Abstract
This paper deals with the heat fixation of compressive deformation of sugi wood (Cryptomeria japonica D. Don) which is a typical Japanese coniferous wood with a low density. After wet specimens were compressed in the radial direction to about 50% of their original thickness and dried under restraint, they were subjected to heat treatment by three methods: beneath the surface of molten metal, and in the presence or absence of air. The relationship between the recovery of deformation and the weight loss was expressed by a hyperbolic equation regardless of heating methods. The retentions of the MOE and the MOR of compressed specimens at the perfect fixation were 89% and 81%, respectively. The perfect fixation of deformation was speculated to have resulted from the release of stresses stored in the cell wall polymers by their degradation as well as the reduction of hygroscopicity of the cell wall polymers.
Zusammenfassung
Bei dieser Untersuchung handelt es sich um die Hitzefixierung von Druckverformung bei Sugiholz (Cryptomeria japonica D. Don), einer typischen japanischen Nadelholzart mit niedriger Rohdichte. Nachdem feuchte Proben in radialer Richtung auf ungefähr 50% ihrer ursprünglichen Dicke zusammengepresst, und in diesem Zustand getrocknet worden waren, wurden sie nach drei verschiedenen Methoden einer Hitzebehandlung unterzogen: Unter der Oberfläche von geschmolzenem Metall, sowie mit und ohne Gegenwart von Luft. Die Beziehung zwischen der Rückbildung der Verformung und dem Gewichtsverlust wurde mittels einer hyperbolischen Gleichung, ungeachtet der Heizmethoden, ausgedrückt. Bei perfekter Fixierung der Verformung der gepreßten Proben beliefen sich MOE und MOR auf 89% und 81%. Es wurde angenommen, daß die perfekte Fixierung derVerformung sowohl von dem Nachlassen der Spannung in den Zellwandpolymeren und durch deren Abbau, als auch durch die Verminderung ihrer Hygroskopität bewirkt wurde.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Fujimoto H (1992) Weathering behavior of chemically modified wood with a maleic acid glycerol (MG) mixture. New Zealand FRI Bull. 176: 87–96
Hillis WE, Rozsa AN (1978) The softening temperatures of wood. Hozforsch. 32(2): 68–73
Inoue M, Norimoto M, Otsuka Y, Yamada T (1990) Surface compression of coniferous wood lumber I. A new technique to compress the surface layer. Mokuzai Gakkaishi. 36(11): 969–975
Inoue M, Norimoto M, Tanahashi M, Rowell RM (1993) Steam or heat fixation of compressed wood. Wood and Fiber Sei. 25(3): 224–235
Inoue M, Minato K, Norimoto M (1994) Permanent fixation of compressive deformation of wood by crosslinking. Mokuzai Gakkaishi. 40(9): 931–936
Itoh T, Ishihara S (1997) Compressive deformation of wood using hot rollpress and its fixation by glyoxal resin. Mokuzai Gakkaishi. 43(1): 52–60
Seborg RM, Stamm A (1945) Heat stabilized compressed wood (Staypak). Mech. Eng. 67(1): 25–31
Seborg RM, Tarkow H, Stamm AJ (1953) Effect of heat upon the dimensional stabilization of wood. J. Forest Prod. Res. Soc 3(3): 59–67
Stamm AJ, Hansen LA (1937) Minimizing wood shrinkage and swelling. Effect of heating in various gases. Ind. Eng. Chem. 29(7): 831–833
Stamm AJ (1964) Wood and Cellulose Science. The Ronald Press Com., New York
Tiemann HD (1920) The kiln drying of lumber. Lippincott, J. P. Co., Philadelphia
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Dwsanto, W., Norirnoto, M., Morooka, T. et al. Radial compression of sugi wood (Cryptomeria japonica D. Don). Holz als Roh- und Werkstoff 56, 403–411 (1998). https://doi.org/10.1007/s001070050342
Issue Date:
DOI: https://doi.org/10.1007/s001070050342