Abstract
The solar energy utilization in built environment has been limited due to its low heat flux, uneven distribution in time and space and temporal difference in day and night. The phase change materials have been used to collect the fluctuant solar energy to form a stable energy source for the terminal equipment of the buildings. In this study, the hybrid organic phase change materials was prepared for the capillary radiant heating system which formed a cascade utilization of solar energy. Firstly, lauric acid and stearic acid were selected as the basic organic phase change materials and the binary equilibrium phase diagram was completed based on the method of step cooling curve according to the experimental tests data. The results showed that the phase transition temperature of the mixed acid at the lowest eutectic point was 31.2°C and the latent heat value was 264.3 kJ/kg when the mass mixing ratio was 70% for lauric acid and 30% for stearic acid. Secondly, the expanded graphite was used as an additive to enwrap the mixed acid and enhance the heat conductivity. The experimental results showed that when the mass proportion of expanded graphite in the mixed acid was 10%), the mixed acid could be completely enclosed by expanded graphite and the stability of melting and solidification was optimal. Additionally, the phase transition temperature of the hybrid phase change material was 31.5°C and the latent heat value was 217.4 kJ/kg. The novel hybrid phase change material has a lower eutectic point and a higher latent heat of phase change, so it has a large application space and is quite suitable for the cascade utilization of solar energy with capillary network heating system.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Yi J., Research report on annual development of China's building energy efficiency. China Architecture & Building Press, 2018. (in Chinese)
Xu W., Zheng R., Lu B., Research report on application development of solar energy in China. China Architecture & Building Press, 2009. (in Chinese)
Pomianowski M., Heiselberg P., Zhang Y.P., Review of thermal energy storage technologies based on PCM application in buildings. Energy and Buildings, 2013, 67: 56–69.
Sharma A., Tyagi V.V., Chen C.R., Buddhi D., Review on thermal energy storage with phase change materials and applications. Renewable & Sustainable Energy Reviews, 2009, 13(2): 318–345.
Mikeska T., Svendsen S., Dynamic behavior of radiant cooling system based on capillary tubes in walls made of high performance concrete. Energy and Buildings, 2015, 108: 92–100.
Zalba B., Marin J.M., Cabeza L.F., Mehling P.L., Review on thermal energy storage with phase change: materials, heat transfer analysis and applications. Applied Thermal Engineering, 2003, 23(3): 251–283.
Mao Q.J., Chen H.Z., Yang Y.Z., Energy storage performance of a PCM in the solar storage tank. Journal of Thermal Science, 2019, 28(2): 195–203.
Tan H.J., Pan C.Y., Yu D., et al., Preparation and analysis of a heat storage phase change composite material taking PNIPAM as carrier. Journal of Functional Materials, 2008, 39(12): 2015–2017+21. (in Chinese)
Saeed R.M., Schlegel J.P., Castano C., Sawafta R., Kuturu V., Preparation and thermal performance of methyl palmitate and lauric acid eutectic mixture as phase change material (PCM). Journal of Energy Storage, 2017, 13: 418–424.
Pielichowska K., Pielichowski K., Phase change materials for thermal energy storage. Progress in Materials Science, 2014, 65: 67–123.
San A., Karaipekli A., Thermal conductivity and latent heat thermal energy storage characteristics of paraffin/ expanded graphite composite as phase change material. Applied Thermal Engineering, 2007, 27(8): 1271–1277.
Liu C., Yuan Y., Zhang N., Cao X., Yang X., A novel PCM of lauric-myristic-stearic acid/expanded graphite composite for thermal energy storage. Materials Letters, 2014, 120: 43–46.
Chen C.Z., Wang L.G., Huang Y., A novel shape-stabilized PCM: Electrospun ultrafine fibers based on lauric acid/polyethylene terephthalate composite. Materials Letters, 2008, 62(20): 3515–3517.
Kong X.F., Zhong Y.L., Rong X., Min C.H., Qi C.Y., Building energy storage panel based on paraffin/expanded perlite: Preparation and thermal performance study. Materials, 2016, 9(2): 70. DOI: 10.3390/ma9020070.
Yao C.Q., Kong X.F., Li Y.T., Du Y.X., Qi C.Y., Numerical and experimental research of cold storage for a novel expanded perlite-based shape-stabilized phase change material wallboard used in building. Energy Conversion and Management, 2018, 155: 20–31.
Kong X.F., Yao C.Q., Jie P.R., Liu Y., Qi C.Y., Rong X., Development and thermal performance of an expanded perlite-based phase change material wallboard for passive cooling in building. Energy and Buildings, 2017, 152: 547–557.
San A., Kaygusuz K., Some fatty acids used for latent heat storage: thermal stability and corrosion of metals with respect to thermal cycling. Renewable Energy, 2003, 28(6): 939–948.
Su D., Jia Y., Alva G., Tang F., Fang G., Preparation and thermal properties of n-octadecane/stearic acid eutectic mixtures with hexagonal boron nitride as phase change materials for thermal energy storage. Energy and Buildings, 2016, 131: 35–41.
Wang Z.S., Yang L.S., Hu X.W., Luo X.L., Gu Z.L., Improvement and experimental study of the T-history method. Journal of Refrigeration (In Chinese), 2017, 38(6): 34–38+45. (in Chinese)
Li C.C., Zhang B., Xie B.S., Zhao X.B., Chen J., Chen Z.S., et al. Stearic acid/expanded graphite as a composite phase change thermal energy storage material for tankless solar water heater. Sustainable Cities and Society, 2019, 44: 458–464.
Ma G.X., Sun J.H., Zhang Y., Jing Y., Jia Y.Z., Preparation and thermal properties of stearic acid-benzamide eutectic mixture/expanded graphite composites as phase change materials for thermal energy storage. Powder Technology, 2019, 342: 131–140.
Zhang D., Chen M.Z., Wu S.P., Riara M., Wan J.M., Li Y.Y., Thermal and rheological performance of asphalt binders modified with expanded graphite/polyethylene glycol composite phase change material (EP-CPCM). Construction and Building Materials, 2019, 194: 83–91.
Acknowledgments
The work was supported by the Innovation Chain of Key Industries of Shaanxi Province under Grant (No.2018ZDCXL-GY-10-03), and the National Natural Science Foundation of China (No.51478386).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wang, Z., Li, R., Hu, J. et al. Experimental Study on Hybrid Organic Phase Change Materials Used for Solar Energy Storage. J. Therm. Sci. 29, 486–491 (2020). https://doi.org/10.1007/s11630-020-1224-3
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11630-020-1224-3