Abstract
The problems encountered with the interpretation of martensite and the various forms of bainite that are found in high strength steel weld metals have been addressed. Field emission gun scanning electron microscopy was found to overcome resolution difficulties often met with light optical microscopy and conventional scanning electron microscopy. Microstructural constituents were characterised both in the as-deposited and reheated tempered states. The characterisation of retained austenite and identification of carbide types remains challenging, and transmission electron microscopy is required.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Takahashi M., Bhadeshia H.K.D.H.: A model for the transition from upper to lower bainite, Materials Science and Technology, 1990, 6, pp. 592–603.
Keehan E., Microstructure characterisation of a high strength steel weld metal containing the novel constituent coalesced bainite, Ph. D. thesis, Chalmers University of Technology, Effect of microstructure on mechanical properties of high strength steel weld metals, Paper 3, 2004.
Keehan E. et al.: Microstructure and properties of novel high strength steel weld metals, Doc. IIW-1703-05 (ex-doc. IX-2146–05), Welding in the World, 2005, Vol. 49, No. 9/10, pp. 19–31.
Keehan E., Effect of microstructure on mechanical properties of high strength steel weld metals, in Experimental Physics, 2004, Chalmers University of Technology: Gothenburg, Sweden.
SSAB, WeldCalc. 1998–99: Oxelösund, Sweden.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Keehan, E., Karlsson, L., Thuvander, M. et al. Microstructural Characterisation of As-Deposited and Reheated Weld Metal — High Strength Steel Weld Metals. Weld World 51, 44–49 (2007). https://doi.org/10.1007/BF03266559
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF03266559