Abstract
The crystal transformation of cellulose I to cellulose II during alkali swelling was investigated in decayed oak wood that was used for shiitake mushroom cultivation and the results were compared with those of sound wood using X-ray diffraction analysis and ultraviolet microscopy. During mercerization, the sapwood cellulose of decayed wood was easily transformed into Na-cellulose I and then Na-cellulose I was easily converted into cellulose II after washing and drying. The sapwood cellulose of sound wood was converted more slowly to Na-cellulose I and very little Na-cellulose was converted to cellulose II. Na-cellulose I of sound wood can be reconverted to cellulose I during washing and drying. Therefore, it could be concluded that lignin prevented the alkali swelling of wood cellulose and the transformation from cellulose I to cellulose II. The decay of crystalline cellulose might cause an increase in the susceptibility of alkali swelling, so that the degree of mercerization may be also affected.
Article PDF
Similar content being viewed by others
Author information
Authors and Affiliations
Corresponding author
About this article
Cite this article
Kim, NH. An investigation of mercerization in decayed oak wood by a white rot fungus (Lentinula edodes). J Wood Sci 51, 290–294 (2005). https://doi.org/10.1007/s10086-004-0650-2
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10086-004-0650-2