Abstract
Analysis of changes in surface roughness of CdS thin films with preparation temperature was carried out using variable angle spectroscopic ellipsometry (VASE). The films studied were prepared by spray pyrolysis technique, in the substrate temperature range 200–360°C. The VASE measurements were carried out in the visible region below the band gap (E g=2·4eV) of CdS so as to reduce absorption by the film. The thickness of the films was in the range 500–600 nm. Bruggeman’s effective medium theory was used for analysis of the surface roughness of the film. The roughness of the film had a high value (∼ 65 nm) for films prepared at low temperature (200°C) and decreased with increase in substrate temperature. This reached minimum value (∼ 27 nm) in the temperature range 280–300°C. Thereafter roughness increased slowly with temperature. The growth rate of the films was calculated for different temperature ranges. It was found that the deposition rate decreases with the increase in substrate temperature and have an optimum value at 300°C. Above this temperature deposition rate decreased sharply. The scanning electron micrograph (SEM) of the film also showed that the film prepared at 280–300°C had very smooth surface texture.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Albin D S and Risbud S H 1987Thin Solid Films 147 203
Arita T, Hanafusa H, Kitamura S and Takakura H 1991Conf. Records of 22nd Photovoltaic specialist conference. Las Vegas, NV, USA, p. 946
Azzam R M A and Bashara N M 1977Ellipsometry and polarized light (Amsterdam: North Holland) Chapter 4
Banerjee A, Nath P, Vankar V D and Chopra K L 1978Phys. Status Solidi (a) 46 723
Basol B M, Kapur V K and Halani A 1991Conf. Records of 22nd Photovoltaic specialist conference. Las Vegas, NV, USA p. 893
Bruggeman D A G 1935Ann. Phys. Leipzig 24 636
Cameron D C, Duncan W and Tsang W M 1979Thin Solid Films 58 61
Chopra K L and Das S R 1983Thin film solar cells (New York: Plenum Press) p. 297
Chow L W, Lee Y C and Lee Kwok H L 1981Thin Solid Films 81 307
Escosura L, Garcia-Camarero E, Arjona F and Rueda F 1984Solar Cells 11 211
Gupta B K and Agnihotri O P 1978Philos. Mag. B37 631
Kakayama N, Matasumoto H, Yamaguchi K and Iegami I S 1976Jpn. J. Appl. Phys. 15 2281
Kaur I, Pandya D K and Chopra K L 1981J. Electrochem. Soc. 127 943
Kwok H L 1980J. Phys. D. 13 1911
Nolly J, Abdullah K K and Vijayakumar K P 1987Phys. Status Solidi (a) 101 K35
Shay J L, Wagneer S, Bachman K, Buchlor E and Kaspor H M 1975Proc. 11th Photovoltaic specialist conference, Phoenix, New York, p. 503
Sunny M and Vijayakumar K P 1994Bull. Mater. Sci. 17 235
Valyommana A G, Vijayakumar K P and Purushothaman C 1992J. Mater. Sci. Lett. 11 616
Vedam K, Mc Marr P J and Narayan J 1985Appl. Phys. Lett. 47 339
Vijayakumar K P 1991aJ. Appl. Phys. 69 6771
Vijayakumar K P 1991bBull. Mater. Sci. 14 57
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Mathew, S., Vijayakumar, K.P. Ellipsometric studies of microscopic surface roughness of CdS thin films. Bull. Mater. Sci. 17, 421–427 (1994). https://doi.org/10.1007/BF02745230
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02745230