Abstract
The main objective of this research was to study the potential of sodium silicate modification on moso bamboo particles as reinforcements for thermoplastic. Moso bamboo particles were modified with sodium silicate aqueous solutions (of 0.5%, 1%, 2%, 5% and 10% concentrations). The mechanical properties of sodium silicate treated moso bamboo particles reinforced PVC composites (BPPC) were calculated and compared with raw bamboo particles filled samples. The thermal characteristics of the BPPC were studied to investigate the feasibility of sodium silicate treatment on moso bamboo particles. The particle morphology and BPPC microstructure were investigated by scanning electron microscopy. Results showed that the tensile strength and modulus of elasticity of the BPPC increased before the concentration of sodium silicate solution reached 5% and got their maximum values of 15.72 MPa and 2956.80 MPa, respectively at 5% concentration. The modulus of rupture obtained the maximum value of 27.73 MPa at 2% concentration. The mechanical curve decreased as the concentration of solution went higher. Differential scanning calorimetric analysis illustrated that the sodium silicate solution treated BPPC possesses a better compatibility. More uniform dispersion of moso bamboo particles in PVC matrix was obtained after the sodium silicate treatment. Hence, the sodium silicate was a feasible and competitive agent of creating moso bamboo particles reinforced PVC composites.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Andy WC L, Chen G, Frank H T. Comparative treatability of moso bamboo and southern pine with CCA preservative using a commercial schedule. Bioresource Technol, 2001, 77(1): 87–88
Austin R, Ueda K. Bamboo. New York: John Weatherhill, Inc. 1970. 215
Thwe M M, Liao K. Effects of environmental aging on the mechanical properties of bamboo-glass fiber reinforced polymer matrix hybrid composites. Compos Part A-Appl S, 2002, 33(1): 43–52
Rao H R, Rajulu A V, Reddy G R, et al. Flexural and compressive properties of bamboo and glass fiber-reinforced epoxy hybrid composites. J Reinf Plast Comp, 2010, 29(10): 1446–1450
Lee S Y, Chun S J, Doh G H, et al. Influence of chemical modification and filler loading on fundamental properties of bamboo fibers reinforced polypropylene composites. J Compos Mater, 2009, 43(15): 1639–1657
Kushwaha P K, Kumar R. Effect of silanes on mechanical properties of bamboo fiber-epoxy composites. J Reinf Plast Comp, 2010, 29(5): 718–724
Krishnaprasad R, Veena N R, Maria H J, et al. Mechanical and thermal properties of bamboo microfibril reinforced polyhydroxybutyrate biocomposites. J Polym Environ, 2009, 17(2): 109–114
Maldas D, Kokta B V. Role of coupling agents on the performance of woodflourfilled polypropylene composites. Int J Polym Mater, 1994, 27: 77–88
Beckermann G W, Pickering K L. Engineering and evaluation of hemp fibre reinforced polypropylene composites: Fibre treatment and matrix modification. Compos Part A-Appl S, 2008 (39): 979–988
Nayak S K, Mohanty S, Samal S K. Hybridization effect of glass fibre on mechanical, morphological and thermal properties of polypropylene-bamboo/glass fibre hybrid composites. Polym Polym Compos, 2010, 18(4): 205–218
Liu H, Wu Q, Han G, et al. Compatibilizing and toughening bamboo flour-filled HDPE composites: Mechanical properties and morphologies. Compos Part A-Appl S, 2008, 39(12): 1891–1900
Kushwaha P K, Kumar R. Studies on water absorption of bamboo-epoxy composites: effect of silane treatment of mercerized bamboo. J Appl Polym S, 2010, 115(3): 1846–1852
Samal S K, Mohanty S, Nayak S K. Polypropylene-bamboo/glass fiber hybrid composites: fabrication and analysis of mechanical, morphological, thermal, and dynamic mechanical behavior. J Reinf Plast Comp, 2009, 28(22): 2729–2747
Kushwaha P K, Kumar R. Enhanced mechanical strength and water resistant of BFRP composites using modified bamboo fibers. Recent Adv Text Compos, 2008: 463–470
Wang H M, Postle R, Kessler R W, et al. Removing pectin and lignin during chemical processing of hemp for textile applications. Text Res J, 2003, 73(8): 664–672
Wang H, Lan T, Sheng K C, et al. Role of alkali treatment on mechanical and thermal properties of bamboo particles reinforced polyvinylchloride composites. Adv Mater Res, 2009, 79–82: 545–548
Wang H, Chang R, Sheng K C, Adl M, Qian X Q. Impact response of bamboo-plastic composites with the properties of bamboo and polyvinylchloride (PVC). J Bionic Eng, 2008, 5(sppl): 28–33
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Wang, H., Sheng, K., Chen, J. et al. Mechanical and thermal properties of sodium silicate treated moso bamboo particles reinforced PVC composites. Sci. China Technol. Sci. 53, 2932–2935 (2010). https://doi.org/10.1007/s11431-010-4123-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11431-010-4123-0