Abstract
This paper describes changes in microtensile strength of six softwood species during natural weathering. All species showed a rapid reduction in both zero span and 10 mm span strength during three months weathering and the method proved capable of distinguishing differences in degradation rate and in the characteristic shape of the strength loss curve for the different species. The results indicated that lignin degradation is initially more rapid than cellulose. Although the principal trend was one of strength loss during weathering, some species showed a small strength increase after short exposure times. The strength changes are consistent with three radiation-induced processes, namely a mechanism whereby strength increases and two degradation processes occuring at different rates. A ‘Zero Intercept’ parameter was derived to characterise the strength loss curves.
Zusammenfassung
Diese Arbeit beschreibt die Änderung der Zugfestigkeit von sechs Nadelholzarten während einer natürlichen Bewitterung über einen Zeitraum von drei Monaten. Bei allen Holzarten ergab sich eine rasche Abnahme der Zugfestigkeit sowohl bei Prüflänge Null als auch bei 10 mm Prüflänge. Die Methode erwies sich als geeignet, Unterschiede in der Abbaurate und im Verlauf des Festigkeitsverlustes für die verschiedenen Holzarten zu erfassen. Die Ergebnisse deuten daraufhin, daß Lignin zunächst rascher abgebaut wird als Cellulose. Entgegen dem allgemeinen Trend eines kontinuierlichen Festigkeitsbverlustes während der Bewitterung zeigten einige Holzarten einen vorübergehenden Anstieg nach kurzer Bewitterungsdauer. Die Festigkeitsänderungen stehen in Zusammenhang mit drei durch Lichtstrahlung induzierten Prozessen, von denen einer zur Erhöhung der Festigkeit führt. Zwei andere beruhen auf Abbauvorgängen mit unterschiedlicher Geschwindigkeit. Aus den Meßdaten wurde ein spezieller Parameter (Zero Intercept) zur Charakterisierung der Abbaukurven entwickelt.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
8 References
Davis, A.; Deane, G. H. W.; Gordon, D.; Howell, G. V.; Ledbury, K. J. 1976: A world-wide program for the continuous monitoring of solar UV radiation using poly (phenylene) oxide film and a consideration of the results. J. Appl. Pol. Sci. 20: 1165–1174
Derbyshire, H.; Miller, E R. 1981: The photodegradation of wood during solar irradiation. Part 1. Effects on the structural integrity of thin wood strips. Holz Roh-Werkstoff 39: 341–350
Derbyshire, H.; Miller, E. R.; Turkulin, H. 1995: Investigation into the photodegradation of wood using microtensile testing. Part 1: The application of microtensile testing to measurement of photodegradation rates. Holz Roh-Werkstoff 53: 339–345
Evans, P. D.; Schmalzl, K. J.; Michell, A. J. 1992: Rapid loss of lignin at wood surfaces during natural weathering. IRG Document no IRG/WP/2390-92
Hon, D. N.-S.; Shiraishi, N. 1991: Wood and Cellulosic Chemistry. Ch. 11. Photochemistry of wood. Marcel Dekker Inc., New York and Basel
Horn, B. A.; Qiu, J. J.; Owen, N. L.; Feist, W. C. 1992: FT-IR studies of weathering effects in Western red cedar and Southern pine. FRI Bulletin 176: 67–76, 7–8 November 1992, Rotorua, New Zealand
Kalnins, M. A.; Knaebe, M. T. 1992: Wettability of weathered wood. J. Adhesion Sci. 6(12): 1325–1330
Williams, R. S.; Plantinga, P. L.; Feist, W. C., 1990: Photodegradation of wood affects paint adhesion. Forest Prod. J. 40(1): 45–49
Author information
Authors and Affiliations
Additional information
The authors wish to express their gratitude to the UK Department of the Environment and to the British Council and the Croatian Ministry of Science for supporting this work which will form part of the PhD thesis of the third author.
Rights and permissions
About this article
Cite this article
Derbyshire, H., Miller, E.R. & Turkulin, H. Investigations into the photodegradation of wood using microtensile testing. Holz als Roh- und Werkstoff 54, 1–6 (1996). https://doi.org/10.1007/s001070050123
Issue Date:
DOI: https://doi.org/10.1007/s001070050123