Abstract
The use of graphite as a moderator in a low temperature thermal nuclear reactor is restricted due to accumulation of energy caused by displacement of atoms by neutrons and high energetic particles. Thermal transients may lead to a release of stored energy that may raise the temperature of the fuel clad above the design limit. Disordered carbon is thought to be an alternative choice for this purpose. Two types of disordered carbon composites, namely, CB (made up of 15 wt. % carbon black dispersed in carbonized phenolic resin) and PAN (made up of 20 vol. % chopped polyacrylonitrile carbon fibre dispersed in carbonized phenolic resin matrix) have been irradiated with 145 MeV Ne6+ ions at three fluence levels of 1.0×1013, 5.0×1013 and 1.5×1014 Ne6+/cm2, respectively. The XRD patterns revealed that both the samples remained disordered even after irradiation. The maximum release of stored energy for CB was 212 J/g and that of PAN was 906 J/g. For CB, the release of stored energy was a first order reaction with activation energy of 2.79 eV and a frequency factor of 3.72×1028 per second. 13% of the defects got annealed by heating up to 700 °C. PAN showed a third-order release rate with activation energy of 1.69 eV and a frequency factor of 1.77×1014 per second. 56% of the total defects got annealed by heating it up to 700 °C. CB seems to be the better choice than PAN as it showed less energy release with a slower rate.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
B.T. Kelly, Materials Science and Technology: Nuclear Materials, Part 1 (VCH, Weinheim, 1994), p. 365
L. Arnold, Windscale 1957, Anatomy of a Nuclear Accident (St. Martin’s Press, London, 1992)
R.E. Nightingale, Nuclear Graphite (Academic Press, New York, London, 1962)
D. Sathiyamoorthy, K. Dasgupta, S.M. Shetty, A.K. Suri, S. Banerjee, Development of Novel Carbon for Innovative Design of Nuclear Reactor, in: CD-ROM Proc. Int. Conf. ‘Carbon 2002’, Beijing, China (2002)
B.T. Kelly, Prog. Nucl. Energ. 2, 21 (1978)
V.I. Klimenkov, Y.N. Aleksenko, USSR Acad. Sci. Phys. 2, 226 (1956)
T.D. Burchell, Phys. Scripta T 64, 17 (1996)
T. Iwata, J. Nucl. Mater. 133/134, 361 (1985)
J.C. Bell, B.S. Gray, Stored Energy Studies made on Windscale Pile Graphite since October 1957, UKAEA Report TRG 84 (W) (1961)
K. Dasgupta, M. Roy, A.K. Tyagi, S.K. Kulshreshtha, Ramani Venugopalan, D. Sathiyamoorthy, Compos. Sci. Technol. (2006), DOI: 10.1016/j.compscitech.2006.10.026
J.P. Biersack, L.G. Haggmark, Nucl. Instrum. Methods 174, 257 (1980)
A.C. Damask, G.J. Dienes, Point Defects in Metals (Gordon and Breach, New York, 1963), p. 145
A. Sarkar, K. Dasgupta, P. Barat, P. Mukherjee, D. Sathiyamoorthy, Int. J. Mod. Phys. B, unpublished
R.W. Weeks, R.O. Scattergood, S.R. Pati, J. Nucl. Mater. 36, 223 (1970)
S.D. Preston, G.T. Melvin, Results from the 1997/98 Stored Energy Survey of Windscale Pile 1, IAEA Technology plc Report AEAT-3400, WPTC 73 (1998)
T. Iwata, H. Suzuki, Radiation Damage in Reactor Materials (IAEA, Vienna, 1963), p. 565
T. Iwata, T. Nihira, Japan. J. Appl. Phys. 15, 575 (1976)
Author information
Authors and Affiliations
Corresponding author
Additional information
PACS
61.80.Jh; 61.80.-x; 61.43Er; 61.43.-j; 68.43.Vx
Rights and permissions
About this article
Cite this article
Dasgupta, K., Barat, P., Sarkar, A. et al. Stored energy release behaviour of disordered carbon. Appl. Phys. A 87, 721–726 (2007). https://doi.org/10.1007/s00339-007-3883-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-007-3883-2