Abstract
In this paper, we report the control of important hysteresis parameters, which are useful for memory devices, viz. M s , H c and M r /M s , by changing the particle size/calcination temperature. An investigation of SrFe12O19 nanopowder from the structural and magnetic aspect is performed using X-ray diffraction (XRD), High Resolution Transmission Electron Microscopy (HRTEM), Scanning Electron Microscopy (SEM) and Vibrating Sample Magnetometer (VSM). The average particle size (APS) of SrFe12O19(nanopowder) increases from 26 to 600 nm with calcination temperatures of 400 and 1100 °C in air, respectively. With the increase in calcination temperature, saturation magnetization (M s ) increases with the decrease in coercivity for the respective sample. The change in saturation magnetization and coercive field are explained on the basis of transition from single domain structure to multi-domain geometry with an increase in the heating temperature. The sample heated at 1000 °C shows a minimum coercive field (2.71 kOe) and an appropriate squareness ratio (M r /M s ) compared to other calcined samples.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Brassard, S., Champigny, B.: In: Dempsey, N.M., deRango, P. (eds.) Proceedings of 18th International Workshop on High Performance Magnets and Their Applications, Annecy, France, 29 August–2 September, vol. 1, p. 22 (2004)
Karabasov, Yu.S. (ed.) New Materials. MISiS, Moscow (2002)
Wang, J.F., Paonton, C.B., Harris, I.R.: J. Magn. Magn. Mater. 298, 122 (2006)
Ataie, A., Heshmati-Manesh, S.: J. Eur. Ceram. Soc. 21, 1951 (2001)
García-Cerda, L.A., Rodríguez-Fernández, O.S., Reséndiz-Hernández, P.J.: J. Alloys Compd. 369, 182 (2004)
Fu, Y.P., Lin, C.H., Pan, K.Y.: J. Alloys Compd. 349, 228 (2003)
Ding, J., Miao, W.F., McCormick, P.G., Street, R.: J. Alloys Compd. 281, 32 (1998)
Vijayalakshmi, A., Gajbhiye, N.S.: J. Appl. Phys. 83, 400 (1997)
Wang, Y., Li, Q., Zhang, C., Li, B.: J. Alloys Compd. 467, 284 (2009)
Liu, X., Wang, J., Gan, L.M., Ng, S.C.: J. Magn. Magn. Mater. 195, 452 (1999)
Ketov, S.V., Yagodkin, Yu.D., Lebed, A.L., Chernopyatova, Yu.V., Khlopkov, K.: J. Magn. Magn. Mater. 300, e479 (2006)
Tenaud, P., Morel, A., Kools, F., Breton, J.M., Lechevallier, L.: J. Alloys Compd. 370, 331 (2004)
Liu, X., Wang, J., Gan, L.M., Ng, S.C.: J. Magn. Magn. Mater. 184, 344 (1998)
Topal, U., Ozkanb, H., Dorosinskii, L.: J. Alloys Compd. 428, 17 (2007)
Bernier, J.C.: Mater. Sci. Eng. 233, 109A (1989)
Cullity, B.D.: Introduction to Magnetic Material. Addison-Wesley, Reading (1972)
Smith, J., Wijin, H.P.J.: Les Ferrites. Dunod, Paris (1961)
Zi, Z.F., Sun, Y.P., Zhu, X.B., Yang, Z.R., Dai, J.M., Song, W.H.: J. Magn. Magn. Mater. 320, 2746 (2008)
Otani, Y.: In: Hadjipapary, G.C., Prinz, G.A. (eds.) Science and Technology of Nanostructured Magnetic Materials, p. 695. Plenum, New York (1991)
Rezlescu, L., Rezlescu, E., Popa, P.D., Rezlescu, N.J.: J. Magn. Magn. Mater. 193, 288 (1999)
Chen, D.-H., Chen, Y.-Y.: Mater. Res. Bull. 37, 801 (2002)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kumar, N., Kumar, A., Jha, R. et al. Impact of Particle Size on Room Temperature Ferrimagnetism of SrFe12O19 . J Supercond Nov Magn 23, 423–427 (2010). https://doi.org/10.1007/s10948-010-0766-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-010-0766-0