Abstract
Due to the high specific surface area of graphene, the effective incorporation of high-content graphene in metals is challenging. Here, aluminum composites with graphene nanoplatelet (GNP) content up to 5.0 vol% were prepared by spark plasma sintering (SPS) of blended powders with various ball milling regimes and subsequent hot extrusion. The effects of GNP distribution state on the properties of GNP/Al composite were investigated. 5.0 vol% GNPs were uniformly dispersed in aluminum matrix by high-speed ball milling (HSBM) process, but with damage GNPs due to the too high energy input. By contrast, the wellstructured and dispersed GNPs in aluminum powders were obtained via shift-speed ball milling (SSBM). The clear GNP-Al interface in extruded SSBM composite was attributed to well-structured GNPs. As a result, the yield strength (YS) and ultimate tensile strength (UTS) of composite produced by SSBM reached 279 and 303 MPa, which are 166% and 116% higher than those of monolithic Al. This demonstrated that it may be promising to introduce high-content GNPs with tailorable interface in Al alloys via modified ball milling technique and hot extrusion.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Dorri Moghadam A, Omrani E, Menezes P L, et al. Mechanical and tribological properties of self-lubricating metal matrix nanocomposites reinforced by carbon nanotubes (CNTs) and grapheme: A review. Compos Part B-Eng, 2015, 77: 402–420
Tsai J L, Tu J F. Characterizing mechanical properties of graphite using molecular dynamics simulation. Mater Des, 2010, 31: 194–199
King A, Johnson G, Engelberg D, et al. Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal. Science, 2008, 321: 382–385
Balandin A A, Ghosh S, Bao W, et al. Superior thermal conductivity of single-layer graphene. Nano Lett, 2008, 8: 902–907
Bolotin K I, Sikes K J, Jiang Z, et al. Ultrahigh electron mobility in suspended graphene. Solid State Commun, 2008, 146: 351–355
Pérez-Bustamante R, Bolaños-Morales D, Bonilla-Martínez J, et al. Microstructural and hardness behavior of graphene-nanoplatelets/aluminum composites synthesized by mechanical alloying. J Alloys Compd, 2014, 615: S578–S582
Li J L, Xiong Y C, Wang X D, et al. Microstructure and tensile properties of bulk nanostructured aluminum/graphene composites prepared via cryomilling. Mater Sci Eng-A, 2015, 626: 400–405
Li Z, Fan G, Guo Q, et al. Synergistic strengthening effect of graphene-carbon nanotube hybrid structure in aluminum matrix composites. Carbon, 2015, 95: 419–427
Shin S E, Bae D H. Deformation behavior of aluminum alloy matrix composites reinforced with few-layer graphene. Compos Part A-Appl Sci Manu, 2015, 78: 42–47
Rashad M, Pan F, Tang A, et al. Effect of Graphene nanoplatelets addition on mechanical properties of pure aluminum using a semi-powder method. Prog Nat Sci-Mater Int, 2014, 24: 101–108
Rashad M, Pan F, Yu Z, et al. Investigation on microstructural, mechanical and electrochemical properties of aluminum composites reinforced with graphene nanoplatelets. Prog Nat Sci-Mater Int, 2015, 25: 460–470
Bisht A, Srivastava M, Kumar R M, et al. Strengthening mechanism in graphene nanoplatelets reinforced aluminum composite fabricated through spark plasma sintering. Mater Sci Eng-A, 2017, 695: 20–28
Wang J, Li Z, Fan G, et al. Reinforcement with graphene nanosheets in aluminum matrix composites. Scripta Mater, 2012, 66: 594–597
Li Z, Guo Q, Li Z, et al. Enhanced mechanical properties of graphene (reduced graphene oxide)/aluminum composites with a bioinspired nanolaminated structure. Nano Lett, 2015, 15: 8077–8083
Liu G, Zhao N, Shi C, et al. In-situ synthesis of graphene decorated with nickel nanoparticles for fabricating reinforced 6061Al matrix composites. Mater Sci Eng-A, 2017, 699: 185–193
Yan S J, Dai S L, Zhang X Y, et al. Investigating aluminum alloy reinforced by graphene nanoflakes. Mater Sci Eng-A, 2014, 612: 440–444
Kwon H, Mondal J, AlOgab K A, et al. Graphene oxide-reinforced aluminum alloy matrix composite materials fabricated by powder metallurgy. J Alloys Compd, 2017, 698: 807–813
Bastwros M, Kim G Y, Zhu C, et al. Effect ofball milling on graphene reinforced Al6061 composite fabricated by semi-solid sintering. Compos Part B-Eng, 2014, 60: 111–118
Li J, Zhang X, Geng L. Improving graphene distribution and mechanical properties of GNP/Al composites by cold drawing. Mater Des, 2018, 144: 159–168
Shin S E, Choi H J, Shin J H, et al. Strengthening behavior of few-layered graphene/aluminum composites. Carbon, 2015, 82: 143–151
Czeppe T, Korznikova E, Ozga P, et al. Application of the high pressure torsion supported by mechanical alloying for the metal-graphene composites preparation. Mechanik, 2015, 147: 41–46
Shin S E, Ko Y J, Bae D H. Mechanical and thermal properties of nanocarbon-reinforced aluminum matrix composites at elevated temperatures. Compos Part B-Eng, 2016, 106: 66–73
Tabandeh-Khorshid M, Omrani E, Menezes P L, et al. Tribological performance of self-lubricating aluminum matrix nanocomposites: Role of graphene nanoplatelets. Eng Sci Tech Int J, 2016, 19: 463–469
Asgharzadeh H, Sedigh M. Synthesis and mechanical properties of Al matrix composites reinforced with few-layer graphene and graphene oxide. J Alloys Compd, 2017, 728: 47–62
Li G, Xiong B. Effects of graphene content on microstructures and tensile property of graphene-nanosheets/aluminum composites. J Alloys Compd, 2017, 697: 31–36
Pillari L K, Shukla A K, Murty S V S N, et al. On the comparison of graphene and multi-wall carbon nanotubes as reinforcements in aluminum alloy AA2219 processed by ball milling and spark plasma sintering. Trans Ind Inst Met, 2018, 71: 1099–1112
Hu Z, Chen F, Xu J, et al. 3D printing graphene-aluminum nanocomposites. J Alloys Compd, 2018, 746: 269–276
Yang W, Zhao Q, Xin L, et al. Microstructure and mechanical properties of graphene nanoplates reinforced pure Al matrix composites prepared by pressure infiltration method. J Alloys Compd, 2018, 732: 748–758
Zhang Z W, Liu Z Y, Xiao B L, et al. High efficiency dispersal and strengthening of graphene reinforced aluminum alloy composites fabricated by powder metallurgy combined with friction stir processing. Carbon, 2018, 135: 215–223
Li M, Gao H, Liang J, et al. Microstructure evolution and properties of graphene nanoplatelets reinforced aluminum matrix composites. Mater Charact, 2018, 140: 172–178
Bhadauria A, Singh L K, Laha T. Combined strengthening effect of nanocrystalline matrix and graphene nanoplatelet reinforcement on the mechanical properties of spark plasma sintered aluminum based nanocomposites. Mater Sci Eng-A, 2019, 749: 14–26
Li J, Zhang X, Geng L. Effect of heat treatment on interfacial bonding and strengthening efficiency of graphene in GNP/Al composites. Compos Part A-Appl Sci Manu, 2019, 121: 487–498
Li M, Zhang Z, Gao H, et al. Formation of multilayer interfaces and the load transfer in graphene nanoplatelets reinforced Al matrix composites. Mater Charact, 2020, 159: 110018
Zhan K, Wu Y, Li J, et al. Investigation on surface layer characteristics of shot peened graphene reinforced Al composite by X-ray diffraction method. Appl Surf Sci, 2018, 435: 1257–1264
Latief F H, SherifE S M. Effects ofsintering temperature and graphite addition on the mechanical properties of aluminum. J Ind Eng Chem, 2012, 18: 2129–2134
Jiang Y, Tan Z, Xu R, et al. Tailoring the structure and mechanical properties of graphene nanosheet/aluminum composites by flake powder metallurgy via shift-speed ball milling. Compos Part A-Appl Sci Manu, 2018, 111: 73–82
Huang C, Hu S, Chen K. Influence of rolling temperature on the interfaces and mechanical performance of graphene-reinforced aluminum-matrix composites. Int J Miner Metall Mater, 2019, 26: 752–759
Ferrari A C, Robertson J. Interpretation of Raman spectra of disordered and amorphous carbon. Phys Rev B, 2000, 61: 14095–14107
Jiang L, Li Z, Fan G, et al. The use of flake powder metallurgy to produce carbon nanotube (CNT)/aluminum composites with a homogenous CNT distribution. Carbon, 2012, 50: 1993–1998
Yan L, Tan Z, Ji G, et al. A quantitative method to characterize the Al4C3-formed interfacial reaction: The case study of MWCNT/Al composites. Mater Charact, 2016, 112: 213–218
Howeyze M, Arabi H, Eivani A R, et al. Strengthening of AA5052 aluminum alloy by equal channel angular pressing followed by softening at room temperature. Mater Sci Eng-A, 2018, 720: 160–168
Bartolucci S F, Paras J, Rafiee M A, et al. Graphene-aluminum nanocomposites. Mater Sci Eng-A, 2011, 528: 7933–7937
Wang J, Zhang X, Zhao N, et al. In situ synthesis of copper-modified graphene-reinforced aluminum nanocomposites with balanced strength and ductility. J Mater Sci, 2019, 54: 5498–5512
Gao X, Yue H, Guo E, et al. Preparation and tensile properties of homogeneously dispersed graphene reinforced aluminum matrix composites. Mater Des, 2016, 94: 54–60
Bhadauria A, Singh L K, Laha T. Effect of physio-chemically functionalized graphene nanoplatelet reinforcement on tensile properties of aluminum nanocomposite synthesized via spark plasma sintering. J Alloys Compd, 2018, 748: 783–793
Zhao M, Xiong D B, Tan Z, et al. Lateral size effect of graphene on mechanical properties ofaluminum matrix nanolaminated composites. Scripta Mater, 2017, 139: 44–48
Han T, Li J, Zhao N, et al. Microstructure and properties of copper coated graphene nanoplates reinforced Al matrix composites developed by low temperature ball milling. Carbon, 2020, 159: 311–323
Yue H, Yao L, Gao X, et al. Effect of ball-milling and graphene contents on the mechanical properties and fracture mechanisms of graphene nanosheets reinforced copper matrix composites. J Alloys Compd, 2017, 691: 755–762
Fu J, Wei C, Wang W, et al. Studies of structure and properties of graphene oxide prepared by ball milling. Mater Res Innova, 2015, 19: S1–S277
Rashad M, Pan F, Zhang J, et al. Use of high energy ball milling to study the role of graphene nanoplatelets and carbon nanotubes reinforced magnesium alloy. J Alloys Compd, 2015, 646: 223–232
Fadavi Boostani A, Yazdani S, Taherzadeh Mousavian R, et al. Strengthening mechanisms of graphene sheets in aluminium matrix nanocomposites. Mater Des, 2015, 88: 983–989
Author information
Authors and Affiliations
Corresponding author
Additional information
This work was supported by the National Key R&D Program of China (Grant No. 2017YFB0703103), and Guangdong Province Key Area R&D Program (Grant No. 2019B010942001).
Rights and permissions
About this article
Cite this article
Zheng, Z., Zhang, X., Li, J. et al. High-content graphene nanoplatelet reinforced aluminum composites produced by ball milling and hot extrusion. Sci. China Technol. Sci. 63, 1426–1435 (2020). https://doi.org/10.1007/s11431-020-1670-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11431-020-1670-4