Sulfide capacities of high alumina blast furnace slags were experimentally determined using the gas-slag equilibration technique. Two different slag systems were considered for the current study, namely, CaO-SiO2-MgO-Al2O3 quaternary and CaO-SiO2-MgO-Al2O3-TiO2 quinary system. The liquid slag was equilibrated with the Ar-CO-CO2-SO2 gas mixture. Experiments were conducted in the temperature range of 1773 to 1873 K. The effects of temperature, basicity, and the MgO and TiO2 contents of slags on sulfide capacity were studied. As expected, sulfide capacity was found to increase with the increase in temperature and basicity. At the higher experimental temperature, titania decreases the sulfide capacity of slag. However, at the lower temperature, there was no significant effect of titania on the sulfide capacity of slag. Sulfide capacity increases with the increase in MgO content of slag if the MgO content is more than 5 pct.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
F.D. Richardson and C.J.B. Fincham: J. Iron Steel Inst., 1954, vol. 178, pp. 4–15.
K. Kärsrud: Scand. J. Metall., 1984, vol. 13, pp. 173–75.
I. Ghita and H.B. Bell: Ironmaking and Steelmaking, 1982, vol. 9 (6), pp. 239–43.
K. Kärsrud: Scand. J. Metall., 1984, vol. 13, pp. 265–68.
V.S. Venkatadri and S.K. Gupta: Trans. Indian Inst. Met., 1979, vol. 32 (3), pp. 235–38.
R.W. Young, J.A. Duffy, G.J. Hassall, and Z. Xu: Ironmaking and Steelmaking, 1992, vol. 19 (3), pp. 201–19.
D.J. Sosinsky and I.D. Sommerville: Metall. Trans. B, 1986, vol. 17B, pp. 331–37.
M.M. Nzotta, D. Sichen, and S. Seetharaman: Iron Steel Inst. Jpn., 1998, vol. 38 (11), pp. 1170–79.
T. Xin and X. Chushao: Iron Steel Inst. Jpn. Int., 1995, vol. 35 (4), pp. 367–71.
S.D. Brown, R.J. Roxburgh, I. Ghita, and H.B. Bell: Ironmaking and Steelmaking, 1982, vol. 9 (4), pp. 163–67.
M.M. Nzotta, D. Sichen, and S. Seetharaman: Iron Steel Inst. Jpn., 1999, vol. 39 (7), pp. 1657–63.
S.R. Simeonov, R. Sridhar, and J.M. Toguri: Metall. Trans. B, 1995, vol. 26B, pp. 325–34.
I.D. Sommerville and H.B. Bell: Can. Metall. Q., 1982, vol. 21 (2), pp. 145–55.
J.A. Duffy and M.D. Ingram: J. Am. Chem. Soc., 1971, vol. 93, pp. 6448–55.
C.B. Fincham and F.D. Richardson: Proc. R. Soc. A, 1954, vol. 223, pp. 40–62.
K.P. Abraham and F.D. Richardson: J. Iron Steel Inst., 1960, vol. 196, pp. 309–17.
K. Karsrud: Scand. J. Metall., 1984, vol. 13, pp. 144–50.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Shankar, A., Görnerup, M., Seetharaman, S. et al. Sulfide capacity of high alumina blast furnace slags. Metall Mater Trans B 37, 941–947 (2006). https://doi.org/10.1007/BF02735016
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02735016