Isothermal and thermokinetic martensitic transformations in low-carbon martensitic steels have been studied. Amodel is proposed that relates the mechanical state of the austenite, as dependent on the parameters of thermal treatment and the law of the grain size distribution, to the volume fraction of transformed martensite. Physical constants of the transformation are determined.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
According to notions of the martensitic transformation, which have been developed by the middle of the 20th century, the main features of this phenomenon are the existence of a critical cooling rate, lack of dependence of the transformation start temperature (M s) on the cooling rate (v cool) varied in a broad range (for the same steel composition), relationship between the volume fraction of martensite and the cooling rate, weak influence of the exposure duration on the amount of retained austenite, instantaneous growth of steel grains, and absence of changes in the phase composition. However, already at the end of 1950 – 1960s, new data appeared that proved the possibility of isothermal martensitic transformation at low temperatures. It was shown that the martensitic transformation should be considered as a usual phase transition in a single-component system [1, 2].
At present, some issues are still not completely clear, including the mechanisms of nucleation of the martensite phase [3], martensite crystal geometry and morphology [4,5,6,7,8,9,10,11,12,13,14], and possibility of predicting the martensite formation kinetics [15,16,17]. The transformation kinetics can be described using equations of the Avrami type [18, 19] derived assuming validity of the first-order reaction kinetics, according to which the elementary event involves only one particle (molecule, atom, ion). An alternative approach is based on the transformation kinetics described assuming a functional relationship between T 0 (temperature of thermodynamic equilibrium of the austenite – martensite transformation) or M s (martensite start temperature) and T tr (transformation temperature) [20-22].
The present work was aimed at studying and modeling the thermokinetic and isothermal martensitic transformations in low-carbon steels of the martensite class.
Methods of Study
The experiments were performed with low-carbon martensitic steel (LMS) grades 07Kh3GNM and 15Kh2G2NMF with lath martensite structure obtained upon austenitizing and cooling in air (austenitization temperature, 950°C), the elemental compositions of which are given in Table 1. The microstructure of steel specimens was studied by optical and electron microscopy, magnetometry, and dilatometry techniques. The extent of shear-induced γ → α transformation was estimated isometrically in 240 – 500°C temperature interval. The true size of austenite grains was determined by the intercept method [23].
The microstructure of specimens was analyzed using a Neophot-32 microscope at × 100 – 400 magnification and FEI Quanta 200 (Philips) scanning electron microscope. The amount of martensite formed during isothermal exposure and on cooling was determined by magnetometry on a modified Akulov type anisometer with automatically controlled experimental parameters.
Results and Discussion
The initial structures of LMS grades studied, as obtained upon quenching in air from rolling temperatures, are presented in Fig. 1 a and b. According to electron-microscopic data for 07Kh3GNM and 15Kh2G2NMFB steels, the most probable grain sizes were 26 and 6.5 μm and the corresponding lath widths were h ~ 460 and 300 nm, respectively.
Taking into account the right-hand asymmetry of the observed austenite grain size distributions (Fig. 2) and the results of previous investigations, it was suggested that these distributions obey a lognormal law [23]. The hypothesis of lognormal distribution of austenite grain sizes was checked according to the Pearson criterion (χ2) [24] at p = 0.05 confidence level (Table 2). Previously, the lognormal size distribution of LMS structure constituents was confirmed in [25, 26].
The most important factor determining the transformation kinetics is the particle (grain) size [22, 27]. The steel structure in specimens upon isothermal exposures represents lath martensite (Fig. 1 c and d), the distinctive features of which are small values of the lath width and misorientation angle and different directions of carbide axes [28].
Martensite formation takes place provided that the difference of free energies (ΔG) of the austenite–martensite transformation becomes equal to the temperature-dependent specific work of conversion [22]. The free energy of martensitic transformation can be calculated as a product of the austenite yield stress and specific coefficient of the mechanical equivalent of heat, according to which [22]
where σ0.2T is the austenite yield stress (with allowance for the phase hardening [22]) at cooling temperature T < T 0; T 0 is the temperature of thermodynamic equilibrium of the austenite–martensite transformation; and b = 1.3 – 1.4 (for steels with Mo and W) and b = 1 (in the absence of these elements). The values of constant coefficient b were determined for lath martensite formation in LMS under conditions of continuous cooling [22]. In this work, it was assumed that these steels admit the dependence of b on the chemical composition. Each particular steel grade was characterized by its own value of this constant, which was the same for all temperatures of isothermal exposure.
As is known [3, 17, 22], growth of the grain size is accompanied by increase in the martensite start temperature and decrease in the austenite yield stress, which is also valid for LNSs [29]. The values of yield stress σ0.2T and grain size d in a broad range (from meso- to nanoscale) obey the Hall–Petch relationship [30] where σ0.2T is the stress characterizing resistance to the propagation of dislocations in the grain body [30] and k is the coefficient describing hindered slip transfer through the grain boundary [30]. Grains of various sizes contribute differently to the austenite yield stress: large grains produce lower hardening than smaller ones. Therefore, it is necessary to take into account the influence of grain size distribution.
The characteristic stress σ0 consists of the temperature-dependent (\( {\sigma}_0^{\ast \ast } \)) and temperature-independent (\( {\sigma}_0^{\ast } \)) parts [31]:
The temperature-independent component \( {\sigma}_0^{\ast } \) is related with resistance to the motion of dislocations from disordered solute atoms, disperse precipitates, and lattice defects.
The austenite yield stress at transformation temperatures close to zero was estimated from data on the temperature dependence of σ0.2 [32] by interpolating it to 0 K. The corresponding σ0.2 value for the austenite grain size within 40 – 50 μm was about 510 MPa. The value of coefficient k in formula (2), which characterizes the resistance of grain boundaries, is independent of the temperature [33] and amounts to k = 0.46 MPa·m1/2 for austenitic steels [27].
The temperature-dependent component c (related to the Peierls–Nabarro stress) obeys according to N. J. Petch data [31] the following relation:
where α and β are constant coefficients. For austenite at room temperature, \( {\sigma}_0^{\ast }=2\cdot {10}^{-4}G \) and amounts to about 38 MPa. As the temperature is reduced to nearly 0 K, the \( {\sigma}_0^{\ast \ast } \) value exhibits more than tenfold growth [31] and reaches a level of about 380 MPa. Then, by jointly solving Eqs. (2) and (3), one can estimate the temperature-independent component as \( {\sigma}_0^{\ast } \) at about 60 MPa.
The minimum size d i of austenite grain capable of transforming into martensite at a given temperature T is found by jointly solving Eqs. (1) and (2):
Then, the resulting volume fraction f m of martensite can be determined by substituting formula (5) into the grain size distribution function expressed by formula (6) below. In all cases, the lognormal distribution law was found to be valid. It was assumed that the transformation of austenite begins with largest grains and ends by the austenite–martensite transformation in finest grains. The volume fraction of martensite corresponding to the distribution of grain sizes is expressed as
where μ and s are parameters of the lognormal distribution function. The use of error function erfc = 1 – erf is related to the aforementioned fact that the transformation begins in largest grains and terminates in small ones (Table 3).
The values of constants α and β calculated by least squares are presented in Table 3. A decrease in the temperature of thermodynamic equilibrium with increasing content of carbon is consistent with published results [22].
Parameters of the grain size distribution according to Eq. (6) were used to construct the temperature dependence of the maximum fraction of transformed austenite during continuous cooling (Fig. 3). Thus, the kinetics of supercooled austenite transformation in LMSs on continuous cooling strongly depends on the grain size distribution.
In order to describe the kinetics of isothermal transformation, it is necessary to study the volume fraction of martensite as function of the duration of exposure. The fraction of transformed austenite determines the yield stress of a steel with the given grain size. During the isothermal exposure, the strength of austenite decreases due to stress relaxation, which allows the transformation volume to grow. However, another factor to be taken into account is the hardening of austenite, which suppresses its transformation. Since this hardening linearly depends on the transformed volume and proceeds in a narrow interval, variation of the mechanical state of γ-phase was described by the following relation [34]:
where \( {\sigma}_{0.2T}^{\tau } \) is the yield stress upon exposure at temperature T for time τ, p is a constant coefficient, and τ0 is the time to stabilization of the transformation at temperature T (0 > τ).
Kinetic curves of the isothermal transformation of supercooled austenite presented in Figs. 4 and 5 were obtained by calculations in which \( {\sigma}_{0.2T}^{\tau } \) was replaced by \( {\sigma}_{0.2T}^{\tau } \). The calculated values of the volume fraction of transformed austenite did not deviate from experimental data by more than 15%.
Conclusions
-
1.
It is established that the distribution of austenite grain sizes is the main factor that determined the volume of martensitic transformation of low-carbon austenite in LMSs.
-
2.
A model is proposed that relates the mechanical state of low-carbon austenite with lognormal law of austenite grain size distribution to the thermodynamic and kinetic parameters of martensitic transformation. This model allows the volume fraction of lath martensite formed during continuous cooling of LMSs under isothermal conditions to be predicted.
References
G. V. Kurdyumov and B. Ya. Lyubov, Kinetic Theory of Phase Transformations [in Russian], Metallurgiya, Moscow (1966), 264 p.
Ya. S. Umanskii, B. N. Finkel’shtein, M. E. Blanter, et al., Physical Principles of Metallography [in Russian], GONTI, Moscow (1955), 724 p.
M. P. Kashchenko and V. G. Chashchina, Dynamic Theory of γ – α Martensitic Transformation in Iron Alloys and Solution of the Problem of Critical Grain Size [in Russian], Regular and Chaotic Dynamics Research Center – Izhevsk Institute of Computer Investigations, Moscow – Izhevsk (2010), 132 p.
V. I. Izotov, “Morphology and crystal geometry of lath (massive) martensite,” Fiz. Met. Metalloved., 34(1), 123 – 132 (1972).
V. M. Schastlivtsev, L. B. Blind, D. P. Rodionov, and I. L. Yakovleva, “Lath martensite structure in structural steels,” Fiz. Met. Metalloved., 66(4), 759 – 769 (1988).
Yu. G. Andreev, L. N. Devchenko, E. I. Zarkova, and M. A. Shtremel’, “Crystal geometry of martensitic shift in a large lath,” Fiz. Met. Metalloved., 56(4), 783 – 790 (1983).
M. A. Shtremel’, Yu. G. Andreev, and D. A. Kozlov, “Lath martensite structure and strength,” Metalloved. Term. Obrab. Met., No. 4, 10 – 15 (1999).
V. M. Schastlivtsev, “Martensite structure peculiarities in structural steels,” Fiz. Met. Metalloved., 33(2), 326 – 334 (1972).
L. V. Karabasova, M. N. Spasskii, and M. A. Shtremel’, ”Hierarchy of low-carbon martensite structures,” Fiz. Met. Metalloved., 37(6), 1238 – 1248 (1974).
A. F. Edneral, V. I. Izotov, L. M. Kleiner, et al., ”Low-carbon martensitic steels,” in: Problems of Metal Science and Physical Metallography [in Russian], Metallurgiya, Moscow (1972), pp. 123 – 134.
L. M. Kleiner, A. A. Shatsov, D. M. Larinin, and M. G. Zakirova, ”Low-carbon martensite structure and structural strength of martensitic steels,” Perspekt. Mater., No. 1, 59 – 67 (2011).
Yu. F. Titovets, N. Yu. Zolotarevskii, A. N. Samoilov, et al., “Modeling the influence of austenite grain size change on the kinetics of γ → α transformation,” Metalloved. Term. Obrab. Met., No. 2, 29 – 36 (2010).
M. Umemoto, E. Yoshitake, and I. Taniura, “The morphology of martensite in Fe – C, Fe – Ni – C, and Fe – Cr – C alloys,” J. Mater. Sci., 18(10), 2893 – 2904 (1983).
D. A. Mirzaev and K. Yu. Okishev, “Kinetic theory of lath martensite formation,” Vestn. Yuzh. Ural. Gos. Univ., No. 21, 9 – 14 (2007).
D. A. Mirzaev, K. Yu. Okishev, V. M. Schastlivtsev, and I. L. Yakovleva, “Kinetics of bainite and lath martensite formation: I. Effect of lath structure,” Fiz. Met. Metalloved., 90(5), 55 – 65 (2000).
D. A. Mirzaev, K. Yu. Okishev, V. M. Schastlivtsev, and I. L. Yakovleva, “Kinetics of bainite and lath martensite formation: II. Effect of incomplete transformation,” Fiz. Met. Metalloved., 90(5), 66 – 74 (2000).
V. A. Lobodyuk and E. I. Éstrin, Martensitic Transformations [in Russian], Fizmatlit, Moscow (2009), 352 p.
D. A. Mirzaev and K. Yu. Okishev, “Lath martensite formation in iron–nickel steels,” Metalloved. Term. Obrab. Met., No. 9, 7 – 14 (2014).
Donghwi Kim, Seok-Jae Lee, and Bruno C. de Cooman, “Microstructure of low-C steel isothermally transformed in the M s to M f temperature range,” Metall. Mater. Trans. A, 43, 4967 – 4983 (2012).
T. Y. Hsu (Xu Zuyao), “Carbon diffusion and kinetics during the lath martensite formation,” J. Phys. IV France, 5, C8-351 – C8-354 (1995).
P. O. Bykova, L. M. Kleiner, A. A. Shatsov, and D. M. Larinin, “Modeling isothermal transformation of low-carbon austenite,” Meterialovedenie, No. 5, 10 – 14 (2013).
M. E. Blanter, Theory of Heat Treatment [in Russian], Metallurgiya, Moscow (1984), 328 p.
S. A. Saltykov, Stereometric Metallography [in Russian], Metallurgiya, Moscow (1976), 272 p.
S. L. Alhnazarova and V. V. Kafarov, Methods of Experiment Organization in Chemical Technology [in Russian], Vysshaya Shkola, Moscow (1985), 319 p.
I. V. Ryaposov, L. M. Kleiner, A. A. Shatsov, and E. A. Noskova, “Grain and lath martensite structure formation by thermal cycling in low-carbon martensitic steels,” Metalloved. Term. Obrab. Met., No. 9, 33 – 39 (2008).
I. V. Ryaposov, L. M. Kleiner, and A. A. Shatsov, “Volume nanostructurization of low-carbon martensitic steels by heat treatment,” Metalloved. Term. Obrab. Met., No. 9, 9 – 14 (2012).
J. Christian, The Theory of Transformations in Metals and Alloys, Part I: Equilibrium and General Kinetic Theory, Pergamon Press, Oxford (1978).
H. K. Bhadeshia, Bainite in Steels, Cambridge University Press, London (2001), 454 p.
L. M. Kleiner, D. M. Larinin, L. V. Spivak, and A. A. Shatsov, “Phase and structure transformations in low-carbon martensitic steels,” Fiz. Met. Metalloved., 108(2), 161 – 168 (2009).
D. L. Merson (ed.), Advanced Materials: Structure and Methods of Investigation (Learning Aid) [in Russian], TGU – MISiS, Togliatti – Moscow (2006), 536 p.
N. J. Petch, in: Proc. Int. Conf. on Atomic Mechanisms of Fracture (April 12 – 16, 1959, Swampscott, MA, United States).
V. N. Arzamasov, V. A. Brostrem, N. A. Bushe, et al. (eds.), Construction Materials (A Handbook) [in Russian], Mashinostroenie, Moscow (1990). 688 p.
W. Dahl and W. Anton (eds.), Static Strength and Fracture Mechanics of Steels [in German], Verlag Stahleisen GmbH, Dusseldorf (1983).
A. M. Borzdyka and L. B. Gertsov, Stress Relaxation in Metals and Alloys [in Russian], Metallurgiya, Moscow (1978), 272 p.
This work was supported by the Ministry of Education and Science of the Russian Federation (Agreement No. 02.G25.31.0068 of 23.05.2013) in the framework of investigations according to Governmental Order No. 218.
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 8, pp. 8 – 14, August, 2017.
Rights and permissions
About this article
Cite this article
Berezin, S.K., Shatsov, A.A., Bykova, P.O. et al. Martensitic Transformation in Low-Carbon Steels. Met Sci Heat Treat 59, 479–485 (2017). https://doi.org/10.1007/s11041-017-0175-0
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11041-017-0175-0