Glasses in the system PbO-BaO-TiO2-B2O3-SiO2 with and without P2O5 as nucleant have been prepared. The glass samples were ceramized based ondta studies. The ferroelectric phase crystallizing out has been found to be BaTiO3 fromxrd. The optical and scanning electron micrographs show the presence of BaTiO3 as major phase. In these glass ceramic samples, dielectric constant and dissipation factor are approximately constant with temperature and frequency upto the glass transition temperatureT g and thereafter increase sharply with temperature and finally level off. The addition of P2O5 as nucleant and molar ratio of (PbO + BaO) to TiO2 has marked influence on the dielectric behaviour and composition of ferroelectric phase crystallizing out.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Bergeron C G 1961Crystallization of perovskite lead titanate from glass, Ph.D. Thesis, University of Illinois
Borrelli N F and Layton M M 1971J. Non-Cryst. Solids 6 197
Grossman D G and Isard J O 1969aJ. Mater. Sci. 4 1059
Grossman D G and Isard J O 1969bJ. Am. Ceram. Soc. 52 230
Herczog A 1964J. Am. Ceram. Soc. 47 107
Herczog A 1984J. Am. Ceram. Soc. 67 484
Kokubo T and Tashiro M 1973/74J. Non-Cryst. Solids 13 328
Lynch S M and Shelby J E 1984J. Am. Ceram. Soc. 67 424
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Parkash, O., Kumar, D. & Rajgopalan, R. Microstructural and dielectric behaviour of glass ceramics in the system PbO-BaO-TiO2-B2O3-SiO2 . Bull. Mater. Sci. 8, 13–21 (1986). https://doi.org/10.1007/BF02744092
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02744092