Abstract.
The laser ablation of polyimide was studied using 308 nm laser irradiation ≤225 mJ cm-2. Confocal Raman microscopy revealed the deposition of carbon surrounding the ablation crater, which consists of amorphous carbon with some crystalline features. Inside the crater, graphitic material was detected on top of the cones, very similar to the material from cw-Ar+ ion laser irradiation. FT-Raman measurements reveal the presence of intermediates of the polyimide decomposition. Imaging-X-ray photoelectron spectroscopy confirmed the deposition of carbon material surrounding the ablation crater and showed that the oxygen and nitrogen contents of the remaining material decrease.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Author information
Authors and Affiliations
Additional information
Received: 21 July 1999 / Accepted: 1 September 1999 / Published online: 22 December 1999
Rights and permissions
About this article
Cite this article
Lippert, T., Ortelli, E., Panitz, JC. et al. Imaging-XPS/Raman investigation on the carbonization of polyimide after irradiation at 308 nm . Appl Phys A 69 (Suppl 1), S651–S654 (1999). https://doi.org/10.1007/s003390051497
Issue Date:
DOI: https://doi.org/10.1007/s003390051497