Abstract
Noble metal particles supported on transition metal oxides (TMO) may undergo a so-called strong metal–support interaction via encapsulation. This perspective addresses catalytic properties of the metal catalysts in the SMSI state which can be explained on the basis of complementary studies performed on well-defined, metal-supported TMO films. In particular, the results of low temperature CO oxidation revealed the key role of weakly bound oxygen species provided by a two-dimensional (“monolayer”) oxide film. The binding energy of such oxygen atoms can be used as a descriptor for oxidation activity. Reaction rate enhancement often observed for TMO films partially covering the metal surface is rationalized within a mechanism in which the metal acts as a promoter to create the most active “oxidered/oxideox” interface formed by reduced and oxidized phases in the film. Although only low temperature CO oxidation is considered, it is tempting to generalize these ideas to other oxidation reactions following the Mars–van Krevelen type mechanism. In addition, metal-supported ultrathin TMO films may serve as well-defined model systems to examine different aspects of the “electron theory of catalysis” which was proposed long ago and which is based on electron transfer mechanisms.
Graphical Abstract
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
The term strong metal–support interaction (SMSI) is commonly associated with the original works of Tauster and co-workers from the late 1970s, who observed that the uptake of H2 and CO drops after some treatment of oxide-supported noble metal catalysts, most markedly for Pt supported on TiO2 [1, 2]. As a possible explanation, the authors first suggested electronic effects via charge transfer and even rejected metal encapsulation which is now considered as the main manifestation of SMSI, based on recent advanced electron spectroscopy studies [3, 4]. SMSI is sometimes used in a more general sense by including support effects on metal dispersion, spatial distribution, and particle shape. Although the Pt/TiO2 system remains the classic example of SMSI via encapsulation, several other combinations of reducible transition metal oxides (TMO) and metals have shown similar behavior [5,6,7,8]. Despite enormous efforts to directly visualize the encapsulation process, the precise mechanism of encapsulation remains unknown. Thermodynamic considerations favor oxide spillover onto the metal surface rather than migration through the metal particle and subsequent segregation to the surface. Considering only the final structure of a catalyst in such a state, we are left, in essence, with a system consisting of a thin oxide film fully or partially covering a metal particle. Accordingly, the morphology and chemical composition of the oxide overlayer can be rationalized on the basis of results obtained for the growth of thin oxide films on metal substrates. In the absence of kinetic effects, the growth mode is determined by a balance between the surface free energies of the oxide, the metal and of the metal/oxide interface [9, 10]. Note, however, that ambient gases may additionally affect the final structure. Since the surface energies of TM oxides are considerably smaller than those of catalytically relevant metals, one expects that the oxide will wet the metal surface. Of course, if the encapsulating oxide film is thick, e.g. a few nanometers, such metal particles “buried” by the oxide support will not be involved in the catalytic reactions. However, when the oxide layer thickness is comparable to the oxide lattice constants the situation is not as straightforward and intriguing effects appear. Henceforth, we refer to such films as “ultrathin”, “two-dimensional (2D-)”, or “monolayer” films. An even more complicated picture develops if the metal surface is only partially covered, either by small patches of a 2D-oxide film or oxide nanoparticles. Therefore, one may reasonably assume that the catalytic properties of TMO supported metal catalysts in the SMSI state (via encapsulation) is intimately linked with the structure and reactivity of metal-supported ultrathin TMO films. This is the focus of the present Perspective.
Well-ordered oxide films grown on metal single crystal surfaces have long been used as planar model systems for studying chemical reactions at oxide surfaces and of metal nanoparticles deposited on them. Such systems facilitate the use of the experimental tools of surface science which are often based on the use of charged particles (ions or electrons) [9, 11,12,13]. In the course of such studies, it has been found that ultrathin films often show structures and properties different from their bulk counterparts and “thick” films [14,15,16,17,18,19]. Therefore, to understand catalytic reactions over a catalyst which underwent encapsulation, one needs to understand the reactivity of ultrathin oxide films. In the following, some examples will be discussed to validate this approach.
2 Discussion
Figure 1 shows scanning tunnelling microscopy (STM) and transmission electron microscopy (TEM) images of Pt particles deposited onto a crystalline Fe3O4(111) film grown on Pt(111) and then vacuum-annealed at 850 K. The images show well-faceted Pt particles exposing primarily the (111) surface [6, 20]. CO uptake measured by temperature programmed desorption (TPD) drops to almost zero upon high-temperature annealing, and as such the system manifests the classic SMSI effect. The STM images of the top facets revealed a hexagonal lattice of protrusions with an ~ 3 Å periodicity and a superstructure with an ~ 25 Å periodicity, which is clearly seen on large particles. This structure was assigned to a well-known monolayer thick FeO(111) film. Preparation of such films on Pt(111) and Pt(001) substrates was initiated by Somorjai and coworkers in the early 1990s [12, 21]. Further evidence for Pt encapsulation came from cross-sectional high-resolution TEM studies [20] as shown in Fig. 2a, b.
As another example, we refer to STM studies of Pt deposited onto a TiO2(110) single crystal [22]. Upon high temperature annealing in vacuum, the top facets of Pt particles showed structures virtually identical to those obtained for ultrathin TiOx films grown on Pt(111) [23]. Although the precise atomic structures remain under debate, this example provides further evidence that oxide overlayers formed upon encapsulation of metal nanoparticles bear close resemblance and may even be virtually identical to the ultrathin oxide films prepared on the respective metal surfaces.
In the case of the Pt/Fe3O4(111) system, which were studied in the CO oxidation reaction at nearly atmospheric pressures, the encapsulated Pt particles showed a considerably higher reaction rate than the uncovered Pt particles prepared at low temperatures [24]. This somewhat unexpected finding demonstrated that encapsulation, which is commonly thought to have a detrimental effect on reactivity, may actually promote a reaction. To rationalize this effect, we studied the structure–reactivity relationships of FeO(111) films on Pt(111). At low temperatures (i.e., below 500 K), the Pt(111) surface shows negligible activity due to the blocking of O2 dissociation by adsorbed CO. The FeO(111) film, on the other hand, showed much higher activity over a wide range of the CO:O2 ratios in the reaction mixture, most markedly in excess of O2 [25]. Therefore, it is the formation of an FeO(111) monolayer film on Pt particles that is responsible for the enhanced reactivity of Pt/Fe3O4(111) in the SMSI state.
Before we address the reaction mechanism, let us first recall that a monolayer FeO(111) film consists of close-packed layers of iron and oxygen stacked as O–Fe–Pt(111) (see Fig. 1d). The Moiré structure originates from the ~ 10% mismatch between the Pt(111) and FeO(111) surface lattices. The polar oxide surface is stabilized by strong inward relaxation of the Fe and O layers accompanied by considerable charge transfer to the Pt atoms at the interface. The film is very stable and chemically inert in UHV conditions. However, at higher oxygen chemical potentials, the FeO(111) film transforms into a structure where O–Fe–O tri-layer domains of local FeO2 stoichiometry form a close-packed structure that follows the Moiré pattern as a template [26] (see below). Note that the Fe ions in the FeO2 film are in the 3+ oxidation state due to electron transfer from the underlying Pt substrate [27].
When compared to the original FeO(111) film, the FeO2−x film possesses a much more weakly bound oxygen species which were revealed by TPD via a low temperature desorption peak that has tentatively been associated with the O atoms in the topmost layer of the FeO2 tri-layer, although the desorption mechanism remains unknown. Therefore, it is the formation of this weakly bound oxygen (WBO) at the oxide surface that likely promotes the CO oxidation reaction. A comparative TPD study [28] of various TMO films further linked the catalytic activity with the state of oxygen in the “oxygen-rich” films (i.e. treated in pure oxygen atmosphere). These studies showed that the weaker the surface oxygen is bound, the higher the reaction rate is (Fig. 2). Thus, the desorption temperature of WBO species can be used as a good descriptor for oxidation activity to first approximation. Since CO adsorbs weakly on almost all oxide surfaces, its adsorption properties do not differ drastically for various oxides, at least for the closed films. Moreover, reactivity studies of FeO(111) monolayer films grown on Au(111) revealed a direct correlation between the total amount of WBO species in the sample and the reaction rate [29]. Although the atomic structure of the “O-rich” films on Au(111) remains unclear and may differ from that on Pt(111), the results further point to weakly bound surface oxygen as the key species in the CO oxidation reaction.
The observed relationship between the reaction rate and O2 desorption temperature favours a Mars–van Krevelen (MvK) type mechanism: The CO2 molecule formed by the CO + O reaction desorbs and leaves an oxygen vacancy behind, which is then filled by O2 from the gas phase to complete the catalytic cycle. On the basis of density functional theory (DFT) calculations performed on a continuous FeO2 tri-layer film on Pt(111), it was concluded that the reaction takes place between CO in the gas phase and O in the film, i.e. via the Eley–Rideal (ER) mechanism. In most cases, however, CO oxidation at surfaces follows the Langmuir–Hinshelwood (LH) mechanism, i.e. the associative reaction of adsorbed CO with O atoms formed by O2 dissociation. For the case of oxide surfaces terminated by oxygen, the reaction may, in fact, be triggered by the ER mechanism that opens up the metal cationic sites and thus provides conditions for the LH mechanism in the steady state via CO adsorption on metal sites and reaction with the surrounding oxygen species. For the FeO(111)/Pt(111) system, such a scenario suggests that CO first reacts with topmost oxygen in the O–Fe–O tri-layer, ultimately creating oxygen vacancies and hence exposing Fe cations for CO adsorption.
Let us now address the case of metal surfaces partially covered by an oxide film. In fact, such studies were used in the past to understand the role of oxide promoters on noble metal catalysts, in particular in CO and CO2 hydrogenation reactions [30]. The results showed a maximum activity at sub-monolayer oxide coverage, scaled with the length of the perimeter at the oxide/metal boundary, and was therefore assigned to reactions taking place at the oxide/metal boundary. These so-called “inverse” [31,32,33], i.e. oxide-on-metal, model catalysts were used for elucidating reaction mechanisms in conventional, i.e. metal-on-oxide, catalysts, assuming that the metal-oxide interfacial structures are similar. With the help of STM, it was found, however, that oxide deposits on metal single crystals often form patches of ultrathin oxides with many different structures and complex phase diagrams [15, 17]. In this respect, ultrathin films of iron oxide show only one stable phase, i.e. FeO(111), on many noble metal surfaces (Pt, Pd, Au), which simplifies establishing structure–reactivity relationships.
The first results of Bao and co-workers for CO oxidation on FeO(111) islands on Pt(111) in UHV conditions were rationalized in terms of the reaction occurring at the FeO(111)/Pt(111) interface [34]. The mechanism was investigated with DFT calculations for several TMO(111) monolayer films supported on Pt(111) [35]. The calculations showed that O2 can dissociate on coordinatively unsaturated Fe sites at the interface resulting in O atoms bonded to both Fe and Pt, which then react with CO adsorbed on Pt to produce CO2. Although such a mechanism seems plausible under UHV conditions, it hardly holds true for higher pressures where the tri-layer FeO2−x phase forms.
CO oxidation on partially covered FeO(111)/Pt(111) films at near atmospheric pressures and 450 K revealed a maximum activity for films covering about 40% of the Pt(111) surface. This indicates that the oxide/metal interface is, indeed, more active than the oxide surface itself [36]. In addition, TPD studies of CO adsorbed on O-rich (i.e., FeO2−x) films also showed a maximum in CO2 production at ~ 40% coverage, whereas the TPD results on “as prepared” sub-monolayer FeO(111) films only showed fingerprints of CO oxidation on bare Pt(111). Therefore, the enhanced reactivity was reasonably assigned to the reaction between CO adsorbed on Pt and oxygen species adsorbed at the edge of FeO2−x (and not of FeO) islands. In principle, one could not rule out that the FeO(111) bilayer remains stable in the highly reducing ambient conditions applied, for example, in PROX (preferential CO oxidation in excess of hydrogen) [37]. However, the role of hydroxyls and water in this reaction remains to be investigated in detail.
Nonetheless, both proposed structures for the most active phase infer that the reaction occurs at the metal/oxide interfaces, either FeO2/Pt or FeO/Pt. However, a very recent study by Zhang et al. [38] provides some solid evidence that the catalytic reaction, in fact, takes place at neither interface, but instead at the boundary between reduced and oxidized phases of the film, in other words, at the oxidered/oxideox interface.
Figure 3 displays STM images of FeO2−x islands, where periodic protrusions of ~ 2 nm in diameter follow the Moiré structure of the original FeO(111) film and are assigned to FeO2 tri-layer domains. These are shown in side view in Fig. 3a [27]. CO exposure at 350–450 K reduces the FeO2−x phase back to FeO(111), even at pressures of 10−6 mbar. Time-lapse ex situ STM imaging showed that the reaction starts at the island edges and propagates into the interior [38]. Interestingly, the Moiré pattern is not lifted uniformly, but instead from the side that is closer to the island edge (Fig. 3b). This suggests that the reaction is initiated at the interface with Pt, and then continues by CO reacting at the interface between the oxidized FeO2−x phase and the reduced, FeO(111)-like phase left behind (Fig. 3c). Basically, the same mechanism is observed in CO and O2 reaction mixtures. Even in excess O2, the regions closest to the island edges undergo reduction, while the interior remains intact. Although in O2-rich atmospheres reduction does not propagate far from the island edge, it is clear that the initial FeO2−x/Pt interface does not exist anymore under the reaction conditions that provide sustained CO2 production (Fig. 4). When the oxygen flow is stopped, the CO2 production drops to zero, and recovers after re-introducing O2. However, the reaction rate is reduced upon cycling O2 flow on and off. Bearing in mind that the FeO2−x islands in pure CO ambient (i.e. in the absence of O2 in the flow) exhibit reduction that propagates from its edge towards the island interior (see Fig. 3), the reduction of the rate can readily be assigned to a decrease of the total perimeter length of the active oxidered/oxideox boundary.
One may argue that the chemical potential of O2 at low pressures used in these experiments is too low to efficiently replenish the O atoms, consumed by the fast reaction between CO on Pt and O at the edges of oxide islands, and hence too low to preserve the FeO2−x/Pt interface from the reduction propagating inside the island. On the other hand, a very similar oxide morphology was observed on dense FeO(111) films by consecutive exposures first to O2 and then to CO in the mbar pressure range [39]. In Fig. 5, one can easily recognize patches of FeO2−x surrounded by the reduced phase. Also, cut Moiré spots at the domain’s edge resemble those shown in Fig. 3b obtained at 10−6 mbar pressure. The formation of the reduced phase in the dense films is probably triggered at defects, whereas it readily occurs at the islands edges thanks to the reaction with CO adsorbed on Pt. Therefore, the volcano-type activity vs coverage plot [36] may be attributed to a facile formation of the oxidered/oxideox interface in vicinity of the oxide/metal boundary rather than to the catalytic reaction at the boundary itself.
The proposed mechanism agrees well with the DFT calculations of the oxygen vacancy formation energy [36]. Yet not all hypothetical structures have been computed, the lowest energy (1.36 eV) is obtained for the O atoms at the FeO2/FeO interface in the FeO2−x film (see Fig. 3a). Note, however, that this interface is not identical, to the oxidered/oxideox interface formed during the CO oxidation reaction, otherwise the reaction would occur homogeneously across the film, which is not the case. For comparison, the respective energies for O atoms at FeO2/Pt (1.53 and 1.58 eV) are considerably higher, which are, in turn, lower than those computed for the topmost oxygen in the FeO2 trilayer (1.67 eV). These are all much more weakly bound than O atoms at the FeO/Pt interface (2.15 eV). Therefore, the DFT calculations nicely corroborate the key role of WBO species in this reaction.
It is worth mentioning that recent studies on CoO(111) islands, grown on Au(111) and Pt(111) and considered as model catalysts for the oxygen evolution reaction [40, 41], revealed close similarities to FeO(111) with respect to the oxygen induced transformations and interaction with water [42]. Even though the CoO(111) films have not yet been studied in catalytic reactions, this finding allows generalization of the principles underlying the formation and reactivity of “tri-layer” TMO films.
Among the thin films studied in CO oxidation, ZnO(0001) films were the least active (Fig. 2). In principle, this may be related to the fact that ZnO is not a reducible oxide, and that the formation energy of an oxygen vacancy is relatively high [43]. Another reason can be related to the fact that the ultrathin ZnO films relax into a graphene-like structure. However, the CO2 production rate considerably increases on ZnO monolayer films on Pt(111) at sub-monolayer coverage [44]. Again, this finding has been interpreted as direct evidence for the reaction occurring at the metal/oxide boundary, although STM studies revealed structural transformations at near atmospheric pressures resulting in ZnO bilayer sheets. Such a rate enhancement was not observed for ZnO bilayer islands grown on Ag(111) [45]. In fact, ZnO deposits suppressed the reactivity of a pure Ag(111) substrate. The support effect was reasonably explained by a much stronger CO adsorption on Pt(111) compared to Ag(111) which increases its residence time and hence probability for CO to react with oxygen at the island edge. However, in the light of the reaction mechanism proposed above for the FeO films, one cannot rule out that Pt eases the formation of the reduced oxide phase at the edge of bilayer ZnO sheets and hence provides conditions for sustained reaction on the oxide surface. Yet the results available to date for ZnO(0001) films do not allow to support or exclude this hypothesis.
So far we discussed systems where a TMO film was artificially grown on a noble metal surface or was formed as a result of encapsulation. However, catalysis on bimetallic or alloy particles containing TM may also result in such systems, even in the absence of SMSI, if the reaction takes place under net oxidizing conditions. In excess oxygen, surface segregation and subsequent oxidation of the least noble metal in the bimetallic particle (i.e. TM) is highly possible. The resulted oxide layer may fully or partially cover the metal particle surface, eventually forming a core–shell structure similar to a particle formed via encapsulation. For example, such a model could be considered to explain the promotional role of Fe added to Pt/Al2O3 catalysts used for PROX [46].
It is generally believed that only reducible TM oxides, either as a support or as additives, have a promotional effect on catalysis by metals. Although there seem to be no systematic studies, alumina and silica (as the classic non-reducible oxides) deposited on metal surfaces will most likely block catalytic reactions. Moreover, metal catalysts supported on Al2O3 and SiO2 show no SMSI effects. Nevertheless, the “ultrathin film” approach can be applied to alumina (silica) supported metal catalysts in strongly oxidizing conditions as well. It is well-documented in the literature that at relatively high O2 pressures and temperatures even noble metals such as Pt, Pd, and Ag may form ultrathin oxide overlayers which are considered the most active (see a short review in ref. [47]). Interestingly, these “native” oxides exhibit in some cases the tri-layer structural motif.
Perhaps the most famous example highlighting the role of native oxide films is the formation of a well-ordered RuO2(110) film on Ru(0001), which may grow up to a few nanometers in thickness depending on the ambient conditions [48]. The results of CO oxidation performed on this system fit nicely the general trend shown in Fig. 2. In this respect, it is worth mentioning that the correlation between oxygen binding energy and catalytic activity was reported long ago for pure oxide catalysts [49]. Such a trend obtained on different systems allows us to make a more general conclusion: The reactivity of ultrathin oxide films is, in essence, determined by its ability to provide “active” WBO oxygen, which is, in turn, linked with the ultra-thinness and/or peculiar structure of the oxide stabilized by the metal support. Indeed, the CO oxidation studies discussed above were carried out in an O2-rich atmosphere in order to maintain the 2D character of the films, which otherwise dewet in O2-lean conditions and slows down the reaction.[25].
The formation of thin oxide layers on metals and its possible effects on catalysis have been intensively discussed since the 1950s, most notably by Volkenstein [50] and Schwab [51]. This culminated in the so-called “electron theory of catalysis” focusing on the role of charge carriers and based, in essence, on models developed for metal/semiconductor interfaces. It was believed that native oxide films formed on metals can be used to control charge transfer to and from surface ad-species rendering them catalytically active. Certainly, this scenario may also be applied to the TMO films formed on metals as a result of encapsulation. Interest in this theory has decreased over time until recently. It has started to receive considerable attention again thanks to the substantial development of experimental tools that allow the preparation of well-defined ultrathin oxide films.
Charge transfer processes mediated by ultrathin oxide films have already been proven, both experimentally and theoretically, for several cases of metal adsorption, most notably on MgO(001) films [52]. The process is controlled by the work function which can, in principle, be tuned by choosing a combination of an oxide and a metal [53]. As far as adsorption of gas molecules is concerned, the situation is less certain as the results are relatively scarce [54,55,56]. A DFT study [57] of CO oxidation over MgO(001)/Ag(001) predicted the reaction mechanism (still awaiting for experimental proof), in which oxygen reacting with CO is activated by charge transfer.
Clearly, further studies remain to be done to identify catalytic reactions which are, governed by charge transfer through the oxide film. Nonetheless, well-defined ultrathin films with a controllable thickness provide good planar models to examine such effects on catalysis.
3 Synopsis
The results discussed here in detail for the iron oxide—Pt system demonstrate that catalytic properties of TMO-supported metal particles in the SMSI state can be rationalized on the basis of complementary studies performed on metal-supported ultrathin TMO films.
In particular, the results of low temperature CO oxidation revealed the key role of weakly bound oxygen species in the reaction. Although only CO oxidation was considered, it is tempting to generalize these ideas to other oxidation reactions that follow a Mars–van Krevelen mechanism.
Reaction rate enhancement observed for TMO films partially covering the metal surface is commonly attributed to reactions occurring at the interfacial sites between ad-species on the metal and the oxygen in the oxide. Recent results provide some evidence for another mechanism, in which Pt solely behaves as a promoter to create the most active “oxidered/oxideox” interface formed by reduced and oxidized phases in the TMO film.
The results suggest that certain precautions must be taken when using “inverse”, i.e. oxide-on-metal, model catalysts to understand reactions occurring on conventional metal/TMO catalysts. It appears that the two-dimensional character of ultrathin films is important for the structure–reactivity relationships observed.
Finally, well-defined ultrathin TMO films supported on metals may serve as good model systems to examine some aspects of “electron theory of catalysis” which was introduced in the past and based on electron transfer mechanisms.
References
Tauster SJ, Fung SC, Garten RL (1978) Strong metal-support interactions. Group 8 noble metals supported on titanium dioxide. J Am Chem Soc 100(1):170–175
Tauster SJ (1987) Strong metal-support interactions. ACC Chem Res 20(11):389–394
Liu J (2011) Advanced electron microscopy of metal–support interactions in supported metal catalysts. ChemCatChem 3(6):934–948
Shi XY, Zhang W, Zhang C, Zheng WT, Chen H, Qi JG (2016) Real-space observation of strong metal-support interaction: state-of-the-art and what’s the next. J Microsc 262(3):203–215
Bernal S, Calvino JJ, Cauqui MA, Gatica JM, Larese C, Pérez Omil JA et al (1999) Some recent results on metal/support interaction effects in NM/CeO2 (NM: noble metal) catalysts. Catal Today 50(2):175–206
Qin ZH, Lewandowski M, Sun YN, Shaikhutdinov S, Freund HJ (2008) Encapsulation of Pt nanoparticles as a result of strong metal–support interaction with Fe3O4(111). J Phys Chem C 112(27):10209–10213
Haller GL, Resasco DE (1989) Metal–support interaction: group VIII metals and reducible oxides. In: Eley DD, Pines H, Weisz PB (eds) Advances in catalysis, vol 36. Academic Press, San Diego, pp 173–235
Bowker M, Stone P, Morrall P, Smith R, Bennett R, Perkins N et al (2005) Model catalyst studies of the strong metal–support interaction: surface structure identified by STM on Pd nanoparticles on TiO2(110). J Catal 234(1):172–181
Campbell CT (1997) Ultrathin metal films and particles on oxide surfaces: structural, electronic and chemisorptive properties. Surf Sci Rep 27(1–3):1–111
Bauer E (1958) Phänomenologische Theorie der Kristallabscheidung an Oberflächen. I. Z Kristal, p 372
Chambers SA (2000) Epitaxial growth and properties of thin film oxides. Surf Sci Rep 39(5):105–180
Weiss W, Ranke W (2002) Surface chemistry and catalysis on well-defined epitaxial iron-oxide layers. Prog Surf Sci 70(1–3):1–151
Kuhlenbeck H, Shaikhutdinov S, Freund H-J (2013) Well-ordered transition metal oxide layers in model catalysis: a series of case studies. Chem Rev 113(6):3986–4034
Franchy R (2000) Growth of thin, crystalline oxide, nitride and oxynitride films on metal and metal alloy surfaces. Surf Sci Rep 38(6–8):195–294
Netzer FP, Allegretti F, Surnev S (2010) Low-dimensional oxide nanostructures on metals: hybrid systems with novel properties. J Vac Sci Technol B 28(1):1–16
Netzer FP, Fortunelli A (eds) (2016) Oxide materials at the two-dimensional limit. Springer, Cham
Wu Q-H, Fortunelli A, Granozzi G (2009) Preparation, characterisation and structure of Ti and Al ultrathin oxide films on metals. Int Rev Phys Chem 28(4):517–576
Freund H-J, Pacchioni G (2008) Oxide ultra-thin films on metals: new materials for the design of supported metal catalysts. Chem Soc Rev 37(10):2224–2242
Goniakowski J, Finocchi F, Noguera C (2008) Polarity of oxide surfaces and nanostructures. Rep Prog Phys 71(1):016501
Willinger MG, Zhang W, Bondarchuk O, Shaikhutdinov S, Freund H-J, Schlögl R (2014) A case of strong metal–support interactions: combining advanced microscopy and model systems to elucidate the atomic structure of interfaces. Angew Chem Int Ed 53(23):5998–6001
Vurens GH, Maurice V, Salmeron M, Somorjai GA (1992) Growth, structure and chemical properties of FeO overlayers on Pt(100) and Pt(111). Surf Sci 268(1–3):170–178
Dulub O, Hebenstreit W, Diebold U (2000) Imaging cluster surfaces with atomic resolution: the strong metal-support interaction state of Pt supported on TiO2(110). Phys Rev Lett 84(16):3646–3649
Barcaro G, Agnoli S, Sedona F, Rizzi GA, Fortunelli A, Granozzi G (2009) Structure of reduced ultrathin TiOx polar films on Pt(111). J Phys Chem C 113(14):5721–5729
Lewandowski M, Sun YN, Qin ZH, Shaikhutdinov S, Freund HJ (2011) Promotional effect of metal encapsulation on reactivity of iron oxide supported Pt catalysts. Appl Catal A 391(1–2):407–410
Sun YN, Qin ZH, Lewandowski M, Carrasco E, Sterrer M, Shaikhutdinov S et al (2009) Monolayer iron oxide film on platinum promotes low temperature CO oxidation. J Catal 266(2):359–368
Sun Y-N, Giordano L, Goniakowski J, Lewandowski M, Qin Z-H, Noguera C et al (2010) The interplay between structure and CO oxidation catalysis on metal-supported ultrathin oxide films. Angew Chem Int Ed 49(26):4418–4421
Giordano L, Lewandowski M, Groot IMN, Sun YN, Goniakowski J, Noguera C et al (2010) Oxygen-induced transformations of an FeO(111) film on Pt(111): a combined DFT and STM study. J Phys Chem C 114(49):21504–21509
Martynova Y, Shaikhutdinov S, Freund H-J (2013) CO oxidation on metal-supported ultrathin oxide films. What makes them active? ChemCatChem 5(8):2162–2166
Weng X, Zhang K, Pan Q, Martynova Y, Shaikhutdinov S, Freund H-J (2017) Support effects on CO oxidation on metal-supported ultrathin FeO(111) films. ChemCatChem 9(4):705–712
Boffa AB, Lin C, Bell AT, Somorjai GA (1994) Lewis acidity as an explanation for oxide promotion of metals: implications of its importance and limits for catalytic reactions. Catal Lett 27(3–4):243–249
Gunter PLJ, Niemantsverdriet JW, Ribeiro FH, Somorjai GA (1997) Surface science approach to modeling supported catalysts. Catal Rev 39(1–2):77–168
Hayek K, Fuchs M, Klötzer B, Reichl W, Rupprechter G (2000) Studies of metal–support interactions with “real” and “inverted” model systems: reactions of CO and small hydrocarbons with hydrogen on noble metals in contact with oxides. Top Catal 13(1):55–66
Leisenberger FP, Surnev S, Koller G, Ramsey MG, Netzer FP (2000) Probing the metal sites of a vanadium oxide–Pd(111) ‘inverse catalyst’: adsorption of CO. Surf Sci 444(1):211–220
Fu Q, Li W-X, Yao Y, Liu H, Su H-Y, Ma D et al (2010) Interface-confined ferrous centers for catalytic oxidation. Science 328(5982):1141–1144
Sun D, Gu X-K, Ouyang R, Su H-Y, Fu Q, Bao X et al (2012) Theoretical study of the role of a metal–cation ensemble at the oxide–metal boundary on CO oxidation. J Phys Chem C 116(13):7491–7498
Pan Q, Weng X, Chen M, Giordano L, Pacchioni G, Noguera C et al (2015) Enhanced CO oxidation on the oxide/metal interface: from ultra-high vacuum to near-atmospheric pressures. ChemCatChem 7(17):2620–2627
Fu Q, Yao Y, Guo X, Wei M, Ning Y, Liu H et al (2013) Reversible structural transformation of FeOx nanostructures on Pt under cycling redox conditions and its effect on oxidation catalysis. Phys Chem Chem Phys 15(35):14708–14714
Zhang K, Li L, Shaikhutdinov S, Freund H-J (2018) Carbon monoxide oxidation on metal-supported monolayer oxide films: establishing which interface is active. Angew Chem Int Ed 57(5):1261–1265
Lewandowski M, Groot IMN, Shaikhutdinov S, Freund HJ (2012) Scanning tunneling microscopy evidence for the Mars-van Krevelen type mechanism of low temperature CO oxidation on an FeO(111) film on Pt(111). Catal Today 181(1):52–55
Walton AS, Fester J, Bajdich M, Arman MA, Osiecki J, Knudsen J et al (2015) Interface controlled oxidation states in layered cobalt oxide nanoislands on gold. ACS Nano 9(3):2445–2453
Fester J, García-Melchor M, Walton AS, Bajdich M, Li Z, Lammich L et al (2017) Edge reactivity and water-assisted dissociation on cobalt oxide nanoislands. Nat Commun 8:14169
Fester J, Sun Z, Rodríguez-Fernández J, Walton A, Lauritsen JV (2018) Phase transitions of cobalt oxide bilayers on Au(111) and Pt(111): the role of edge sites and substrate interactions. J Phys Chem B 122(2):561–571
Janotti A, Walle CGVd (2005) Oxygen vacancies in ZnO. Appl Phys Lett 87(12):122102
Martynova Y, Liu BH, McBriarty ME, Groot IMN, Bedzyk MJ, Shaikhutdinov S et al (2013) CO oxidation over ZnO films on Pt(111) at near-atmospheric pressures. J Catal 301(0):227–232
Pan Q, Liu BH, McBriarty ME, Martynova Y, Groot IMN, Wang S et al (2014) Reactivity of ultra-thin ZnO films supported by Ag(111) and Cu(111): a comparison to ZnO/Pt(111). Catal Lett 144(4):648–655
Liu X, Korotkikh O, Farrauto R (2002) Selective catalytic oxidation of CO in H2: structural study of Fe oxide-promoted Pt/alumina catalyst. Appl Catal A 226(1):293–303
Shaikhutdinov S, Freund H-J (2012) Ultrathin oxide films on metal supports: structure-reactivity relations. Annu Rev Phys Chem 63(1):619–633
Over H (2012) Surface chemistry of ruthenium dioxide in heterogeneous catalysis and electrocatalysis: from fundamental to applied research. Chem Rev 12(6):3356–3426
Pankratiev YD (1982) Correlation between oxygen binding energy and catalytic activity of oxides. React Kinet Catal Lett 20(3):255–259
Vol’kenshtein FF (1966) Experiment and the electronic theory of catalysis. Russ Chem Rev 35(7):537
Schwab G-M (1979) Electronics of supported catalysts. In: Eley DD, Pines H, Weisz P (eds) Advances in catalysis, Vol 27. Academic Press, San Diego, pp 1–22
Sterrer M, Risse T, Martinez U, Giordano L, Heyde M, Rust H-P et al (2007) Control of the charge state of metal atoms on thin MgO films. Phys Rev Lett 98(9):096107
Giordano L, Pacchioni G (2011) Oxide films at the nanoscale: new structures, new functions, and new materials. Acc Chem Res 44(11):1244–1252
Grönbeck H (2006) Mechanism for NO2 charging on metal supported MgO. J Phys Chem B 110(24):11977–11981
Gonchar A, Risse T, Freund H-J, Giordano L, Di Valentin C, Pacchioni G (2011) Activation of oxygen on MgO: O2.—radical ion formation on thin, metal-supported MgO(001) films. Angew Chem Int Ed 50(11):2635–2638
Merte LR, Heard CJ, Zhang F, Choi J, Shipilin M, Gustafson J et al (2016) Tuning the reactivity of ultrathin oxides: NO adsorption on monolayer FeO(111). Angew Chem Int Ed 55(32):9267–9271
Hellman A, Klacar S, Grönbeck H (2009) Low temperature CO oxidation over supported ultrathin MgO films. J Am Chem Soc 131(46):16636–16637
Acknowledgements
Open access funding provided by Max Planck Society. I am grateful to Hajo Freund for giving me opportunity to lead the group “Structure and Reactivity” in the Fritz-Haber Institute. I thank all my coworkers listed in the references for their tremendous work in laboratories. These studies could not be performed successfully without a substantial theoretical support by Gainfranco Pacchioni, Claudine Noguera, Jacek Goniakowski, and Livia Giordano, I am fortunate to collaborate with.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
There are no conflicts to declare.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Shaikhutdinov, S. Strong Metal–Support Interaction and Reactivity of Ultrathin Oxide Films. Catal Lett 148, 2627–2635 (2018). https://doi.org/10.1007/s10562-018-2499-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10562-018-2499-9