Abstract
A cyclic voltammetry method is used to show that the process of reduction of sodium (and, possibly, lithium) out of melts of corresponding chlorides on the molybdenum, glassy-carbon, and graphite electrodes is complicated by the process of dissolution of the corresponding alkali metal in the melt. A notion called “reversibility of material balance” is introduced. The notion reflects the ratio of the amount of substance that undergoes oxidation in the anodic half-cycle of a voltammetric curve to the amount of substance that is deposited in the cathodic half-cycle of the curve. The adsorption of sodium and lithium on glassy carbon and graphite plays an important role in the process of reduction, leading to an increase in the reversibility of the process. This is pronounced especially strongly at potential scan rates below 1 V s−1. The sodium intercalation into graphite leads to a decrease in the reversibility of the process of reduction, the more so at potential scan rates below 0.03 V s−1. However, the intercalation of lithium (probably because of its small atomic radius) does not exert practically any influence on the reversibility of process at the above potential scan rates.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
REFERENCES
Iijima, S., Nature (London), 1991, vol. 354, p. 56.
Hsu, W.K., Hare, J.P., Terrones, M., Kroto, H.W., Walton, D.R.M., and Harris, P.J.F., Nature (London), 1995, vol. 377, p. 687.
Hsu, W.K., Terrones, M., Hare, J.P., Terrones, H., Kroto, H.W., and Walton, D.R.M., Chem. Phys. Lett., 1996, vol. 262, p. 161.
Chen, G.Z., Fan, X., Luget, A., Shaffer, M.S.P., Fray, D.J., and Windle, A.H., J. Electroanal. Chem., 1998, vol. 446, p. 1.
Chen, G.Z, Kinloch, I., Shaffer, M.S.P., Fray, D.J., and Windle, A.H., in Advances in Molten Salts: From Structural Aspects to Waste Processing, Gaune-Escard, M., Ed., Begel House, 1999, p. 97.
Fray, D.J., in Advances in Molten Salts: From Structural Aspects to Waste Processing, Gaune-Escard, M., Ed., Begel House, 1999, p. 196.
Xu, Q., Schwandt, C., Chen, G.Z., and Fray, D.J., J. Electroanal. Chem., 2002, vol. 530, p. 16.
Chen, G.Z. and Fray, D.J., J. Min. Met., 2003, vol. 39, p. 309.
Bai, J.B., Hamon, A.-L., Marraud, A., Jouffrey, B., and Zymla, V., Chem. Phys. Lett., 2002, vol. 365, p. 184.
Kaptay, G., Sytchev, J., Miklosi, J., Nagy, P., Poczik, P., Papp, K., and Kalman, E., in Progress in Molten Salt Chemistry, Berg, R.W. and Hjuler, H.A., Eds., Amsterdam: Elsevier, 2000, p. 257.
Kaptay, G., Sytchev, I., Yaghmaee, M.S., Kovacs, A., Cserta, E., and Ark, M., 6th Int. Symp. on Molten Salt Chemistry and Technology, Nianyi, C. and Zhiyu, Q., Eds., Shanghai: Shanghai Univ., 2001, p. 168.
Yaghmaee, M.S., Demeter, Z., Sytchev, J., Lakatos, J., and Kaptay, G., J. Min. Met, 2003, vol. 39, p. 343.
Borisenko, N., Sytchev, J., and Kaptay, G., J. Min. Met, 2003, vol. 39, p. 369.
Smirnov, M.V., Chebykin, V.V., and Tsiovkina, L.A., Electrochim. Acta, 1981, vol. 26, p. 1275.
Author information
Authors and Affiliations
Corresponding author
Additional information
__________
Translated from Elektrokhimiya, Vol. 41, No. 9, 2005, pp. 1079–1086.
Original Russian Text Copyright © 2005 by Sychev, Borisenko, Kaptay, Kushkhov.
Rights and permissions
About this article
Cite this article
Sychev, J., Borisenko, N.V., Kaptay, G. et al. Intercalation of Sodium and Lithium into Graphite as a First Stage in an Electrochemical Method for Producing Carbon Nanotubes. Russ J Electrochem 41, 956–963 (2005). https://doi.org/10.1007/s11175-005-0163-3
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11175-005-0163-3