Abstract
A new process called “mechanical alloying” has been developed which produces homogeneous composite particles with an intimately dispersed, uniform internal structure. Materials formed by hot consolidation of this powder achieve the long-sought combination of dispersion strengthening and age-hardening in a high temperature alloy. While the process is amenable to making a variety of alloys, its first use has been to combine yttrium oxide and gamma prime hardening hr at 1400°F and 15,000 psi for 100 hr at 1900°F together with excellent sulfidation and cyclic oxidation resistance. From a fundamental standpoint, results show that the age-hardening dominates the low-temperature strength, dispersion strengthening dominates at high temperature, and the two are augmentative in the intermediate temperature range 1300° to 1500°F.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
W. D. Coolidge;Proc. Am. Inst. Elec. Eng., 1910, p. 961.
R. Irmann;Metallurgia, 1952, vol. 49, p. 125.
E. Gregory and N. J. Grant:AIME Trans., 1954, vol. 200, p. 247.
F. V. Lenel, A. B. Backensto, Jr., and M. V. Rose:AIME Trans., 1957, vol. 209, p. 124.
C. J. Leadbeater and discussion by E. Gregory: Symposium on Powder Metallurgy, 1954, Iron Steel Inst. Spec. Rept. No. 58, pp. 149–59, 357.
G. B. Alexanderet al.: U.S. Patent No. 2,972,529, Feb. 21, 1961.
F. J. Anders, Jr.: U.S. Patent No. 3, 159, 908, Dec. 8, 1964.
E. Gregory and C. G. Goetzel:Trans. TMS-AIME, 1958, vol. 212, p. 868.
K. M. Zwilsky and N. J. Grant:Trans. TMS-AIME, 1961, vol. 221, p. 371.
V. A. Tracey and D. K. Worn:Powder Met., 1962, no. 10, p. 34.
R. Murphy and N. J. Grant:Powder Met., 1962, no. 10, p. 1.
C. J. Smithells: U.S. Patent No. 2,406, 172, Aug. 20, 1946.
Dutch Patent No. 64030, Sept. 15, 1949.
J. C. Chaston:J. Inst. Metals, 1945, vol. 71, pp. 23–35.
L. J. Bonis and N. J. Grant:Trans. TMS-AIME, 1962, vol. 224, p. 308.
H. Spengler:Metall, 1964, vol. 18, p. 727.
M. Adachi and N. J. Grant:Trans. TMS-AIME, 1960, vol. 218, p. 881.
G. H. Howe:Powder Metallurgy, J. Wulff, ed., p. 530, ASM, 1942.
A. Steiner and K. L. Komarek:Trans. TMS-AIME, 1964, vol. 230, p. 786.
H. Wadham:J. Oil Colour Chemists Assoc., 1964, p. 728.
A. Szegvari: U. S. Patent No. 2,764, 359, Sept. 25, 1956.
A. M. Gaudin:Principles of Mineral Dressing, p. 106, McGraw Hill Book Co., New York, 1939.
F. C. Kelly:Weld. J. N. Y., 1951, vol. 30, p. 728.
S. L. Hoyt:AIME Trans., 1930, vol. 89, p. 9, see esp. p. 25.
G. S. Ansell and J. Weertman:Trans. TMS-AIME, 1959, vol. 215, p. 838.
High Temperature, High Strength Nickel-Base Alloys, The International Nickel Co., Inc., New York, 1964; Note: The values for the properties of TD Nickel are given only for reference and represent an average of the numbers reported in the open literature and in manufacturers’ pamphlets for varying bar sizes of this alloy.
J. W. Schultz: The International Nickel Co., Inc., Paul D. Merica Research Laboratory, Sterling Forest, Suffern, N. Y., private communication, 1969.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Benjamin, J.S. Dispersion strengthened superalloys by mechanical alloying. Metall Trans 1, 2943–2951 (1970). https://doi.org/10.1007/BF03037835
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF03037835