 steel were identified by Mossbauer spectroscopy in conjunction with microscopic observations, and were correlated with fracture toughness. Specimens with the peak temperature raised to 1350 °C showed mostly martensite. With the peak temperature raised to 900 °C, the martensite fraction was reduced, while bainite or martensite islands were formed because of the slow cooling from the lower austenite region and the increase in the prior austenite grain size. As the martensite fraction present inside the HAZ increased, hardness and strength tended to increase, whereas fracture toughness decreased. The microstructures were not changed much from the base metal because of the minor tempering effect when it was raised to 650 °C or 700 °C. However, fracture toughness of the subcritical HAZ with the peak temperature raised to 650 °C to 700 °C was seriously reduced after postweld heat treatment (PWHT) because carbide particles were of primary importance in initiating voids. Thus, the most important microstructural factors affecting fracture toughness were the martensite fraction before PWHT and the carbide fraction after PWHT.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
H.G. Pisarski and J. Kudoh: in Welding Metallurgy of Structural Steels, J.Y. Koo, ed., TMS, Denver, CO, 1987, pp. 263–75.
B.C. Kim, S. Lee, N.J. Kim, and D.Y. Lee: Metall. Trans. A, 1991, vol. 22A, pp. 139–49.
K. Uchino and Y. Ohno: Proc. 7th Int. Conf. on Offshore Mechanics and Arctic Engineering, Houston, TX, ASME, Golden, CO, 1988, pp. 159–65.
S. Lee, B.C. Kim, and D. Kwon: Metall. Trans. A, 1993, vol. 24A, pp. 1133–41.
D.P. Fairchild: in Welding Metallurgy of Structural Steels, J.Y. Koo, ed., TMS, Denver, CO, 1987, pp. 303–18.
S. Lee: Scripta Metall., 1988, vol. 22, pp. 59–64.
K. Easterling: Introduction to the Physical Metallurgy of Welding, Butterworth and Co., London, 1983, ch. 1.
G.R. Wang, T.W. Lau, G.C. Weatherly, and T.H. North: Metall. Trans. A, 1989, vol. 20A, pp. 2093–2100.
J.Y. Koo and A. Ozekcin: in Welding Metallurgy of Structural Steels, J.Y. Koo, ed., TMS, Denver, CO, 1987, pp. 119–35.
S. Lee, B.C. Kim, and D. Kwon: Metall. Trans. A, 1992, vol. 23A, pp. 2803–16.
T.D. Park, K.K. Baek, and D.S. Kim: Metall. Mater., 1997, vol. 3, pp. 46–50.
P.G. Debrunner and H. Frauenfelder: in An Introduction to Mossbauer Spectroscopy, L. May, ed., Plenum Press, New York, NY, 1971, pp. 155–76.
G.J. Long: in Mossbauer Spectroscopy Applied to Inorganic Chemistry, G.J. Long, ed., Plenum Press, New York, NY, 1984, pp. 7–25.
J.R. Genin: Metall. Trans. A, 1987, vol. 18A, pp. 1371–88.
H. Ino, T. Moriya, F.E. Fujita, Y. Maeda, Y. Ono, and Y. Inokuti: J. Phys. Soc. Jpn., 1968, vol. 25, pp. 88–99.
M. Ron and Z. Mathalone: Phys. Rev. B, 1971, vol. 4, pp. 774–77.
F. Aubertin, L. Abada, and U. Gonser: Hyp. Int., 1998, vol. 111, pp. 201–04.
M. Ron, H. Shechter, and S. Niedzwidz: J. Appl. Phys., 1968, vol. 39, pp. 265–75.
B. Fultz: in Mossbauer Spectroscopy Applied to Magnetism and Materials Science, G.J. Long and F. Grandjean, eds., Plenum Press, New York, NY, 1993, pp. 1–26.
D. Rosenthal: Trans. ASME, 1946, Nov., pp. 849–66.
J.H. Kim and E.P. Yoon: J. Kor. Inst. Met. Mater., 1998, vol. 36, pp. 1329–37.
K. Suzuki: in Neutron Irradiation Effects in Solids, M.A. Kirk, ed., NHC, Argonne, IL, 1981, pp. 443–50.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kim, S., Kang, S.Y., Lee, S. et al. Correlation of the microstructure and fracture toughness of the heat-affected zones of an SA 508 steel. Metall Mater Trans A 31, 1107–1119 (2000). https://doi.org/10.1007/s11661-000-0106-2
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-000-0106-2