The scope is considered for increasing the high-temperature stability to deformation in ceramic items as regards comprehensive improvement in characteristics corresponding to current economic trends.
Article PDF
Avoid common mistakes on your manuscript.
References
M. Miura, T. Shimadzu, H. Shin, et al., “Evaluation of softening deformation behavior in porcelain bodies during firing,” Ceram. Eng. Sci. Proc., 20, No. 2, 99–111 (1999).
Zh. V. Kolpashchikova, E. V. Shcherbakova, and N. S. Kostyukov, “Polarization processes in electrotechnical porcelain over a wide frequency range,” Steklo i Keramika, No. 11, 19–21 (2003).
N. K. Mitra, A. Basumajumdar, S. K. Das, Sudip Saha, et al., “Development of zirconia porcelain in presence of active silica and its characterization,” J. Indian Chem. Soc., 81, No. 6, 531–533 (2004).
S. S. Ordan’yan, O. S. Gerasimova, and N. A. Andreeva, “Aspects of component interaction in a porcelain material containing feldspar liquid,” Ogneupory i Tekhnicheskaya Keramika, No. 2, 2–7 (2004).
S. M. Olhero, G. Tari, and J. M. F. Ferreira, “Feedstock formulations for direct consolidation of porcelains with polysaccharides,” J. Amer. Ceram. Soc., 84, No. 4, 719 (2001).
N. A. Andreeva and S. S. Ordan’yan, “Scope for improving the physicomechanical properties of electrical porcelain,” in: Proceedings of the 3rd International Conference on Electrical Insulators 2002 [in Russian], Nestor, St. Petersburg (2002), pp. 109–110.
N. A. Andreeva, “Some technological possibilities for improving the properties of porcelain,” in: Proceedings of the 2nd All-Russia Conference on Chemistry and Chemical Engineering at the Start of the Third Millennium [in Russian], TPU, Tomsk (2002), pp. 3–5.
Y. Kobayashi, O Ohira, T. Satoh, et al., “Effect of quartz on the sintering and bending strength of the porcelain bodies in quartz-feldspar-kaolin system,” J. Ceram. Soc. Japan, 102, No. 1181, 99–104 (1994).
Y. Kobayashi, O. Ohira, and H. Isoyama, “Effect of particle size of raw materials on densification and bending strength of porcelain,” J. Ceram. Soc. Jap., 108, No. 1262, 921–925 (2001).
L. P. Kachalova, Determination of the Optimum Granulometric Composition of Porcelain Bodies: Proc. 9th Conf. Silicate Ind. (SiliConf), Budapest, 1967, Budapest (1968), pp. 355–360.
V. P. Il’ina, “Effects of feldspar raw material grain size on the physicomechanical properties of low-temperature porcelain,” in: Abstracts for the 4th All-Russia Conference on Physicochemical Problems of Creating New Constructional Ceramic Materials: Raw Materials, Synthesis, and Properties [in Russian], Komi Scientific Center, Urals Division of the RAS, Syktyvkar (2001), pp. 183–185.
A. P. Pyzhova, V. V. Korobkina, and V. S. Kosov, Defects in Fine-Grained Ceramic Items: Causes and Methods of Elimination [in Russian], Legprombytizdat, Moscow (1993).
P. P. Budnikov, A. A. Varuzhanyan, M. P. Volarovich, et al., “A study of the effects of a water vapor medium on the viscosity changes in clays on heating,” Zh. Prikl. Khim., No. 39, 2111–2114 (1966).
E. I. Evtushenko, I. Yu. Moreva, V. I. Bedina, et al., “Porcelain-faience items based on two-component bonding agents,” in: Proceedings of the 2nd Conference on Scientists, Instructors, Leading Experts, and Young Researchers on Ceramics and Refractories: Promising Decisions and Nanotechnology [in Russian], BGTU, Belgorod (2009), pp. 246–249.
V. A. Lotov, “Monitoring structure formation in the technology of ceramic and silicate materials,” Steklo i Keramika, No. 5, 21–25 (1999).
P. Boch, J. Boisson, and D. Vandermarcq, “Development of bodies and techniques enabling a decrease of the deformations occurring in porcelain bodies during shaping and firing,” Bull. Soc. Fr. Ceram., No. 121, 3–16 (1978).
A. I. Zakharov, “Ceramic homogeneity: Connection with the method of forming and geometrical characteristics,” Steklo i Keramika, No. 9, 35–38 (2003).
A. I. Zakharov and I. A. Karnaushchenko, “Capillary impregnation in research on the homogeneity of the surfaces of ceramic semifinished products and items,” Steklo i Keramika, No. 10, 37–40 (2008).
I. Štubòa, A. Lintnerová, and L. Vozár, “Anisotropic mechanical properties of textured quartz porcelain,” Ceramics-Silikaty, 52, No. 2, 90–94 (2008).
P. P. Budnikov and Kh. O. Gevorkyan, Firing Porcelain [in Russian], Stroiizdat, Moscow (1972).
J. J. Restrepo and D. R. Dinger, “Monitoring of pyroplastic deformation of triaxial porcelain bodies using dilatometric analysis,” Ceram. Ind. (Saõ Paulo, Brazil), 8, No. 4, 37–48 (2003).
S. Kr. Das and K. Dana, “Differences in densification behaviour of K- and Na-feldspar-containing porcelain bodies,” Thermochim. Acta, No. 406, 199–206 (2003).
S. R. Braganca and C. P. Bergmann, “A view of whitewares mechanical strength and microstructure,” Ceram. Int., 29, No. 7, 801–806 (2003).
I. A. Levitskii and Yu. A. Klimosh, “Structure formation in a sintering ceramic for domestic purposes,” Steklo i Keramika, No. 6, 32–36 (2005).
G. P. Sedmale, I. E. Shperberga, and U. Ya. Sedmalis, “Formation of mullite from compositions of hydromica clay with aluminum oxide,” Steklo i Keramika, No. 2, 16–18 (2004).
G. P. Sedmale, I. E. Shperberga, and U. Ya. Sedmalis, “A high-temperature ceramic based on modified illite clays,” Ogneupory i Tekhnicheskaya Keramika, No. 4, 9–12 (2004).
K. Dana and S. Kumar Das, “Evolution of microstructure in flyash-containing porcelain body on heating at different temperatures,” Bull. Mater. Sci., 27, No. 2, 183–188 (2004).
Y. Kobayashi, O. Ohira, and H. Isoyama, Nippon seramikkusu Kyokai Gakujutsu Ronbunshi (J. Ceram. Soc. Jap.) 111, No. 1290, 122–125 (2003).
W.-P. Tai, K. Kimura, H. Tateyama, et al., “Fabrication of new porcelain bodies in the system of glass microspheres-quartzaluminous cement,” J. Ceram. Soc. Jap., 107, No. 1241, 8–14 (1999).
J. Liebermann andW. Shulle, “Bauxite porcelain: Anew refractory material for producing high-voltage insulators,” [in Polish] Szklo i Ceram., 54, No. 4, 25–29 (2003).
F. Porte, R. Brydson, B. Rand, et al., “Creep viscosity of vitreous china,” J. Am. Ceram. Soc., 87, No. 5, 923–928 (2004).
S. Lyng, “Über die Glasphase in Porzellan,” Ber. Dtsch. Keram. Ges., 46, No. 5, 260–261 (1969).
F. Srbek and I. Galkina, “Plastic deformation of porcelain materials with high content of alumina at high temperatures,” Silikaty (Prague), 18, No. 2, 155–172 (1974).
A. Awgustinik and I. T. Sinznowa, “Making high-strength porcelain,” Silikattechnik, 19, No. 4, 111–114 (1968).
V. B. Kulish, “Effect of a temperature field on the deformation of flat china pieces,” Steklo i Keramika, No. 11, 21–22 (1980).
O. N. Kanygina, A. G. Chetverikova, A. A. Skripnikov, et al., “Effects of heating rate on the physicomechanical properties of silica ceramic,” Steklo i Keramika, No. 6, 17–19 (1999).
E. Blond, N. Schmitt, F. Hild, et al., “Microstructural variation in porcelain stoneware as function of flux system,” J. Amer. Ceram. Soc., 87, No. 10, 1959–1966 (2004).
Y. Kobayashi and E. Kato, “Low-temperature sintering of porcelain in CaO–Al2O3–SiO2 system,” J. Ceram. Soc. Jap., 108, No. 1255, 271–276 (2000).
C. Zografou, “Die Gefugeausbildung von Hartporzellan bei der Anwendung von Mineralisatoren,” Tonind. Ztg., 92, No. 1–2, 478–479 (1968).
G. N. Maslennikova and T. V. Stoikova, “Domestic-use porcelain with added mineralizers,” Steklo i Keramika, No. 7, 20–21 (2001).
A. V. Abdrakhimov, “Effects of iron-bearing man-made raw material on the viscosity of ceramic materials,” Ogneupory i Tekhnicheskaya Keramika, No. 2, 48–50 (2006).
E. S. Abdrakhimova, “Phase transformations on firing clay materials with various chemical and mineral compositions,” Ogneupory i Tekhnicheskaya Keramika, No. 2, 21–29 (2006).
T. Wiedmann, “Hochilestporzellane. Teil IV,” Sprechsaal Keram., Glas, Emaill, Silik, 101, No. 11, 439–440, 442, 446; No. 14, 591–596; No. 15, 631–635; No. 17, 767–772; No. 18, 774, 776 (1968).
Author information
Authors and Affiliations
Additional information
Translated from Novye Ogneupory, No. 8, pp. 45–52, August, 2009.
Rights and permissions
About this article
Cite this article
Andreev, D.V., Zakharov, A.I. Ceramic item deformation during firing: effects of composition and microstructure (review). Refract Ind Ceram 50, 298–303 (2009). https://doi.org/10.1007/s11148-009-9191-y
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11148-009-9191-y